초록 ▼

A selective hydrogenation catalyst, with alumina as carrier, and palladium as active component that distributed on the surface of the carrier in an egg-shell form, characterized in that: provided that the catalyst is weighed 100%, it comprises 0.2-0.5 wt % active component Pd, 2-8 wt % aids lanthanu

A selective hydrogenation catalyst, with alumina as carrier, and palladium as active component that distributed on the surface of the carrier in an egg-shell form, characterized in that: provided that the catalyst is weighed 100%, it comprises 0.2-0.5 wt % active component Pd, 2-8 wt % aids lanthanum and/or cerium, and 2-8 wt % alkaline earth metal. The specific surface area of the catalyst is 70-150 m2/g, the pore volume is 0.3-0.6 ml/g, and the crystal form of the carrier may be θ form or θ, α mixed form mainly composed of θ form. The catalyst is suitable for the selective hydrogenation of medium or low distillate oil, especially for the first stage selective hydrogenation of pyrolysis gasoline. The catalyst has good hydrogenation performance, and can keep good hydrogenation activity and stability especially under the condition that the feed contains a small quantity of water, and the content of colloid, arsenic, and diolefin is higher.

대표청구항 ▼

1. A selective hydrogenation catalyst comprising alumina as a carrier and palladium (Pd) as an active component that is distributed on the surface of the carrier in an egg-shell form, wherein based on the total weight of the catalyst, it comprises: 0.2 to 0.5 wt % Pd as an active component,2 to 8 wt

1. A selective hydrogenation catalyst comprising alumina as a carrier and palladium (Pd) as an active component that is distributed on the surface of the carrier in an egg-shell form, wherein based on the total weight of the catalyst, it comprises: 0.2 to 0.5 wt % Pd as an active component,2 to 8 wt % lanthanum and/or cerium as aids,2 to 8 wt % alkaline earth metal, and0 to 2.0 wt % Ag and/or K, wherein said catalyst has a shell thickness of 0.07 to 0.15 mm, a specific surface area of 70 to 150 m2/g, a pore volume of 0.3 to 0.6 ml/g; and the crystal form of said carrier is θ form or θ, α mixed form mainly composed of θ form. 2. The selective hydrogenation catalyst according to claim 1, wherein the alkaline earth metal is one or more selected from the group consisting of calcium, magnesium, strontium and barium. 3. The selective hydrogenation catalyst according to claim 1, wherein the alkaline earth metal in the catalyst is in the amount of 3 to 6 wt %. 4. The selective hydrogenation catalyst according to claim 1, wherein the catalyst has a specific surface area of 80 to 120 m2/g. 5. The selective hydrogenation catalyst according to claim 1, wherein the Pd in the catalyst is in the amount of 0.2 to 0.4 wt %. 6. The selective hydrogenation catalyst according to claim 1, wherein the lanthanum and/or cerium in the catalyst is in the amount of 2 to 6 wt %. 7. The selective hydrogenation catalyst according to claim 1, wherein in the case where the alumina carrier is in θ, α mixed form mainly composed of θ form, the α form is less than 15%. 8. The selective hydrogenation catalyst according to claim 1, wherein the added amount of Ag and/or K in the catalyst is 0.4 to 1.7 wt %. 9. A method for preparing the selective hydrogenation catalyst according to claim 1 comprising: adding the alkaline earth metal, lanthanum and/or cerium to the carrier so as to provide the carrier comprising the alkaline earth metal, lanthanum and/or cerium; andadding palladium to the carrier comprising the alkaline earth metal, lanthanum and/or cerium;wherein said adding palladium comprises:impregnating the carrier comprising the alkaline earth metal, lanthanum and/or cerium with a solution comprising palladium. 10. A method for preparing the selective hydrogenation catalyst according to claim 1 comprising: adding alkaline earth metal, lanthanum and/or cerium to the carrier, wherein the carrier is prior to the formation of alumina in θ form or θ, α mixed form. 11. A method for preparing the selective hydrogenation catalyst according to claim 1 comprising: dissolving soluble salts of alkaline earth metal element, lanthanum and/or cerium in water to form a solution;impregnating the carrier with said solution;drying the impregnated carrier at 40 to 120° C.;calcinating the dried carrier at 900 to 1100° C. for 4 to 6 hours, thereby forming the carrier in θ form or θ, α mixed form comprising alkaline earth metal element, lanthanum and/or cerium;pre-impregnating said carrier in θ form or in θ, α mixed form with a liquid miscible with a salt solution containing noble metal palladium;then impregnating the pre-impregnated carrier in θ form or in θ, α mixed form with the salt solution containing noble metal palladium;washing and drying the resultant impregnated carrier in θ form or in θ, α mixed form; and calcinating the washed and dried carrier at 350 to 500° C. for 2 to 4 hours, thereby obtaining the catalyst.