초록 ▼

Photoactivatable prepolymers and methods of use thereof are disclosed for microencapsulation of a substantially water-insoluble material within a nonporous shell. As provided herein, the microencapsulated material is released with no more than a slow release rate. Upon exposure of the nonporous shel

Photoactivatable prepolymers and methods of use thereof are disclosed for microencapsulation of a substantially water-insoluble material within a nonporous shell. As provided herein, the microencapsulated material is released with no more than a slow release rate. Upon exposure of the nonporous shell to light, the nonporous shell is converted into a porous shell having an increased release rate for the microencapsulated material.

대표청구항 ▼

1. A method for producing microcapsules comprising a substantially water-insoluble liquid material within a non-porous, light-sensitive shell, wherein the non-porous shell is characterized by a release rate of the liquid material in the absence of light of less than 1 ppm/minute, wherein exposure to

1. A method for producing microcapsules comprising a substantially water-insoluble liquid material within a non-porous, light-sensitive shell, wherein the non-porous shell is characterized by a release rate of the liquid material in the absence of light of less than 1 ppm/minute, wherein exposure to light converts the nonporous shell into a porous shell characterized by a release rate of the liquid material of from 1 to at least 100 ppm/minute, the method comprising the steps of: (a) providing an organic solution comprising said liquid material and a photoactivatable prepolymer or mixture of a photoactivatable prepolymer and a nonphotoactive-based prepolymers dissolved therein, wherein the photoactivatable prepolvmer is selected from the group consisting of (+/−)3-[1-(2-aminoethoxy)-2-oxo-2-phenylethyl] phenoxy acetic acid, 2-(2-hydroxyethoxy)-2-[3-(2-hydroxyethoxy)-5-methylphenyl]-1-phenylethanone, and photoactivatable combinations thereof;(b) creating an emulsion of said organic solution in a continuous phase aqueous solution comprising water and a surface-active agent, wherein said emulsion comprises discrete droplets of said organic solution dispersed in said continuous phase aqueous solution, there being formed thereby an interface between the discrete droplets of organic solution and the surrounding continuous phase aqueous solution; and(c) causing in situ self-condensation and curing of said prepolymers in the organic phase of said discrete droplets adjacent to said interface by catalysis using heat, pH, or a chemical or free radical initiator for a time sufficient to allow substantial completion of in situ condensation of said prepolymers, thereby converting the liquid droplets of said organic solution to microcapsules comprising a solid nonpermeable polymer shell that encloses said liquid material. 2. A method according to claim 1, wherein the prepolymer of step (a) comprises from about 1% to about 70% of the organic solution on a weight basis. 3. A method according to claim 1, wherein the droplets of the dispersion formed in step (b) are from about 0.5 microns to about 4000 microns in diameter. 4. A method according to claim 1, wherein the in situ self-condensation in step (c) is performed at a pH of between about 1.0 and about 12.0. 5. A method according to claim 1, wherein the in situ self-condensation in step (c) is performed at a temperature between about 10 degrees C. and about 100 degrees C. 6. A method according to claim 1, wherein said organic solution contains a wall-modifying agent which serves to modify the character of the microcapsule polymeric wall by varying its permeability to the core material. 7. A method according to claim 1, wherein the liquid material comprises a fragrance, a flavor, a drug, an herbicide or a pesticide. 8. A method according to claim 1, wherein the liquid material comprises a plurality of substantially water-insoluble compounds that are fragrances, flavorings, drugs, herbicides or pesticides.