There are disclosed a water-absorbent resin composition and its production process, wherein the water-absorbent resin composition causes little gel-blocking and is excellent in the liquid permeability and liquid diffusibility and is high also in the absorption performances and further is strong also
There are disclosed a water-absorbent resin composition and its production process, wherein the water-absorbent resin composition causes little gel-blocking and is excellent in the liquid permeability and liquid diffusibility and is high also in the absorption performances and further is strong also against the physical damage; and there are further disclosed a water-absorbent resin composition and its production process, wherein the water-absorbent resin composition has the following further advantages, in addition to the above, of involving little segregation of the metal compound and further having a dust prevention effect. One of water-absorbent resin compositions according to the present invention is a water-absorbent resin composition comprising water-absorbent resin particles obtained by polymerizing a monomer including acrylic acid and/or its salt, with the composition having a mass-average particle diameter of 100 to 600 μm and comprising water-soluble polyvalent metal salt particles and the water-absorbent resin particles that have been surface-crosslinked.
대표청구항▼
1. A water-absorbent resin composition, which is a water-absorbent resin composition comprising water-absorbent resin particles obtained by polymerizing a monomer including acrylic acid and/or its salt, with the composition having a mass-average particle diameter of 100 to 600 μm and comprising wate
1. A water-absorbent resin composition, which is a water-absorbent resin composition comprising water-absorbent resin particles obtained by polymerizing a monomer including acrylic acid and/or its salt, with the composition having a mass-average particle diameter of 100 to 600 μm and comprising water-soluble polyvalent metal salt particles and the water-absorbent resin particles that have been surface-crosslinked, and where at least a part of the water-absorbent resin particles are agglomerates, and at least a part of the water-soluble polyvalent metal salt particles are fused to surfaces of the water-absorbent resin particles. 2. A water-absorbent resin composition according to claim 1, wherein the water-soluble polyvalent metal salt particles are particles of an aluminum salt having water of crystallization. 3. A water-absorbent resin composition according to claim 1, wherein the water-absorbent resin particles are those which have been surface-crosslinked with a polyhydric alcohol. 4. A water-absorbent resin composition, which is a water-absorbent resin composition having a mass-average particle diameter of 100 to 600 μM comprising water-absorbent resin particles and water-soluble polyvalent metal salt particles, wherein the water-absorbent resin particles are obtained by polymerizing a monomer including acrylic acid and/or its salt, with the composition having a saline flow conductivity of at least 50 (×10−7·cm3·s·g−1) and a retention ratio of the saline flow conductivity of not less than 40%, and where at least a part of the water-absorbent resin particles are agglomerates, and at least a part of the water-soluble polyvalent metal salt particles are fused to surfaces of the water-absorbent resin particles. 5. A water-absorbent resin composition according to claim 4, wherein the retention ratio of the saline flow conductivity after a paint shaker test is not less than 70%. 6. A process for production of a water-absorbent resin composition, which is characterized by comprising the steps of: adding a binder to water-absorbent resin particles obtained by polymerizing a monomer including acrylic acid and/or its salt; and thenmixing the binder and the water-absorbent resin particles with water-soluble polyvalent metal salt particles to produce the water-absorbent resin composition having a mass-average particle diameter of 100 to 600 μm, and where at least a part of the water-absorbent resin particles are agglomerates, and at least a part of the water-soluble polyvalent metal salt particles are fused to surfaces of the water-absorbent resin particles. 7. A process for production of a water-absorbent resin composition according to claim 6, wherein the water-absorbent resin particles are surface-crosslinked ones. 8. A process for production of a water-absorbent resin composition according to claim 6, wherein the binder contains a surface-crosslinking agent. 9. A process for production of a water-absorbent resin composition according to claim 6, wherein the binder includes water and/or a polyhydric alcohol. 10. A process for production of a water-absorbent resin composition according to claim 6, wherein, when the binder is added to the water-absorbent resin particles, the temperature of the water-absorbent resin particles is in the range of 40 to 100° C. 11. A water-absorbent resin composition according to claim 5, wherein the water-absorbent resin particles have a mass-average particle diameter of not larger than 500 μm; and the water-soluble polyvalent metal salt has a mass-average particle diameter of not larger than 500 μm. 12. A water-absorbent resin composition according to claim 1, 4 or 5, wherein the water-absorbent resin particles have been surface-crosslinked with an organic surface-crosslinking agent. 13. A water-absorbent resin composition according to claim 12, wherein the organic surface-crosslinking agent is a polyhydric alcohol. 14. A process for production of a water-absorbent resin composition according to claim 6, 7 or 8, wherein the water-absorbent resin particles have a mass-average particle diameter of not larger than 500 μm; and the water-soluble polyvalent metal salt particles have a mass-average particle diameter of not larger than 500 μm. 15. A water-absorbent resin composition according to claim 4, wherein the composition is prepared by dry mixing the water-soluble polyvalent metal salt and the water-absorbent resin particles. 16. A water-absorbent resin composition according to claim 1 or claim 4, wherein the water-soluble polyvalent metal salt particles are a powder having a mass-average particle diameter of not larger than 1,000 μm. 17. A water-absorbent resin composition according to claim 1, wherein the fusion is heat-fusion. 18. A water-absorbent resin composition according to claim 4, which has a saline flow conductivity of not less than 100×10−7·cm3·s/g. 19. The process for production of a water-absorbent resin composition according to claim 6, wherein the water-soluble polyvalent metal salt particles comprise one or more members selected from the group consisting of alkaline metal salts and polyvalent metal salts (except polyvalent metal salts of organic acids having not fewer than 7 carbon atoms per molecule); with the process comprising the steps of:heating the water-absorbent resin particles and/or the water-soluble polyvalent metal salt particles to a temperature of not lower than the melting point of the water-soluble polyvalent metal salt particles; andthereby fusing at least a part of the water-soluble polyvalent metal salt particles to surfaces of the water-absorbent resin particles. 20. The water-absorbent resin composition of claim 1, wherein the amount of the agglomerates is not smaller than 5 mass %. 21. The water-absorbent resin composition of claim 4, wherein the amount of the agglomerates is not smaller than 5 mass %. 22. The process for the production of a water-absorbent composition of claim 6, wherein the amount of the agglomerates is not smaller than 5 mass %. 23. The water-absorbent resin composition of claim 4, wherein the fusion is heat-fusion. 24. The process of claim 6, wherein the fusion is heat-fusion.
Chmelir Miroslav (Grnkesdyk 36 4150 Krefeld DEX) Dahmen Kurt (von-Velsen.str.6 MDEX) Hoffman Georg (Westwall 165 4150 Krefeld DEX) Werner Georg (Dresdner Str.7 4154 Tnisvorst 1 DEX), Absorbents for blood and serous body fluids.
Brandt Kerryn A. (Cincinnati OH) Goldman Stephen A. (Cincinnati OH) Inglin Thomas A. (Cincinnati OH), Hydrogel-forming polymer compositions for use in absorbent structures.
Irie Yoshio (Himeji JPX) Hatsuda Takumi (Himeji JPX) Yonemura Koichi (Suita JPX), Method for production of particulate hydrated gel polymer and absorbent resin.
Weaver Mary Ollidene (Peoria IL) Bagley Edward B. (Morton IL) Fanta George F. (Peoria IL) Doane William M. (Morton IL), Method of reducing water content of emulsions, suspensions, and dispersions with highly absorbent starch-containing poly.
Mertens, Richard; Harren, Jorg, Powdery, cross-linked polymers which absorb aqueous liquids and blood, method for the production thereof and their use.
Gartner Herbert (Baden-Baden DEX) Burgert Josef (Achern-Fautenbach DEX), Surface crosslinked and surfactant coated absorbent resin particles and method of preparation.
Harada Nobuyuki (Osaka JPX) Wada Katsuyuki (Osaka JPX) Obara Hisanori (Osaka JPX) Shimomura Tadao (Osaka JPX) Sano Yoshinori (Hyogo JPX), Water absorbent matter and method for producing it as well as water absorbent and method for producing it.
Breitbach Ludger,DEX ; Dahmen Kurt,DEX ; Houben Jochen,DEX ; Kuster Erich,DEX, Water-swelling polymers cross-linked with unsaturated amino alcohols, the production and use of same.
Tian, Gonglu; Ondisco, Matthew Thomas; Bergman, David L.; Messner, Bernfried; Smith, Scott J., Particulate superabsorbent polymer composition having improved stability.