Slurries and methods of making light weight gypsum board
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C04B-011/00
C04B-026/28
C04B-024/38
출원번호
US-0709159
(2010-02-19)
등록번호
US-8257489
(2012-09-04)
발명자
/ 주소
Yu, Qiang
Song, Weixin D.
Lynn, Michael R.
출원인 / 주소
United States Gypsum Company
대리인 / 주소
Leydig Voit & Mayer, Ltd.
인용정보
피인용 횟수 :
15인용 특허 :
195
초록▼
The invention generally provides gypsum-containing slurries including stucco, naphthalenesulfonate dispersant, and pregelatinized starch. The naphthalenesulfonate dispersant is present in an amount of about 0.1%-3.0% by weight based on the weight of dry stucco. The pregelatinized starch is present i
The invention generally provides gypsum-containing slurries including stucco, naphthalenesulfonate dispersant, and pregelatinized starch. The naphthalenesulfonate dispersant is present in an amount of about 0.1%-3.0% by weight based on the weight of dry stucco. The pregelatinized starch is present in an amount of at least about 0.5% by weight up to about 10% by weight of pregelatinized starch by weight based on the weight of dry stucco in the formulation. Other slurry additives can include trimetaphosphate salts, accelerators, binders, paper fiber, glass fiber, and other known ingredients.
대표청구항▼
1. A slurry comprising water, stucco, pregelatinized starch, and a naphthalenesulfonate dispersant; the pregelatinized starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco, and the naphthalenesulfonate dispersant is present in an amount from about 0
1. A slurry comprising water, stucco, pregelatinized starch, and a naphthalenesulfonate dispersant; the pregelatinized starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco, and the naphthalenesulfonate dispersant is present in an amount from about 0.2% to about 3.0% by weight based on the weight of the stucco;when the slurry is cast and dried as board, the board has a density of about 34 pcf or less; andwhen the slurry is cast and dried as said board that is about 1/2 inch thick, the board has a nail pull resistance of at least about 65 lb, an average core hardness of at least about 11 lb, and an average flexural strength of at least about 36 lb in a machine direction and/or about 107 lb in a cross-machine direction, the nail pull resistance, the core hardness and the flexural strength as determined in accordance with ASTM C473. 2. The slurry of claim 1, wherein the naphthalenesulfonate dispersant is present in an amount from about 0.25% to about 3.0% by weight based on the weight of the stucco. 3. The slurry of claim 1, wherein the pregelatinized starch is present in an amount from about 0.5% to about 3% by weight based on the weight of the stucco. 4. The slurry of claim 1, wherein the slurry is further formed from a water soluble polyphosphate present in an amount from about 0.12% to about 0.4% by weight based on the weight of the stucco. 5. The slurry of claim 1, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a dry weight from about 1000 lb/MSF to about 1400 lb/MSF. 6. The slurry of claim 1, wherein when the slurry is cast and dried as board, the board has a density from about 24 pcf to about 34 pcf. 7. The slurry of claim 6, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a nail pull resistance of at least about 77 lb. 8. The slurry of claim 6, the slurry having a wet compressive strength of at least about 340 psi when the slurry is cast as a two-inch cube. 9. The slurry of claim 6, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a nail pull resistance to core hardness ratio from about 4 to about 8. 10. The slurry of claim 6, wherein when the slurry is cast and dried as board, the board has a ratio of density (pcf) to core hardness (lb) of less than about 3.2. 11. A slurry comprising water, stucco, starch, and foam; the starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco and effective to increase the average core hardness of the slurry when set as relative to the slurry without the starch when set;when the slurry is cast and dried as board, the board has a density from about 24 pcf to about 34 pcf; andwhen the slurry is cast and dried as said board that is about 1/2 inch thick, the board has an average core hardness of at least about 11 lb, and at least one of: a nail pull resistance of at least about 65 lb, an average flexural strength of at least about 36 lb in a machine direction, and an average flexural strength of at least about 107 lb in a cross-machine direction, the core hardness, the nail pull resistance, and the flexural strength as determined in accordance with ASTM C473. 12. The slurry of claim 11, wherein the slurry is further formed from naphthalenesulfonate dispersant present in an amount from about 0.1% to about 3.0% by weight based on the weight of the stucco. 13. The slurry of claim 11, wherein the starch is a pregelatinized starch and is present in an amount from about 0.5% to about 3% by weight based on the weight of the stucco. 14. The slurry of claim 11, wherein the slurry is further formed from a water soluble polyphosphate present in an amount of at least about 0.12% by weight based on the weight of the stucco. 15. The slurry of claim 11, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a dry weight from about 1000 lb/MSF to about 1400 lb/MSF. 16. The slurry of claim 11, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a nail pull resistance of at least about 77 lb. 17. The slurry of claim 11, wherein the slurry is formed from the water, the stucco, pregelatinized starch, and a naphthalenesulfonate dispersant, the slurry having a wet compressive strength of at least about 340 psi when the slurry, exclusive of added foam therein, is cast as a two-inch cube. 18. The slurry of claim 11, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a nail pull resistance to core hardness ratio from about 4 to about 8. 19. The slurry of claim 11, wherein when the slurry is cast and dried as board, the board has a ratio of density (pcf) to core hardness (lb) of less than about 3.2. 20. A method of making a light weight gypsum board, comprising: (a) mixing at least water, stucco, pregelatinized starch, and a naphthalenesulfonate dispersant to form a slurry, the pregelatinized starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco, and the naphthalenesulfonate dispersant is present in an amount from about 0.2% to about 3.0% by weight based on the weight of the stucco;(b) disposing the slurry between a first cover sheet and a second cover sheet to form a panel;(c) cutting the panel into a board; and(d) drying the board;such that the dried board has a density of about 34 pcf or less; andwhen the dried board is about 1/2 inch thick, the board has a nail pull resistance of at least about 65 lb, an average core hardness of at least about 11 lb, and an average flexural strength of at least about 36 lb in a machine direction and/or about 107 lb in a cross-machine direction, the nail pull resistance, the core hardness and the flexural strength as determined in accordance with ASTM C473. 21. The method of claim 20, wherein the slurry is further formed from a water soluble polyphosphate present in an amount from about 0.12% to about 0.4% by weight based on the weight of the stucco. 22. The method of claim 20, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a dry weight from about 1000 lb/MSF to about 1400 lb/MSF. 23. The method of claim 20, wherein when the slurry is cast and dried as board, the board has a density from about 24 pcf to about 34 pcf. Zone Name: C7,AMD,M 24. The method of claim 23, wherein the pregelatinized starch is present in an amount from about 0.5% to about 3% by weight based on the weight of the stucco. 25. The method of claim 23, the slurry having a wet compressive strength of at least about 340 psi when the slurry is cast as a two-inch cube. 26. The method of claim 23, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a nail pull resistance to core hardness ratio from about 4 to about 8. 27. The method of claim 23, wherein when the slurry is cast and dried as board, the board has a ratio of density (pcf) to core hardness (lb) of less than about 3.2. 28. A method of making a light weight gypsum board, comprising: (a) mixing at least water, stucco, starch, and foam to form a slurry, the starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco and effective to increase the average core hardness of the slurry when set as relative to the slurry without the starch when set;(b) disposing the slurry between a first cover sheet and a second cover sheet to form a panel;(c) cutting the panel into a board; and(d) drying the board;such that the dried board has a density from about 24 pcf to about 34 pcf; andwhen the dried board is about 1/2 inch thick, the board has an average core hardness of at least about 11 lb, and at least one of: a nail pull resistance of at least about 65 lb, an average flexural strength of at least about 36 lb in a machine direction, and an average flexural strength of at least about 107 lb in a cross-machine direction, the core hardness, the nail pull resistance, and the flexural strength as determined in accordance with ASTM C473. 29. The method of claim 28, wherein the slurry is further formed from naphthalenesulfonate dispersant present in an amount from about 0.1% to about 3.0% by weight based on the weight of the stucco. 30. The method of claim 28, wherein the slurry is further formed from a water soluble polyphosphate present in an amount of at least about 0.12% by weight based on the weight of the stucco. 31. The method of claim 28, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a dry weight from about 1000 lb/MSF to about 1400 lb/MSF. 32. The method of claim 28, wherein the slurry is formed from the water, the stucco, pregelatinized starch, and a naphthalenesulfonate dispersant, the slurry having a wet compressive strength of at least about 340 psi when the slurry, exclusive of added foam therein, is cast as a two-inch cube. 33. The method of claim 28, wherein when the slurry is cast and dried as board that is about 1/2 inch thick, the board has a nail pull resistance to core hardness ratio from about 4 to about 8. 34. The method of claim 28, wherein when the slurry is cast and dried as board, the board has a ratio of density (pcf) to core hardness (lb) of less than about 3.2.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (195)
Englert, Mark H.; Stevens, Richard B.; Sucech, Steven W.; Fults, Therese A.; Porter, Michael J.; Petersen, Bruce L.; Dombeck, Russell A., Acoustical panel comprising interlocking matrix of set gypsum and method for making same.
Englert,Mark H.; Stevens,Richard B.; Sucech,Steven W.; Fults,Therese A.; Porter,Michael J.; Petersen,Bruce L.; Dombeck,Russell A., Acoustical panel comprising interlocking matrix of set gypsum and method for making same.
Sironi, Enrico; Margheritis, Giampietro; Pfeiffer, Ugo Claudio; Bassi, Giuseppe Li, Additives based on hydroxyalkyl guar derivatives for use in mortars and mortars including them.
Glowaky Raymond Charles (Matteson IL) Rudolph Stephen Edward (Glenwood IL) Bierwagen Gordon Paul (Homewood IL), Aqueous compositions containing starch ester dispersants.
Otey Felix H. (Peoria IL) Westhoff Richard P. (Peoria IL), Biodegradable film compositions prepared from starch and copolymers of ethylene and acrylic acid.
Klauck Wolfgang,DEX ; Kluth Hermann,DEX ; Huebner Wilfried,DEX ; Kolenda Felicitas,DEX, Composition for producing light plaster, production of the foaming agent used therefor and its use.
Albrecht, Gerhard; Hübsch, Christian; Leitner, Hubert; Grassl, Harald; Kern, Alfred, Copolymers based on unsaturated mono-or dicarboxylic acid derivatives and oxyalkylene glycol alkenyl ethers, method for the production and use thereof.
Plunguian Mark (6912 Columbia Drive BOTH OF ; Alexandria VA 22307) Cornwell Charles E. (7104 Marlan Drive BOTH OF ; Alexandria VA 22307), Foamed cementitious compositions and method of producing same.
Francis, Hubert C.; Ksionzyk, Anne H.; Esguerra, Fabio E., Gypsum board having polyvinyl alcohol binder in interface layer and method for making the same.
Liu, Qingxia; Shake, Michael P.; Blackburn, David R.; Wilson, John W.; Randall, Brian; Lettkeman, Dennis M., Gypsum products utilizing a two-repeating unit dispersant and a method for making them.
Liu, Qingxia; Shake, Michael P.; Blackburn, David R.; Wilson, John W.; Randall, Brian; Lettkeman, Dennis M., Gypsum products utilizing a two-repeating unit dispersant and a method of making them.
Yu, Qiang; Sucech, Steven W.; Groza, Brent E.; Mlinac, Raymond J.; Jones, Frederick T.; Henkels, Paul J., Gypsum-containing board and tile, and method for producing gypsum-containing board and tile.
Yu, Qiang; Sucech, Steven W.; Groza, Brent E.; Mlinac, Raymond J.; Jones, Frederick T.; Henkels, Paul J., Gypsum-containing board and tile, and method for producing same.
Yu, Qiang; Sucech, Steven W.; Groza, Brent E.; Mlinac, Raymond J.; Jones, Frederick T.; Henkels, Paul J., Gypsum-containing product and method for producing same.
Qiang Yu ; Steven W. Sucech ; Brent E. Groza ; Raymond J. Mlinac ; Frederick T. Jones ; Paul J. Henkels, Gypsum-containing product having increased resistance to permanent deformation and method and composition for producing it.
Yu, Qiang; Sucech, Steven W.; Groza, Brent E.; Mlinac, Raymond J.; Jones, Frederick T.; Boehnert, Frederick M., Gypsum-containing product having increased resistance to permanent deformation and method and composition for producing it.
Andersen Per Just (Santa Barbara CA) Hodson Simon K. (Santa Barbara CA), Inorganically filled, starch-bound compositions for manufacturing containers and other articles having a thermodynamical.
Cowan Jack C. (Lafayette LA) House Roy F. (Houston TX) Harrington Andree\H. (Lafayette LA), Lightweight particulate cementitious materials and process for producing same.
Sucech Steven W. (Lake Villa IL) Hinshaw Stewart E. (Sweetwater TX) Nemeth Bradley S. (Bedford IN) Buster Kip R. (Burlington IA), Method for preparing uniformly foamed gypsum product with less foam agitation.
Putt, Dean L.; Hartman, Jr., John J.; Hallett, Chester W.; Moser, Andrea M., Method for producing an inorganic foam structure for use as a durable acoustical panel.
Baehr Donald O. (Arlington Heights IL) Izard David G. (Hoffman Estates IL), Method for the production of glass fiber-reinforced gypsum sheets and gypsum board formed therefrom.
Baehr Donald O. (Arlington Heights IL) Izard David G. (Hoffman Estates IL), Method for the production of glass fiber-reinforced gypsum sheets and gypsum board formed therefrom.
Tanis Rick A. ; Merser N. Keith ; Hyde-Smith Peter K., Method of filling a seam of a panel assembly using a thixotropic polyurethane elastomeric filler adhesive.
Liu, Qingxia; Blackburn, David R.; Shake, Michael P.; Randall, Brian; Wilson, John W.; Lettkeman, Dennis M., Method of making a gypsum slurry with modifiers and dispersants.
Hauber, Robert J.; Sanders, Christopher J.; Hennis, Mark E.; Fahey, Michael P., Method of manufacture of glass reinforced gypsum board and apparatus therefor.
Sellers Dwight G. (Fort Dodge IA) Altman Franklin A. (Hortense GA) Richards Turner W. (Conyers GA), Method of manufacturing a water-resistant gypsum composition.
Schfer Karl K. (Gengenbach DEX) Melzer Gerhard M. (Lautertal DEX) Scriba Jrg (Ortenberg TX DEX) Bhagwat Suda G. (Double Oak TX) Eisses James (Coeus D\Alene ID), Method of manufacturing fiber gypsum board.
Baig Mirza A. (Des Plaines IL) Englert Mark H. (Buffalo Grove IL) Gaynor John C. (Antioch IL) Kacner Michael A. (Lindenhurst IL) Singh Rajinder (Mundelein IL), Mineral wool-free acoustical tile composition.
Lettkeman, Dennis M.; Shake, Michael P.; Liu, Qingxia; Wilson, John W.; Randall, Brian; Blackburn, David R., Modifiers for gypsum slurries and method of using them.
Lettkeman, Dennis M.; Shake, Michael P.; Liu, Qingxia; Wilson, John W.; Randall, Brian; Blackburn, David R., Modifiers for gypsum slurries and method of using them.
Hillmer Roy Wayne (Parker CO) Morrone Nicholas Francis (Littleton CO) Slahetka Chester Robert (Littleton CO), Perlite insulation board and method of making the same.
Kurt N. Peterson ; Gerry L. Heschel ; Dick C. Engbrecht ; Frederick T. Jones, Process for making gypsum board having improved through-penetration strength.
Stipek Josef (Bad Hersfeld DEX) Bahner Friedrich (Rotenburg a.d.G. DEX) Hose Horst (Kassel DEX) Freisinger Karl (Bad Hersfeld DEX) Eidam Helmut (Schenklengsfeld DEX), Process for making gypsum fiberboard.
Koslowski Thomas (Aachen DEX) Hessler Klaus M. (Herzogenrath DEX) Musebrink Olaf (D-Ubach-Palenberg DEX) Kieker Joachim (Wegberg DEX), Process for producing gypsum building materials.
Dillenbeck, Robert L.; Heinold, Thomas; Rogers, Murray J.; Bray, Windal S., Ultra low density cementitious slurries for use in cementing of oil and gas wells.
Helbling,Andre Marcel; Hills,Michael Robert; Stollmaier,Friederike Theresia; Annen,Thomas Martin Stephan, Use of starch dispersions as binder in coating compositions and process for preparing the starch dispersions.
Kiesewetter Ren (Soltau-Ahlften DEX) Szablikowski Klaus (Walsrode DEX) Lange Werner (Visselhvede DEX), Water-soluble sulphoalkyl hydroxyalkyl derivatives of cellulose and their use in gypsum- and cement-containing compounds.
Sang, Yijun; Song, Weixin D.; Chan, Cesar; Lee, Chris C., Method of preparing pregelatinized, partially hydrolyzed starch and related methods and products.
Sang, Yijun; Lee, Chris C.; Chan, Cesar; Song, Weixin David, Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto.
Li, Alfred; Lee, Chris C.; Chan, Cesar; Schenck, Ronald E.; Song, Weixin David; Loring, Curtis B.; Wittbold, James R.; Rago, William J.; Nelson, Christopher Robert, Slurry distributor, system and method for using same.
Li, Alfred; Lee, Chris C.; Chan, Cesar; Schenck, Ronald E.; Song, Weixin David; Loring, Curtis B.; Wittbold, James R.; Rago, William J.; Nelson, Christopher Robert, Slurry distributor, system and method for using same.
Wittbold, James; Lee, Chris C.; Li, Alfred C.; Punati, Naveen; Rago, William J.; Carrazco, Luis, Slurry distributor, system, and method for using same.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.