초록 ▼

A method of preparing a catalyst comprising selecting a zeolite having a mean particle size of equal to or less than about 6 microns, blending the zeolite with a binder and water to form a paste, shaping the paste into a bound zeolite support, adding a metal to the bound zeolite support to form a me

A method of preparing a catalyst comprising selecting a zeolite having a mean particle size of equal to or less than about 6 microns, blending the zeolite with a binder and water to form a paste, shaping the paste into a bound zeolite support, adding a metal to the bound zeolite support to form a metalized catalyst support, and adding at least one halide to the metalized catalyst support to form the catalyst. A catalytic reforming process for converting hydrocarbons to aromatics comprising: contacting a catalyst comprising a silica bound zeolite, a Group VIII metal supported thereby, and at least one halide with a hydrocarbon feed in a reaction zone under reforming conditions and recovering aromatics from the reaction zone, wherein the silica bound zeolite comprises a zeolite having a mean particle size of equal to or less than about 6 microns and a median particle size of equal to or less than about 5 microns.

대표청구항 ▼

1. A method of preparing a catalyst comprising: selecting a zeolite having a mean particle size ranging from equal to or greater than 1.4 microns to equal to or less than about 6 microns and a median particle size of equal to or less than about 5 microns wherein the zeolite comprises an L-zeolite;bl

1. A method of preparing a catalyst comprising: selecting a zeolite having a mean particle size ranging from equal to or greater than 1.4 microns to equal to or less than about 6 microns and a median particle size of equal to or less than about 5 microns wherein the zeolite comprises an L-zeolite;blending the zeolite with a binder and water to form a paste wherein the paste has a dough-like consistency and is characterized by a resistance to crumbling and the ability to maintain a cohesive form;shaping the paste into a bound zeolite support;adding a metal to the bound zeolite support to form a metalized catalyst support; andadding at least one halide to the metalized catalyst support to form the catalyst. 2. The method of claim 1 wherein the binder comprises synthetic or naturally occurring zeolites, alumina, silica, clays, or combinations thereof. 3. The method of claim 1 wherein the catalyst has a weight ratio of the zeolite to the binder in a range of from about 90:10 to about 70:30. 4. The method of claim 1 wherein the catalyst has a particle density in a range of from about 1 to about 1.3 g/cc. 5. The method of claim 1 wherein the bound zeolite support, the metalized catalyst support, or the catalyst thereof have a crush strength of equal to or greater than about 3.0 lb/mm. 6. The method of claim 1 wherein the amount of water used to form the paste is reduced when compared to an otherwise identical paste with the mean particle size of the zeolite is greater than about 6 microns. 7. The method of claim 1 wherein the metal comprises a Group VIII metal. 8. The method of claim 1 wherein the metal comprises platinum. 9. The method of claim 1 wherein the at least one halide comprises fluoride, chloride, bromide, iodide, or combinations thereof. 10. A method of preparing a catalyst comprising: selecting a L-zeolite having a mean particle size ranging from equal to or greater than 1.4 microns to equal to or less than about 6 microns and a median particle size of equal to or less than about 5 microns;blending the L-zeolite with a silica sol and water to form a paste wherein the paste has a dough-like consistency and is characterized by a resistance to crumbling and the ability to maintain a cohesive form; wherein a weight ratio of the L-zeolite to the silica is in a range of from about 90:10 to about 70:30;shaping the paste into a bound zeolite support;adding a Group VIII metal to the bound zeolite support to form a metalized catalyst support; andadding chloride and fluoride to the metalized catalyst support to form the catalyst;and wherein the bound zeolite support, the metalized catalyst support; or the catalyst has a crush strength of equal to or greater than about 3.0 lb/mm. 11. The method of claim 10 wherein the catalyst has an improved crush strength over an otherwise similar catalyst having a mean particle size of greater than about 6 microns and a median particle size of greater than about 5 microns. 12. The method of claim 10 wherein the paste further comprises an extrusion aid. 13. The method of claim 10 wherein the catalyst has a bulk density of from about 35 lb/ft3 to about 47 lb/ft3. 14. The method of claim 10 wherein the bound zeolite support, the metalized catalyst support, or the catalyst thereof have a crush strength of equal to or greater than about 3.5 lb/mm.