The present invention provides catalysts, reactors, and methods of steam reforming over a catalyst. Surprisingly superior results and properties obtained in methods and catalysts of the present invention are also described. For example, a coated catalyst was demonstrated to be highly stable under st

The present invention provides catalysts, reactors, and methods of steam reforming over a catalyst. Surprisingly superior results and properties obtained in methods and catalysts of the present invention are also described. For example, a coated catalyst was demonstrated to be highly stable under steam reforming conditions (high temperature and high pressure of steam). Methods of making steam reforming catalysts are also described.

대표청구항 ▼

1. A method of making a steam reforming catalyst composition, comprising: providing a coating composition comprising an alumina precursor;applying the composition onto a substrate to form a coated substrate;providing an alumina stabilizer;drying the coated substrate to form a dried support; andhydro

1. A method of making a steam reforming catalyst composition, comprising: providing a coating composition comprising an alumina precursor;applying the composition onto a substrate to form a coated substrate;providing an alumina stabilizer;drying the coated substrate to form a dried support; andhydrothermally pre-aging the dried support in a gas atmosphere comprising at least 5 atm H2O (partial pressure) and a temperature of at least 850° C. to form a hydrothermally stabilized support. 2. The method of claim 1, further comprising a step of depositing a catalytic metal on the hydrothermally stabilized support. 3. The method of claim 2, wherein the metal comprises Rh and further comprising a step of reducing the metal at a temperature of at least 300° C. 4. The method of claim 1 wherein the coating composition comprises an alumina sol and soluble Mg. 5. The method of claim 2 wherein the step of providing an alumina stabilizer occurs subsequent to the step of applying the coating composition onto a substrate. 6. The method of claim 2 wherein the step of applying comprises dip coating. 7. The method of claim 1 wherein the substrate is metal. 8. The method of claim 7 wherein the substrate is FeCrAlY. 9. The method of claim 7 wherein the substrate's surface is oxidized prior to applying the coating composition. 10. The method of claim 2 wherein the coating composition consists essentially of alumina sol and soluble Mg. 11. The method of claim 1 wherein the alumina precursor comprises an alumina sol. 12. The method of claim 2 wherein the coating composition comprises an alumina sol and soluble Mg, and wherein the catalytic metal comprises ruthenium, rhodium, iridium, nickel, palladium, platinum, or combinations thereof. 13. The method of claim 1 wherein, during hydrothermal pre-aging, the H2O partial pressure is in the range of 1 to 25 atm. 14. The method of claim 13 wherein, during hydrothermal pre-aging, the temperature is 900-925° C. 15. The method of claim 7 wherein the substrate comprises a microchannel wall.