초록 ▼

An opacifying pigment that includes a pigment particle having an average particle diameter of from 0.005 to 5 microns and an index of refraction of at least 1.8 such as, for example TiO2, at least partially encapsulated in polymer is provided. Also provided are processes for forming the encapsulated

An opacifying pigment that includes a pigment particle having an average particle diameter of from 0.005 to 5 microns and an index of refraction of at least 1.8 such as, for example TiO2, at least partially encapsulated in polymer is provided. Also provided are processes for forming the encapsulated pigment particle and compositions including the encapsulated pigment particle.

대표청구항 ▼

1. An opacifying pigment encapsulated in polymer comprising: 1) a pigment particle having an average particle diameter of from 0.005 to 5 microns and an index of refraction of at least 1.8;2) from 0.1% to 25% by weight, based on the weight of the pigment particle, of a water-soluble first polymer, t

1. An opacifying pigment encapsulated in polymer comprising: 1) a pigment particle having an average particle diameter of from 0.005 to 5 microns and an index of refraction of at least 1.8;2) from 0.1% to 25% by weight, based on the weight of the pigment particle, of a water-soluble first polymer, the molecular weight of which is controlled by 0 to 10 weight percent, based on the weight of the water-soluble first polymer, of an alkyl mercaptan or an alcohol or a halogenated compound, which water-soluble first polymer consists essentially of: a) at least three moieties of a sulfur acid monomer or a salt thereof; andb) structural units of at least one other monomer selected from the group consisting of an amine functional monomer; styrene; vinyl toluene; vinyl acetate; vinyl versatate; acrylonitrile; (meth)acrylamide; C1-C40 esters of (meth)acrylic acid; alcohol containing monomers; and ethylenically unsaturated mono-, di- and trialkyl esters of ethylenically unsaturated carboxylic acids and anhydrides; and3) from 10% to 200% by weight, based on the weight of the pigment particle a second polymer that at least partially encapsulates the pigment particle. 2. The opacifying pigment encapsulated in polymer of claim 1 wherein 1) the pigment particle is TiO2;2) the sulfur acid monomer is selected from the group consisting of sulfoethyl (meth)acrylate; 2-(meth)acrylamido-2-methylpropane sulfonic acid; styrene sulfonic acid; and vinyl sulfonic acid; and salts thereof; and3) the at least one other monomer is selected from the group consisting of dimethylaminoethyl (meth)acrylate; dimethylaminopropyl (meth)acrylamide; t-butylaminoethyl (meth)acrylate; methyl (meth)acrylate; ethyl (meth)acrylate; butyl (meth)acrylate; 2-ethylhexyl acrylate; acrylic acid; methacrylic acid; itaconic acid; styrene; vinyl acetate; hydroxyethyl (meth)acrylate; maleic acid; and maleic anhydride. 3. The opacifying pigment encapsulated in polymer of claim 1 wherein the water-soluble first polymer consists essentially of: a) at least three moieties of a sulfur acid monomer selected from the group consisting of sulfoethyl methacrylate and 2-acrylamido-2-methylpropane sulfonic acid and salts thereof;b) an amine monomer selected from the group consisting of dimethylaminoethyl (meth)acrylate; dimethylaminopropyl (meth)acrylamide; and t-butylaminoethyl (meth)acrylate; andc) structural units of at least one other monomer selected from the group consisting of methyl methacrylate; ethyl acrylate; butyl acrylate; 2-ethylhexyl acrylate; acrylic acid; methacrylic acid; itaconic acid; styrene; vinyl acetate; hydroxyethyl (meth)acrylate; maleic acid; and maleic anhydride. 4. The opacifying pigment encapsulated in polymer of claim 2 wherein the water-soluble first polymer consists essentially of structural units of 2-acrylamido-2-methylpropane sulfonic acid; dimethylaminoethyl methacrylate; butyl acrylate; and methyl methacrylate; wherein the second polymer completely encapsulates the TiO2 particle. 5. The opacifying pigment encapsulated in polymer of claim 1 wherein the second polymer comprises at least two phases, wherein one polymer phase has a Tg greater than or equal to 45° C., and one polymer phase has a Tg less than or equal to 12° C. 6. The opacifying pigment encapsulated in polymer of claim 1 wherein the second polymer comprises structural units of a sulfur acid monomer or a salt thereof. 7. The opacifying pigment encapsulated in polymer of claim 6 wherein second polymer comprises structural units of styrene sulfonic acid or a salt thereof, and wherein the molecular weight of the water-soluble first polymer is controlled by an alkyl mercaptan. 8. A process comprising: 1) dispersing opacifying pigment particles having an average particle diameter of from 0.005 to 5 microns and an index of refraction of at least 1.8; with a water-soluble first polymer, the molecular weight of which is controlled by 0 to 10 weight percent, based on the weight of the water-soluble first polymer, of an alkyl mercaptan or an alcohol or a halogenated compound, which water-soluble first polymer consists essentially of: a) at least three moieties of a sulfur acid monomer or a salt thereof; andb) structural units of at least one other monomer selected from the group consisting of an amine functional monomer; styrene; vinyl toluene; vinyl acetate; vinyl versatate; acrylonitrile; (meth)acrylamide; C1-C40 esters of (meth)acrylic acid; alcohol containing monomers; and ethylenically unsaturated mono-, di- and trialkyl esters of ethylenically unsaturated carboxylic acids and anhydrides; and2) contacting the dispersion of step 1) with an aqueous dispersion of a monomer emulsion under emulsion polymerization conditions to form opacifying pigment particles at least partially encapsulated in 10 to 200 weight percent, based on the weight of the pigment particles, of a second polymer. 9. The process of claim 8 wherein the at least one other monomer is selected from the group consisting of dimethylaminoethyl (meth)acrylate; dimethylaminopropyl (meth)acrylamide; t-butylaminoethyl (meth)acrylate; methyl (meth)acrylate; ethyl (meth)acrylate; butyl (meth)acrylate; 2-ethylhexyl acrylate; acrylic acid; methacrylic acid; itaconic acid; styrene; vinyl acetate; hydroxyethyl (meth)acrylate; maleic acid; and maleic anhydride. 10. The process of claim 8 wherein the water-soluble first polymer consists essentially of: a) at least three moieties of a sulfur acid monomer selected from the group consisting of sulfoethyl methacrylate and 2-acrylamido-2-methylpropane sulfonic acid and salts thereof;b) an amine monomer selected from the group consisting of dimethylaminoethyl (meth)acrylate; dimethylaminopropyl (meth)acrylamide; and t-butylaminoethyl (meth)acrylate; andc) structural units of at least one other monomer selected from the group consisting of methyl methacrylate; ethyl acrylate; butyl acrylate; 2-ethylhexyl acrylate; acrylic acid; methacrylic acid; itaconic acid; styrene; vinyl acetate; hydroxyethyl (meth)acrylate; maleic acid; and maleic anhydride. 11. The process of claim 8 wherein 1) the pigment particles are TiO2 particles totally encapsulated in the second polymer; and2) the water-soluble first polymer consists essentially of structural units of 2-acrylamido-2-methylpropane sulfonic acid; dimethylaminoethyl methacrylate; butyl acrylate; and methyl methacrylate; whereinthe dispersion from step 1) is further contacted with from 0.1 to 20 percent by weight, based on the weight of monomers in the monomer emulsion, of a sulfur acid monomer. 12. The process of claim 11 wherein the sulfur acid monomer or salt thereof comprises from 0.25 to 5 percent by weight, based on the weight of the monomers, of styrene sulfonic acid or a salt thereof, wherein the molecular weight of the water-soluble first polymer is controlled by an alkyl mercaptan.