Method for producing vinylidene fluoride resin transparent film
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B32B-037/08
B32B-037/15
B32B-027/16
B32B-027/28
B32B-027/30
출원번호
US-0287992
(2008-10-15)
등록번호
US-8303875
(2012-11-06)
우선권정보
JP-2004-234790 (2004-08-11)
발명자
/ 주소
Wada, Kazuhito
Shimamoto, Yukihiro
출원인 / 주소
Kaneka Corporation
대리인 / 주소
Hamre, Schumann, Mueller & Larson, P.C.
인용정보
피인용 횟수 :
0인용 특허 :
30
초록▼
A method for producing a vinylidene fluoride resin film having excellent transparency, weather resistance, chemical resistance, break resistance and formability is provided. The film is shaped by sandwiching a vinylidene fluoride resin in a molten state between rollers or metal belts so as to let th
A method for producing a vinylidene fluoride resin film having excellent transparency, weather resistance, chemical resistance, break resistance and formability is provided. The film is shaped by sandwiching a vinylidene fluoride resin in a molten state between rollers or metal belts so as to let them cool down, thus realizing polyvinylidene fluoride with a fine average spherocrystal diameter. Thus, the vinylidene fluoride resin film having the above-stated properties can be obtained.
대표청구항▼
1. A method for producing a vinylidene fluoride resin film that includes a vinylidene fluoride resin layer as a surface layer and a methacrylic resin composition (C) layer as a base layer, the base layer being laminated on one side of the surface layer, the method comprising: shaping a vinylidene fl
1. A method for producing a vinylidene fluoride resin film that includes a vinylidene fluoride resin layer as a surface layer and a methacrylic resin composition (C) layer as a base layer, the base layer being laminated on one side of the surface layer, the method comprising: shaping a vinylidene fluoride resin in a molten state as the surface layer and a methacrylic resin composition (C) as the base layer by sandwiching the vinylidene fluoride resin and the methacrylic resin composition (C) between rollers or metal belts at a temperature of 10° C. to 100° C. so as to cool down the vinylidene fluoride resin and the methacrylic resin composition (C),wherein an average spherocrystal diameter of polyvinylidene fluoride in the produced vinylidene fluoride resin film is less than 1.0 μm by observation using a transmission electron microscope. 2. The method for producing the vinylidene fluoride resin film according to claim 1, wherein a melting point of the vinylidene fluoride resin ranges from 145° C. to 180° C. 3. The method for producing the vinylidene fluoride resin film according to claim 1, wherein the average spherocrystal diameter of the polyvinylidene fluoride in the produced film is less than 0.1 μM by observation using a transmission electron microscope. 4. The method for producing the vinylidene fluoride resin film according to claim 1, wherein a haze of the vinylidene fluoride resin film is less than 1%. 5. The method for producing the vinylidene fluoride resin film according to claim 1, wherein the vinylidene fluoride resin is a composition comprising 50 to 99.9 parts by weight of a vinylidene fluoride resin (D) and 0.1 to 50 parts by weight of a methacrylic resin composition (C). 6. The method for producing the vinylidene fluoride resin film according to claim 5, wherein the methacrylic resin composition (C) is a methacrylic resin composition obtained by polymerization of a methacrylate polymer (A) in the presence of acrylate crosslinked elastic particles (B),wherein:(1) the methacrylate polymer (A) is obtained by polymerization of a monomer mixture comprising 50 to 100 weight % of alkyl methacrylate and 0 to 50 weight % of alkyl acrylate;(2) the acrylate crosslinked elastic particles (B) are obtained by copolymerization of a monomer mixture (b) comprising 50 to 100 weight % of alkyl acrylate and 50 to 0 weight % of alkyl methacrylate and a multi-functionality monomer having two or more non-conjugated double bonds per one molecule;(3) 5 to 45 weight % of the acrylate crosslinked elastic particles (B) are contained; and(4) 0.01 to 30 parts by weight of an ultraviolet absorber indicated by following formula (1) is copolymerized with respect to 100 parts by weight of the methacrylic resin composition (C); where X denotes H or halogen, R1 denotes H, a methyl group, or a t-alkyl group with a carbon number of 4 to 6, R2 denotes an alkylene group with a carbon number of 2 to 10 in a straight chain shape or a branch shape, and R3 denotes H or a methyl group. 7. A method for producing a vinylidene fluoride resin film comprising; co-extruding a vinylidene fluoride resin composition and a methacrylic resin composition; andshaping the co-extruded compositions by sandwiching the co-extruded compositions between rollers or metal belts at a temperature of 10° C. to 100° C. so as to cool down the co-extruded compositions,wherein an average spherocrystal diameter of polyvinylidene fluoride of the produced film is less than 1.0 μm by observation using a transmission electron microscope. 8. The method for producing the vinylidene fluoride resin film according to claim 7, wherein a temperature of the rollers or the metal belts is made different between the vinylidene fluoride resin composition side and the methacrylic resin composition side. 9. The method for producing the vinylidene fluoride resin film according to claim 7, wherein a temperature of the rollers or the metal belts is kept at 10° C. to 80° C. on the vinylidene fluoride resin composition side and at 10° C. to 100° C. on the methacrylic resin composition side. 10. The method for producing the vinylidene fluoride resin film according to claim 7, wherein a melting point of the vinylidene fluoride resin ranges from 145 to 180° C. 11. The method for producing the vinylidene fluoride resin film according to claim 7, wherein the average spherocrystal diameter of the polyvinylidene fluoride of the film produced is less than 0.1 μm by observation using a transmission electron microscope. 12. The method for producing the vinylidene fluoride resin film according to claim 7, wherein a haze of the vinylidene fluoride resin film is less than 1%. 13. The method for producing the vinylidene fluoride resin film according to claim 7, wherein the vinylidene fluoride resin is a composition comprising 50 to 99.9 parts by weight of a vinylidene fluoride resin (D) and 0.1 to 50 parts by weight of a methacrylic resin composition (C). 14. The method for producing the vinylidene fluoride resin film according to claim 12, wherein the methacrylic resin composition (C) is a methacrylic resin composition obtained by polymerization of a methacrylate polymer (A) in the presence of acrylate crosslinked elastic particles (B),wherein:(1) the methacrylate polymer (A) is obtained by polymerization of a monomer mixture comprising 50 to 100 weight % of alkyl methacrylate and 0 to 50 weight % of alkyl acrylate;(2) the acrylate crosslinked elastic particles (B) are obtained by copolymerization of a monomer mixture (b) comprising 50 to 100 weight % of alkyl acrylate and 50 to 0 weight % of alkyl methacrylate and a multi-functionality monomer having two or more non-conjugated double bonds per one molecule;(3) 5 to 45 weight % of the acrylate crosslinked elastic particles (B) are contained; and(4) 0.01 to 30 parts by weight of an ultraviolet absorber indicated by following formula (I) is copolymerized with respect to 100 parts by weight of the methacrylic resin composition (C); where X denotes H or halogen, R1 denotes H, a methyl group, or a t-alkyl group with a carbon number of 4 to 6, R2 denotes an alkylene group with a carbon number of 2 to 10 in a straight chain shape or a branch shape, and R3 denotes H or a methyl group.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (30)
Beard Charles D. (Sierra Madre CA) Doddi Namassivaya (Upland CA) Yamada Akira (Kyoto JPX), 2′-hydroxy-5′-(hydroxyalkyl)phenyl-2H-benzotriazoles.
Ken Okanishi JP; Minoru Yoshida JP; Tatsuo Suzuki JP; Tetsuo Shimizu JP; Takahisa Aoyama JP, Agent for minimizing size of spherulite of crystalline fluorine-containing resin and crystalline resin and crystalline fluorine-containing resin composition comprising said agent.
Sempio Carlo (Busto Arsizio ITX) Anghileri Andrea (Milan ITX) Binaghi Marc (Milan ITX) Ronchetti Tullo (Milan ITX) Vailati Italo (Castelanza ITX), Coextruded multilayer and a process for preparing the same.
Bertelo Chris ; Meunier Gilles,FRX ; Lermite Andre,FRX ; Dargelos Pascale,FRX ; Drujon Xavier,FRX, Impact additive of the core/shell type for thermoplastic polymers.
Kitaike, Yukio; Abe, Yoshinori; Abe, Junichi; Kitashima, Koichiro; Okazaki, Shogo; Fujii, Hideyuki, Multilayer structure polymer and resin composition together with acrylic resin film material, acrylic resin laminate film, photocurable acrylic resin film or sheet, laminate film or sheet and laminate molding obtained by laminating thereof.
Lindner Christian (Cologne DEX) Uerdingen Walter (Leverkusen DEX) Ott Karl-Heinz (Leverkusen DEX) Braese hans-Eberhard (Cologne DEX), Thermoplastic moulding compositions with high notched impact strength.
Beard Charles D. (Sierra Madre CA) Yamada Akira (Kyoto CA JPX) Doddi Namassivaya (Upland CA), Ultraviolet absorbing polymers comprising 2-hydroxy-5-acrylyloxyphenyl-2H-benzotriazoles.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.