초록 ▼

A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor

A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

대표청구항 ▼

1. A holding seal material comprising: alumina-silica based fibers aggregated into a mat shape as a constituent element of the holding seal material, andsaid alumina-silica based fibers placed in a gap between a ceramic body capable of allowing a fluid to flow through the inside thereof and a metal

1. A holding seal material comprising: alumina-silica based fibers aggregated into a mat shape as a constituent element of the holding seal material, andsaid alumina-silica based fibers placed in a gap between a ceramic body capable of allowing a fluid to flow through the inside thereof and a metal shell covering the outer circumference of the ceramic body, whereinat least one of said alumina-silica based fibers has a deformed shape in its cross-section,at least one of said alumina-silica based fibers comprises an elongated hollow fiber. 2. The holding seal material according to claim 1, wherein said alumina-silica based fibers comprise fibers branched together by a ceramic cross linking bridge in an overlapping area of the alumina-silica based fibers. 3. The holding seal material according to claim 1, wherein said alumina-silica based fiber has a flat shape in its cross-section comprising at least one substantially flat side. 4. The holding seal material according to claim 1, wherein said alumina-silica based fiber has a substantially cocoon shape in its cross-section. 5. The holding seal material according to claim 1, wherein said alumina-silica based fiber is chopped from longer fibers. 6. The holding seal material according to claim 1, wherein said ceramic body includes a catalyst carrier, and said holding seal material is used as a holding seal material for a catalyst converter. 7. A method for manufacturing the holding seal material according to one of claims 1-6, comprising: a spinning step for obtaining a precursor fiber comprising an alumina-silica based fiber by using a spinning stock solution prepared by using an inorganic salt;a sintering step for heating and sintering the precursor fiber;a cutting step for chopping a long fiber of the resultant precursor fiber into a predetermined length to obtain a short fiber; anda forming step for three-dimensionally aggregating the short fiber to form a mat-shaped fiber aggregation. 8. The holding seal material according to claim 1, wherein said alumina-silica based fiber has a substantially elliptical shape in its cross section. 9. The holding seal material according to claim 8, wherein said alumina-silica based fiber with the substantially elliptical shape in its cross section has an oblateness ratio of a minor axis to a major axis ranging from 1:1.1 to 1:3. 10. The holding seal material according to claim 1, further including a ceramic cross linking bridge comprising at least one of zirconia, titania, yttria, ceria, calcia, magnesia, and silica. 11. The holding seal material according to claim 1, wherein the elongated hollow fiber has an opening extending completely through the fiber. 12. The holding seal material according to claim 1, further comprising: a ceramic cross linking bridge adjoining adjacent ones of the alumina-silica based fibers together. 13. The holding seal material according to claim 12, wherein the ceramic cross linking bridge adjoins adjacent ones of the alumina-silica based fibers together in an overlapping area of the alumina-silica based fibers.