초록 ▼

Desirable composites of polysiloxane polymers and inorganic nanoparticles can be formed based on the appropriate selection of the surface properties of the particles and the chemical properties of the polymer. High loadings of particles can be achieved with good dispersion through the polymer. The c

Desirable composites of polysiloxane polymers and inorganic nanoparticles can be formed based on the appropriate selection of the surface properties of the particles and the chemical properties of the polymer. High loadings of particles can be achieved with good dispersion through the polymer. The composites can have good optical properties. In some embodiments, the inorganic particles are substantially free of surface modification.

대표청구항 ▼

1. A method for forming a composite, the method comprising: combining well dispersed inorganic particles in a dispersant liquid comprising a polar solvent with a first polysiloxane in a suitable solvent different from the dispersant liquid and miscible with the dispersant liquid for solubilizing the

1. A method for forming a composite, the method comprising: combining well dispersed inorganic particles in a dispersant liquid comprising a polar solvent with a first polysiloxane in a suitable solvent different from the dispersant liquid and miscible with the dispersant liquid for solubilizing the first polysiloxane to form a blend, the inorganic particles having an average particle diameter of no more than about 250 nm and being substantially free of organic surface modification distinct from the polysiloxane, wherein the inorganic particles comprise a metal oxide, a metal nitride or a combination thereof,wherein the first polysiloxane comprises functional side groups, andwherein about 5 number percent to about 50 number percent of the functional side groups comprise aromatic functional groups or polar functional groups selected from the group consisting of —ROH, —RNH2, RSH, —RCN, —RNO, RCOOH, and —RX, where X is F, Cl, Br, or I and R is an organic group. 2. The method of claim 1 wherein the first polysiloxane comprises compatible functional groups that have stabilizing interactions with the inorganic particles. 3. The method of claim 1 wherein the inorganic particles comprise a metal oxide. 4. The method of claim 1 wherein the inorganic particles were synthesized in a flow based process. 5. The method of claim 1 wherein the inorganic particles are dispersed in an alcohol. 6. The method of claim 1 wherein the polysiloxane comprises a polar functional group. 7. The method of claim 1 further comprising combining a second polysiloxane with the blend of the inorganic particles and the first polysiloxane. 8. The method of claim 1 further comprising forming the blend into a desired structure and drying the blend to remove the liquid. 9. The method of claim 1 wherein the inorganic particles comprise a mixture of inorganic particles. 10. A method for the formation of a composite, the method comprising: combining well dispersed inorganic particles in a dispersant liquid comprising a polar solvent with a first polysiloxane in a suitable solvent miscible with the dispersant liquid for solubilizing the first polysiloxane to form a blend, the inorganic particles having an average particle diameter of no more than about 250 nm and being free of organic surface modification distinct from the first polysiloxane, and wherein the inorganic particles comprise a metal oxide, a metal nitride or a combination thereof; andcombining a second polysiloxane with the blend of the inorganic particles and the first polysiloxane wherein the second polysiloxane does not have compatible functional groups,wherein the first polysiloxane comprises functional side groups, andwherein about 5 number percent to about 50 number percent of the functional side groups comprise aromatic functional groups or polar functional groups selected from the group consisting of —ROH, —RNH2, RSH, —RCN, —RNO, RCOOH, and —RX, where X is F, Cl, Br, or I and R is an organic group. 11. The method of claim 10 wherein the resulting composite composition has a loading of at least about 20 weight percent inorganic particles, wherein the composite has a transparency of at least about 90 percent for a selected visible light wavelength when formed into a film having a thickness of 2.5 microns. 12. The method of claim 10 wherein the inorganic particles comprise a metal oxide. 13. The method of claim 10 wherein the first polysiloxane polymer or second polysiloxane comprises a polar functional group. 14. The method of claim 10 wherein the second polysiloxane is an oligomer. 15. The method of claim 10 further comprising forming the blend into a desired structure and drying the blend to remove the liquid. 16. The method of claim 15 wherein the blend comprises at least 15 weight percent of the first polysiloxane polymer after drying.