초록 ▼

A method of making a crosslinked polyimide membrane is described. A monoesterified membrane is formed from a monoesterified polyimide polymer. The monoesterified membrane is subjected to transesterification conditions to form a crosslinked membrane. The monoesterified membrane is incorporated with a

A method of making a crosslinked polyimide membrane is described. A monoesterified membrane is formed from a monoesterified polyimide polymer. The monoesterified membrane is subjected to transesterification conditions to form a crosslinked membrane. The monoesterified membrane is incorporated with an organic titanate catalyst before or after formation of the monoesterified membrane. A crosslinked polyimide membrane made using the aforementioned method and a method of using the membrane to separate fluids in a fluid mixture, such as methane and carbon dioxide, are also disclosed.

대표청구항 ▼

1. A method of making a crosslinked polyimide membrane, comprising: (a) forming a monoesterified membrane from a monoesterified polyimide polymer, and(b) subjecting the monoesterified membrane to transesterification conditions to form a crosslinked fiber membrane; wherein the forming of the monoeste

1. A method of making a crosslinked polyimide membrane, comprising: (a) forming a monoesterified membrane from a monoesterified polyimide polymer, and(b) subjecting the monoesterified membrane to transesterification conditions to form a crosslinked fiber membrane; wherein the forming of the monoesterified membrane includes incorporating an organic titanate catalyst into the monoesterified membrane and the content of the organic titanate is present at between 10 and 50 parts per million by weight of the membrane. 2. The method of claim 1 wherein: the monoesterified polyimide polymer and the organic titanate catalyst are placed together in a solution and then the monesterified membrane is formed. 3. The method of claim 1 wherein: the monoesterified polyimide membrane is formed and then the organic titanate catalyst is imbibed into the monoesterified polyimide membrane. 4. The method of claim 3: the monoesterified polyimide polymer is spun into a hollow fiber membrane and then the organic titanate catalyst is imbibed into the hollow fiber membrane. 5. The method of claim 4 wherein: the organic titanate catalyst is dissolved in a solution which maintains the morphology of the membrane; andthe organic titanate catalyst is imbibed into the membrane. 6. The method of claim 1 wherein: the monoesterified membrane is heated for less than 24 hours to form the crosslinked membrane. 7. The method of claim 1 wherein: the monoesterified membrane is heated for less than 12 hours to form the crosslinked fiber membrane. 8. The method of claim 1 wherein: the mono esterified membrane is heated for less than 6 hours to form the crosslinked fiber membrane. 9. The method of claim 1 wherein: the transesterification conditions include heating the membrane at between 50-200° C. 10. The method of claim 1 wherein: the transesterification conditions include heating the membrane at between 75-150° C. 11. The method of claim 1 wherein: the transesterification conditions include heating the membrane at less than 150° C. 12. The method of claim 1, wherein: the organic titanate catalyst is an alkyl titanate. 13. The method of claim 1, wherein: the organic titanate catalyst is a titanium chelate. 14. A method of making a crosslinked polyimide membrane, comprising: (a) forming a monoesterified membrane from a monoesterified polyimide polymer, and(b) subjecting the monoesterified membrane to transesterification conditions to form a crosslinked fiber membrane; wherein the forming of the monoesterified membrane includes incorporating an organic titanate catalyst into the monoesterified membrane and the content of the organic titanate is present at less than 50 parts per million by weight of the membrane.