초록 ▼

A gas diffusion media for a fuel cell, such as a proton exchange membrane fuel cell, is provided. The gas diffusion media includes carbonizable acrylic pulp fibers instead of conventional phenolic resin as a binder material. The acrylic fibers are mixed with the carbon fiber dispersion during the pa

A gas diffusion media for a fuel cell, such as a proton exchange membrane fuel cell, is provided. The gas diffusion media includes carbonizable acrylic pulp fibers instead of conventional phenolic resin as a binder material. The acrylic fibers are mixed with the carbon fiber dispersion during the papermaking step, thus eliminating the phenolic resin impregnation step typically associated with conventional gas diffusion media manufacturing processes. The mat is then cured and carbonized to produce gas diffusion media.

대표청구항 ▼

1. A gas diffusion layer for use in fuel cells, comprising: a mat comprised of plurality of carbon fibers; anda plurality of acrylic pulp fibers incorporated into the carbon fiber mat;wherein the acrylic pulp fibers are cured and carbonized after incorporation into the carbon fiber mat, and wherein

1. A gas diffusion layer for use in fuel cells, comprising: a mat comprised of plurality of carbon fibers; anda plurality of acrylic pulp fibers incorporated into the carbon fiber mat;wherein the acrylic pulp fibers are cured and carbonized after incorporation into the carbon fiber mat, and wherein the carbon fibers are present in a range of about 25 to about 50 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 2. The invention according to claim 1, wherein the carbon fibers are present in an amount of about 35 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 3. The invention according to claim 1, wherein the acrylic pulp fibers are present in a range of about 50 to about 75 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 4. The invention according to claim 1, wherein the acrylic pulp fibers are present in an amount of about 65 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 5. The invention according to claim 1, wherein the carbon fibers added to the pre-carbonized mat are present in a range of about 40 to about 70 weight percent based on the total weight of the gas diffusion layer after the curing and carbonization step. 6. The invention according to claim 1, wherein the carbonized acrylic fibers are present in a range of about 30 to about 60 weight percent based on the total weight of the gas diffusion layer after the curing and carbonization step. 7. The invention according to claim 1, wherein the gas diffusion layer is incorporated into a proton exchange membrane fuel cell. 8. A gas diffusion layer for use in fuel cells, comprising: a mat comprised of a plurality of carbon fibers; anda plurality of acrylic pulp fibers incorporated into the carbon fiber mat;wherein the acrylic pulp fibers are cured and carbonized after incorporation into the carbon fiber mat;wherein the carbon fibers are present in a range of about 25 to about 50 weight percent based on the total weight of the gas diffusion layer prior to being cured and carbonized;wherein the acrylic pulp fibers are present in a range of about 50 to about 75 weight percent based on the total weight of the gas diffusion layer prior to being cured and carbonized. 9. The invention according to claim 8, wherein the carbon fibers are present in an amount of about 35 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 10. The invention according to claim 8, wherein the acrylic pulp fibers are present in an amount of about 65 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 11. The invention according to claim 8, wherein the carbon fibers added to the pre-carbonized mat are present in a range of about 40 to about 70 weight percent based on the total weight of the gas diffusion layer after the curing and carbonization step. 12. The invention according to claim 8, wherein the carbonized acrylic fibers are present in a range of about 30 to about 60 weight percent based on the total weight of the gas diffusion layer after the curing and carbonization step. 13. The invention according to claim 8, wherein the gas diffusion layer is incorporated into a proton exchange membrane fuel cell. 14. A method for forming a gas diffusion layer for use in fuel cells, comprising: providing a plurality of carbon fibers;providing a plurality of acrylic pulp fibers;combining the acrylic pulp fibers and the carbon fibers to form a mat; andcuring and carbonizing the acrylic fibers, wherein the carbon fibers are present in a range of about 25 to about 50 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 15. The invention according to claim 14, further comprising graphitizing the gas diffusion layer. 16. The invention according to claim 14, wherein the carbon fibers are present in an amount of about 35 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 17. The invention according to claim 14, wherein the acrylic pulp fibers are present in a range of about 50 to about 75 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 18. The invention according to claim 14, wherein the acrylic pulp fibers are present in an amount of about 65 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization. 19. The invention according to claim 14, wherein the carbon fibers added to the pre-carbonized mat are present in a range of about 40 to about 70 weight percent based on the total weight of the gas diffusion layer after the curing and carbonization step. 20. The invention according to claim 14, wherein the carbonized acrylic fibers are present in a range of about 30 to about 60 weight percent based on the total weight of the gas diffusion layer after the curing and carbonization step. 21. The invention according to claim 14, wherein the gas diffusion layer is incorporated into a proton exchange membrane fuel cell. 22. A gas diffusion layer for use in fuel cells, comprising: a mat comprised of plurality of carbon fibers; anda plurality of acrylic pulp fibers incorporated into the carbon fiber mat;wherein the acrylic pulp fibers are cured and carbonized after incorporation into the carbon fiber mat, and wherein the acrylic pulp fibers are present in a range of about 50 to about 75 weight percent based on the total weight of the gas diffusion layer prior to curing and carbonization.