초록 ▼

A cementitious composition the properties of which are useful for: a) reducing shrinkage cracking in stucco systems due to excess water present in initial mixing required to achieve adequate slump necessary for application, but not necessary for material hydration b) reducing full thickness cracking

A cementitious composition the properties of which are useful for: a) reducing shrinkage cracking in stucco systems due to excess water present in initial mixing required to achieve adequate slump necessary for application, but not necessary for material hydration b) reducing full thickness cracking as a result of minor structural movement by increasing the flexural strength, c) reducing the time required to place the layers of a three-coat exterior stucco system. The composition of this material is a blend of ASTM C 150 Portland cement, an ASTM C 1328 Plastic (Stucco) cement and a minor amount of a sulfonated naphthalene formaldehyde condensate (SNF), also described as Polynaphthalene sulfonates (PNS) cement superplasticizer, also known as a HRWR (High Range Water Reducer).

대표청구항 ▼

1. A cementitious composition for use in a one coat or three coat stucco application, the composition comprising: a Portland cement meeting the requirements of ASTM C150 and having a C3A composition greater than about 7% by weight based upon the cement;a Plastic stucco cement meeting the requirement

1. A cementitious composition for use in a one coat or three coat stucco application, the composition comprising: a Portland cement meeting the requirements of ASTM C150 and having a C3A composition greater than about 7% by weight based upon the cement;a Plastic stucco cement meeting the requirements of ASTM C 1328;a sulfonated naphthalene formaldehyde condensate in an amount of from about 8 to about 10 ounces per hundredweight of cement;wherein the Portland cement and Plastic stucco cement are present in a ratio sufficient for the composition to have a C3A content greater than 7% by weight based upon the cement, an initial set time of from about 90 to about 150 minutes, an amount of air entrainment from about 8 to about 20 percent, and a surface area greater than about 5300 cm/g. 2. The composition of claim 1 wherein the composition has a water demand of from 0.38 to about 0.41. 3. The composition of claim 1 wherein the sulfonated naphthalene formaldehyde condensate is powdered. 4. The composition of claim 3 wherein the sulfonated naphthalene formaldehyde condensate has a molecular weight of about 12,000 grams per mole. 5. The composition of claim 1 wherein the C3A content of the composition is less than about 8% by weight based upon the cement. 6. The composition of claim 1 wherein the surface area is greater than about 5800 cm/g. 7. The composition of claim 1 wherein the initial set time is greater than about 100 minutes. 8. The composition of claim 1 wherein the flexural strength of the composition is greater than 1,000 psi at 7 days after application. 9. The composition of claim 1 wherein the compressive strength of the composition is greater than about 8,000 pounds at 28 days after application. 10. The composition of claim 1 wherein the Portland cement is selected from the group consisting of Type I, Type II, Type V, or Type III, and mixtures thereof. 11. The composition of claim 10 wherein the Portland cement is Type III Portland cement. 12. The composition of claim 1 wherein the composition has a strength greater than about 2690 in 24 hours after application. 13. A cementitious composition for use in a one coat or three coat stucco application, the composition comprising: a Type III Portland cement meeting the requirements of ASTM C150 and having a C3A composition greater than 7%;a Plastic stucco cement meeting the requirements of ASTM C 1328;a sulfonated naphthalene formaldehyde condensate in an amount of from about 8 to about 10 ounces per hundredweight of cement;wherein the Type III Portland cement and Plastic stucco cement are present in ratio of from 40:60 to 60:40 by weight;wherein the composition has a C3A content greater than 7% by weight based upon the cement, an initial set time of from about 90 to about 150 minutes, an amount of air entrainment from about 8 to about 20 percent, and a surface area greater than about 5300 cm/g;wherein the composition is adapted for use in a stucco application where sulfate attack is an issue. 14. The composition of claim 13 wherein the ratio of Type III Portland cement to Plastic cement is about 50:50 by weight. 15. The composition of claim 13 wherein the composition has a water demand of from 0.38 to about 0.41. 16. The composition of claim 13 wherein the sulfonated naphthalene formaldehyde condensate is powdered. 17. The composition of claim 16 wherein the sulfonated naphthalene formaldehyde condensate has a molecular weight of about 12,000 grams per mole. 18. The composition of claim 13 wherein the C3A content of the composition is less than about 8% by weight based upon the cement. 19. The composition of claim 13 wherein the surface area is greater than about 5800 cm/g.