초록 ▼

Methods of forming composite materials include coating particles of titanium dioxide with a substance including boron (e.g., boron carbide) and a substance including carbon, and reacting the titanium dioxide with the substance including boron and the substance including carbon to form titanium dibor

Methods of forming composite materials include coating particles of titanium dioxide with a substance including boron (e.g., boron carbide) and a substance including carbon, and reacting the titanium dioxide with the substance including boron and the substance including carbon to form titanium diboride. The methods may be used to form ceramic composite bodies and materials, such as, for example, a ceramic composite body or material including silicon carbide and titanium diboride. Such bodies and materials may be used as armor bodies and armor materials. Such methods may include forming a green body and sintering the green body to a desirable final density. Green bodies formed in accordance with such methods may include particles comprising titanium dioxide and a coating at least partially covering exterior surfaces thereof, the coating comprising a substance including boron (e.g., boron carbide) and a substance including carbon.

대표청구항 ▼

1. A method of forming a composite material, comprising the following steps in the sequence set forth: (1) at least partially coating particles comprising titanium dioxide (TiO2) with boron carbide (B4C) and a carbon source to form coated particles;(2) mixing the coated particles with silicon carbid

1. A method of forming a composite material, comprising the following steps in the sequence set forth: (1) at least partially coating particles comprising titanium dioxide (TiO2) with boron carbide (B4C) and a carbon source to form coated particles;(2) mixing the coated particles with silicon carbide (SiC) particles to form a particle mixture;(3) forming a green body from the particle mixture; and(4) sintering the green body, comprising: (a) reacting the titanium dioxide (TiO2) with the boron carbide (B4C) and carbon of the carbon source to form titanium diboride (TiB2); and(b) forming a sintered body comprising grains of titanium diboride (TiB2) dispersed substantially throughout a matrix comprising silicon carbide (SiC). 2. The method of claim 1, wherein at least partially coating particles comprising titanium dioxide (TiO2) comprises at least partially coating titanium dioxide (TiO2) particles. 3. The method of claim 1, wherein at least partially coating particles comprising titanium dioxide (TiO2) comprises at least partially coating oxidized titanium diboride (TiB2) particles. 4. The method of claim 1, where step (1) comprises at least partially coating particles comprising titanium dioxide (TiO2) with a polymeric material. 5. The method of claim 4, therein at least partially coating particles comprising titanium dioxide (TiO2) with the polymeric material comprises at least partially coating particles comprising titanium dioxide (TiO2) pith a phenolic polymer material. 6. The method of claim 4, wherein step (1) comprises: (a) mixing titanium dioxide (TiO2) particles, boron carbide (B4C) particles, the polymeric material, and a solvent to form a slurry; and, (b) drying the slurry to form the coated particles. 7. The method of claim 6, further comprising the step of thermally treating the partially coated particles to convert the carbon source into substantially pure carbon. 8. The method of claim 7, wherein the thermal treatment comprises heating the partially coated particles at a temperature between about 600° C. and about 900° C. 9. The method of claim 7, further comprising the step of crushing the partially coated and treated particles to reduce the average particle size. 10. The method of claim 1, further comprising providing a molar ratio of titanium dioxide (TiO2) to boron carbide (B4C) in the particle mixture of between about 1:1 and about 2:1. 11. The method of claim 10, further comprising providing a molar ratio of titanium dioxide (TiO2) to boron carbide (B4C) in the particle mixture of about 5:3. 12. The method of claim 10, further comprising providing a molar ratio of titanium dioxide (TiO2) to carbon of the carbon source in the particle mixture of between about 1:1 and about 2:3. 13. A method of forming an armor component, the method comprising the following steps in the sequence set forth: (1) at least partially coating particles comprising titanium dioxide (TiO2) with boron carbide (B4C) and a carbon source to form coated particles;(2) mixing the coated particles with silicon carbide (SiC) particles to form a particle mixture;(3) forming a green armor component from the particle mixture;(4) sintering the green armor component to form an at least substantially fully sintered armor component, sintering the green armor component comprising reacting the titanium dioxide (TiO2) with the boron carbide (B4C) and the carbon to form titanium diboride (TiB2). 14. The method of claim 13, wherein step (1) comprises: (a) mixing titanium dioxide (TiO2) particles, boron carbide (B4C) particles, the carbon source, and a liquid solvent to form a slurry; and(b) drying the slurry to form the coated particles. 15. The method of claim 14, wherein sintering the green armor component comprises heating the green armor component in a furnace to a temperature of about 2000° C. or more at a pressure of about five (5.0) pounds per square inch gauge (psig) or less.