초록 ▼

Composite structures are described that have a porous anodic oxide layer such as, for example, a porous anodic aluminum oxide layer. In one aspect, the present invention includes a composite gas separation module having a porous metal substrate; a porous anodic aluminum oxide layer, wherein the poro

Composite structures are described that have a porous anodic oxide layer such as, for example, a porous anodic aluminum oxide layer. In one aspect, the present invention includes a composite gas separation module having a porous metal substrate; a porous anodic aluminum oxide layer, wherein the porous anodic aluminum oxide layer overlies the porous metal substrate; and a dense gas-selective membrane, wherein the dense gas-selective membrane overlies the porous anodic aluminum oxide layer. A composite filter is described having a porous non-aluminum metal substrate; and a porous anodic aluminum oxide layer, wherein the porous anodic aluminum oxide layer defines pores extending through the porous anodic aluminum oxide layer. Methods for fabricating composite gas separation modules and composite filters and methods for selectively separating hydrogen gas from a hydrogen gas-containing gaseous stream are also described.

대표청구항 ▼

1. A composite gas separation module, comprising: a) a porous metal substrate of at least one member selected from the group consisting of stainless steel, chromium and nickel;b) a porous anodic aluminum oxide layer, wherein the porous anodic aluminum oxide layer overlies the porous metal substrate;

1. A composite gas separation module, comprising: a) a porous metal substrate of at least one member selected from the group consisting of stainless steel, chromium and nickel;b) a porous anodic aluminum oxide layer, wherein the porous anodic aluminum oxide layer overlies the porous metal substrate; andc) a dense gas-selective membrane, wherein the dense gas-selective membrane overlies the porous anodic aluminum oxide layer. 2. The composite gas separation module of claim 1 wherein the dense gas-selective membrane is a dense hydrogen-selective membrane. 3. The composite gas separation module of claim 2 wherein the dense hydrogen-selective membrane includes palladium or an alloy thereof. 4. A composite filter, comprising: a) a porous non-aluminum metal substrate of stainless steel; andb) a porous anodic aluminum oxide layer, wherein the porous anodic aluminum oxide layer overlies the porous non-aluminum metal substrate, and wherein the porous anodic aluminum oxide layer defines pores extending from a first side of the porous anodic aluminum oxide layer through the porous anodic aluminum oxide layer to a second side of the porous anodic aluminum oxide layer. 5. The composite filter of claim 4 wherein the porous non-aluminum metal substrate defines pores having an first mean pore diameter, wherein the porous anodic aluminum oxide layer defines pores having a second mean pore diameter, and wherein the second mean pore diameter is less than the first mean pore diameter. 6. The composite filter of claim 5 wherein the second mean pore diameter is less than half of the first mean pore diameter. 7. A method for fabricating a composite gas separation module, comprising the steps of: a) applying an aluminum metal layer over a porous metal substrate;b) oxidizing the aluminum metal layer by anodic oxidation, thereby forming a first anodic aluminum oxide layer;c) removing at least a portion of the first anodic aluminum oxide layer, thereby forming a template, wherein the template includes unoxidized aluminum metal;d) oxidizing the aluminum metal of the template by anodic oxidation, thereby forming the porous anodic aluminum oxide layer; ande) applying a dense gas-selective membrane over the porous anodic aluminum oxide layer, thereby forming the composite gas separation module. 8. The method of claim 7 wherein the gas-selective membrane is a hydrogen-selective membrane. 9. A method for fabricating a composite filter, comprising: a) applying an aluminum metal layer over a porous non-aluminum metal substrate;b) oxidizing the aluminum metal layer by anodic oxidation, thereby forming a first anodic aluminum oxide layer;c) removing at least a portion of the first anodic aluminum oxide layer, thereby forming a template, wherein the template includes unoxidized aluminum metal; andd) oxidizing the aluminum metal of the template by anodic oxidation, thereby forming a porous anodic aluminum oxide layer. 10. The method of claim 9 wherein the porous anodic aluminum oxide layer includes non-porous anodic aluminum oxide and further comprising removing at least a portion of the non-porous anodic aluminum oxide from the porous anodic aluminum oxide layer. 11. The method of claim 7 further including annealing the aluminum metal layer in an atmosphere comprising an inert gas and hydrogen gas.