High SRI cementitious systems comprising integral concrete coloring admixtures, toppings, dry-shake hardeners, and other cementitious systems are provided. The high-SRI cementitious systems comprise one or more IR reflective pigments and other components to make-up the cementitious system, depending
High SRI cementitious systems comprising integral concrete coloring admixtures, toppings, dry-shake hardeners, and other cementitious systems are provided. The high-SRI cementitious systems comprise one or more IR reflective pigments and other components to make-up the cementitious system, depending on the application. The high-SRI cementitious systems of the invention may be in the form of mixtures which increase the total solar reflectivity (TSR or albedo) and the Solar Reflectance Index (SRI) of concrete. The high-SRI cementitious systems may be toppings mixed with water for application to existing concrete surfaces, dry-shake hardeners for application to freshly-placed plastic concrete, or the IR reflective pigments may be mixed into integrally colored concrete in various forms, such as conventional cast-in-place concrete, lightweight concrete, pervious concrete and concrete building panels, pavers or masonry units. The topping and dry-shake hardener formulations of the invention may further comprise one or more of cementitious binder(s), graded aggregates, super-plasticizers, one or more pigments selected for improving infrared reflectivity and color composition, and/or optionally other additives, such as dry redispersible polymers or fillers to provide decorative and LEED compliant, highly durable (sustainable) concrete hardscapes and other decorative concrete.
대표청구항▼
1. A method of preparing a high-SRI colored concrete using a high-SRI cementitious system the method comprising: (a) providing components of a cementitious system comprising a cementitious matrix or concrete coloring admixture;(b) combining an infrared reflective pigment composition with the cementi
1. A method of preparing a high-SRI colored concrete using a high-SRI cementitious system the method comprising: (a) providing components of a cementitious system comprising a cementitious matrix or concrete coloring admixture;(b) combining an infrared reflective pigment composition with the cementitious system to form the high-SRI cementitious system, wherein the infrared reflective pigment composition comprises:one or more infrared reflective pigments selected from the group consisting of: black infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 40%, red infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; orange to yellow infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 65%; beige to brown infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; green infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; blue infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 50%; gray to white infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; and combinations thereof, wherein the percent reflectance at 1000 nm is measured in white portland cement, and wherein the infrared reflective pigments are compliant with ASTM C979; and(c) applying the high-SRI cementitious system to a concrete to form the high-SRI colored concrete, wherein the high-SRI cementitious system has an SRI value of at least 29 SRI units, and wherein the high-SRI cementitious system is selected from the group consisting of a topping, a dry-shake color hardener, and an integral concrete coloring admixture. 2. The method according to claim 1 wherein the high-SRI cementitious system-comprises a topping for applying to hardened concrete. 3. The method according to claim 1 wherein the high-SRI cementitious system comprises a dry-shake color hardener for applying to freshly placed concrete. 4. The method according to claim 1 wherein the high-SRI cementitious system comprises an integral concrete coloring admixture used in a conventional cast-in-place concrete. 5. The method according to claim 1 wherein the high-SRI cementitious system comprises an integral concrete coloring admixture used in lightweight concrete. 6. The method according to claim 1 wherein the high-SRI cementitious system comprises an integral concrete coloring admixture used in pervious concrete. 7. The method according to claim 1 wherein the high-SRI cementitious system comprises an integral concrete coloring admixture used in concrete cast into manufactured building panels or pavers, and the infrared reflective pigments are added to the concrete during mixing of the wet concrete, and before casting the manufactured building panels or pavers. 8. The method according to claim 1 wherein the high-SRI cementitious system comprises an integral concrete coloring admixture or cementitious matrix, and the pigment composition comprises a blend of brown and black CICP pigments having a % reflectance at 1000 nm of at least 5% and less than 40% with one or more black infrared reflective pigments having a % reflectance at 1000 nm of at least 40% to meet an SRI requirement of 32 or higher. 9. The method according to claim 1 wherein the high-SRI cementitious system has an SRI value of at least 32 SRI units. 10. The method according to claim 1 wherein the high-SRI cementitious system has an SRI value of at least 40 SRI units. 11. The method according to claim 1 wherein the black infrared reflective pigments are selected from the group consisting of: manganese-vanadium oxide spinels, chromium green-black hematites, aluminum- and titanium-doped chromium green-black modified hematites, chromium iron oxides, hematite chromium green-blacks, iron chromite brown spinels, manganese ferrite spinels, chromium iron nickel black spinels, perylene blacks- and combinations thereof. 12. The method according to claim 1 wherein the black infrared reflective pigment is a complex inorganic colored black pigment (CICP). 13. The method according to claim 1 wherein the red infrared reflective pigments are selected from the group consisting of: o-chloro-p-nitroaniline coupled β-napthols, m-nitro-p-toluidine coupled with β-napthols, diazotized p-aminobenzamide coupled with BON-o-phentidines, diketo-pyyrolo-pyrrole reds, high IR iron (III) oxide hematites, cerium sesquisulfides, quinacridone magenta B, pigment red 149, perylene reds, and combinations thereof. 14. The method according to claim 13 wherein the red infrared reflective pigments are an iron (III) oxide hematite, a cerium sesquisulfide, or a combination thereof. 15. The method according to claim 1 wherein the orange to yellow infrared reflective pigments are selected from the group consisting of: benzimidazolone blends, chromium antimony titanate rutiles, o-dianisidine coupled with aceto-acetanilides, dinitraniline coupled with beta-naphthols, insoindoline yellows, o-(2-methoxy-4-nitrophenylhydrazono)-α-aceto-2′-methoxyacetanilides, monoarylide yellows, nickel antimony titanium rutiles, m-nitro-o-anisidine coupled with acetoacet-o-anisidines, potassium cerium sulfides, pyrazolo-quinazolones, quinophthalone yellows, and combinations thereof. 16. The method according to claim 1 wherein the orange to yellow infrared reflective pigments are a nickel antimony titanium rutile, a chrome antimony titanium rutile, an isoindoline yellow, or a combination thereof. 17. The method according to claim 16 wherein at least one of the orange to yellow infrared reflective pigment is a nickel antimony titanium rutile. 18. The method according to claim 1 wherein the beige to brown infrared reflective pigments are selected from the group consisting of: chrome antimony titanium rutiles, chromium iron oxide spinels, chrome niobium buff rutiles, chrome tungsten titanium rutiles, iron titanium spinels, manganese antimony titanium rutiles, manganese tungsten titanium rutiles, zinc ferrite spinels, zinc iron chromite spinels, manganese ferrite brown spinels, and combinations thereof. 19. The method according to claim 18 wherein at least one of the beige to brown infrared reflective pigment is a manganese antimony titanium rutile. 20. The method according to claim 18 further comprising one or more red, orange, or yellow infrared reflective pigment. 21. The method according to claim 1 wherein the green infrared reflective pigments are selected from the group consisting of: chlorinated copper phthalocyanines, chromium hematites, chromium modified hematites, chromium oxides, cobalt chromite spinels, cobalt chromite spinels, cobalt titanate spinels, and combinations thereof. 22. The method according to claim 1 wherein the green infrared reflective pigments are a chromium hematite, a cobalt chromite spinel, a chromium modified pigment, and combinations thereof. 23. The method according to claim 22 wherein at least one of the green infrared reflective pigments is a cobalt chromite spinel. 24. The method according to claim 1 wherein the blue infrared reflective pigments are selected from the group consisting of: cobalt aluminate spinels, cobalt chromite spinels, cobalt chromium zinc aluminate spinels, cobalt lithium titanate spinels, copper phthalocyanines, indanthrones, and combinations thereof. 25. The method according to claim 24 wherein the blue infrared reflective pigments are a cobalt chromite spinel, a cobalt aluminum spinel, or a combination thereof. 26. The method according to claim 1 wherein the infrared reflective pigments are selected to provide a gray, light gray, dark gray or bright white IR reflective cementitious system, and wherein the pigments are selected from the group consisting of: black infrared reflective pigments, chromium hematites, anatase TiO2, chrome antimony titanium rutiles, and combinations thereof. 27. The method according to claim 1 wherein the infrared reflective pigments are: anatase TiO2 and one or more black infrared reflective pigments; oranatase TiO2 and one or more infrared reflective pigments to produce a pastel color. 28. The method according to claim 1 wherein the black infrared reflective pigments, red infrared reflective pigments; orange to yellow infrared reflective pigments, beige to brown infrared reflective pigments, green infrared reflective pigments, blue infrared reflective pigments, and gray-white infrared reflective pigments are combined with a concrete coloring admixture in a concrete or a cementitious matrix to form an intermediate colored cementitious system. 29. A method of preparing a high-SRI colored concrete using a high-SRI cementitious system, the method comprising: (a) providing components of a cementitious system comprising a cementitious matrix or concrete coloring admixture;(b) combining an infrared reflective pigment composition with the cementitious system to form the high-SRI cementitious system, wherein the infrared reflective pigment composition comprises:one or more infrared reflective pigments selected from the group consisting of: black infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 40%, red infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; orange to yellow infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 65%; beige to brown infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; green infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; blue infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 50%; gray to white infrared reflective pigments having a percent reflectance at 1000 nanometers of at least 60%; and combinations thereof, wherein the percent reflectance at 1000 nm is measured in white portland cement, and wherein the infrared reflective pigments are compliant with ASTM C979; andTiO2 comprising anatase TiO2 or rutile TiO2; and(c) applying the high-SRI cementitious system to a concrete to form the high-SRI colored concrete, wherein the high-SRI cementitious system has an SRI value of at least 29 SRI units, and wherein the high-SRI cementitious system is selected from the group consisting of a topping, a dry-shake color hardener, and an integral concrete coloring admixture. 30. The method according to claim 29 wherein the TiO2 comprises pigment, ultrafine, or photocatalytic grade anatase TiO2, and wherein the TiO2 provides SRI-restoring function upon exposure to UV radiation. 31. The method according to claim 29 wherein the TiO2 comprises low tint strength or non-pigmentary TiO2. 32. The method according to claim 29 wherein the TiO2 comprises low tint strength or non-pigmentary TiO2 and the TiO2 is combined with to improve the overall reflectivity of the cementitious system.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (20)
Robert Michael Sullivan ; Terry James Detrie ; Daniel Russell Swiler, Alkaline earth-manganese oxide pigments.
Supcoe Robert F. (1227 Mt. Pleasant ; Rt. 9 Annapolis MD 21401) Greenberg Melvin (314 Dewey Dr. Annapolis MD 21401), Formulation for producing low infrared coating in the 2-15 micron range.
Modly Zoltan M. (Shaker Heights OH), Pigment consisting of a mixture of chromium oxide and iron oxide useful in high infra red reflectance gray vinyl composi.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.