초록 ▼

Metal oxide nanowires and carbon-coated metal nanowires are effective as supports for particles of an expensive catalyst material, such as platinum metal group catalyst. Such supported catalysts are useful when included in an electrode on, for example, a proton exchange membrane in a hydrogen/oxygen

Metal oxide nanowires and carbon-coated metal nanowires are effective as supports for particles of an expensive catalyst material, such as platinum metal group catalyst. Such supported catalysts are useful when included in an electrode on, for example, a proton exchange membrane in a hydrogen/oxygen fuel cell. For example, tin oxide nanowires are formed on carbon fibers of carbon paper and platinum nanoparticles are deposited on the tin oxide nanowires. The nanowires provide good surfaces for effective utilization of the platinum material.

대표청구항 ▼

1. A method of making a supported catalyst for a fuel cell, the method comprising: forming tin oxide (SnO2) nanowires directly on carbon fibers by oxidative thermal evaporation of tin metal powder in an oxygen-containing inert gas atmosphere to form tin oxide nanowires and depositing the tin oxide n

1. A method of making a supported catalyst for a fuel cell, the method comprising: forming tin oxide (SnO2) nanowires directly on carbon fibers by oxidative thermal evaporation of tin metal powder in an oxygen-containing inert gas atmosphere to form tin oxide nanowires and depositing the tin oxide nanowires from the oxygen-containing inert gas atmosphere on carbon fibers, said tin oxide nanowires comprising a substantially circular cross-sectional shape, said circular cross-sectional shape having a diameter; and thendepositing nanoparticles of a catalytic metal on the tin oxide nanowires formed on the carbon fibers. 2. A method of making a supported catalyst for a fuel cell as recited in claim 1 in which an oxygen-containing inert gas stream is flowed over the tin metal powder. 3. A method of making a supported catalyst for a fuel cell as recited in claim 1 in which an oxygen-containing argon stream is flowed over the tin metal powder. 4. A method of making a supported catalyst as recited in claim 1 in the which deposited catalytic metal comprises a metal of the platinum group of metals, and the catalytic metal is deposited as nanoparticles, either chemically or by cyclic voltammetry, on the tin oxide nanowires formed on the carbon fibers. 5. A method of making a supported catalyst as recited in claim 1 in which surfaces of the deposited tin oxide nanowires are oxidized before depositing of the catalytic metal. 6. A method of making a supported catalyst as recited in claim 1 in which the surfaces of the deposited tin oxide nanowires are oxidized with nitric acid, and then platinum particles are deposited chemically or by cyclic voltammetry on the tin oxide nanowires. 7. A method of making a supported catalyst as recited in claim 1 in which the deposited catalytic metal comprises as metal of the platinum group of metals. 8. A method of making a supported catalyst as recited in claim 1 in which the tin oxide nanowires are formed in an oxygen-containing argon atmosphere, the surfaces of the nanowires are oxidized, and then platinum nanoparticles are deposited chemically or by cyclic voltammetry on the tin oxide nanowires. 9. A method of making a supported catalyst as recited in claim 1 in which tin oxide nanowires are formed in an oxygen-containing argon atmosphere, the surfaces of the nanowires are oxidized with nitric acid, and then platinum nanoparticles are deposited chemically or by cyclic voltammetry on the tin oxide nanowires.