초록 ▼

An internal gear manufacturing method capable of manufacturing time reduction and easy core removal, and a metallic glass internal gear manufactured thereby. A carbon core formed into a shape of an external gear is arranged in a thin, long tubular mold of a length equal thereto with a space extendin

An internal gear manufacturing method capable of manufacturing time reduction and easy core removal, and a metallic glass internal gear manufactured thereby. A carbon core formed into a shape of an external gear is arranged in a thin, long tubular mold of a length equal thereto with a space extending longitudinally therealong. A molten metal material is pressure-injected under a temperature higher than a melting point thereof into the space between the mold and the core. The molten metal material is resolidified by rapid cooling at or above a critical cooling rate thereof together with the mold and the core. After resolidification of the molten metal material, the core is removed by pulverization or dissolution. Along internal gear formed of the resolidified metal material is cut into a plurality of segments of a prescribed length.

대표청구항 ▼

1. An internal gear manufacturing method comprising: providing a thin, long tubular mold;providing a non-metallic solid core having a gear portion in a shape of an external gear, said non-metallic solid core has a length equal to that of said tubular mold;positioning said non-metallic solid core ins

1. An internal gear manufacturing method comprising: providing a thin, long tubular mold;providing a non-metallic solid core having a gear portion in a shape of an external gear, said non-metallic solid core has a length equal to that of said tubular mold;positioning said non-metallic solid core inside and longitudinally along said tubular mold so as to provide a uniform space between the tubular mold and the non-metallic solid core;pouring a molten metal material under a temperature higher than a melting point thereof into the space between said tubular mold and said non-metallic solid core;letting said metal material resolidify in said mold containing said core; and removing said solid core by pulverization or dissolution after resolidification of said molten metal material, wherein said resolidified metal material with the solid core removed forms an internal gear structure. 2. The internal gear manufacturing method in accordance with claim 1, further including a cutting step for cutting a molded article formed of said resolidified metal material into a plurality of segments of a prescribed length, said cutting step following said core removal step. 3. The internal gear manufacturing method in accordance with claim 1, wherein said core further comprises, a bearing portion disposed on a first end of said gear portion and with an outer diameter smaller than that of said gear portion, and a motor engaging portion disposed on a second end of said gear portion and with an outer diameter greater than that of said bearing portion. 4. The internal gear manufacturing method in accordance with claim 1, wherein said core is made of carbon, boron nitride, or ceramics and has a melting point of 1,000° C. or higher. 5. The internal gear manufacturing method in accordance with claim 1, wherein said core removal is performed by pulverization of said core by blasting. 6. The internal gear manufacturing method in accordance claim 1, wherein said core removal is performed by dissolution of said core by a solvent. 7. The internal gear manufacturing method in accordance with claim 1, wherein said metal pouring is performed by pouring said molten metal material into said space by vacuum-pressure casting. 8. A metallic glass internal gear manufactured by the internal gear manufacturing method in accordance with claim 1.