초록 ▼

A process for preparing a composite membrane comprising a porous support layer and a discriminating layer, comprising the steps of: (a) providing a porous support layer;(b) incorporating an inert liquid into the pores of the support layer;(c) applying a curable composition to the support layer; and(

A process for preparing a composite membrane comprising a porous support layer and a discriminating layer, comprising the steps of: (a) providing a porous support layer;(b) incorporating an inert liquid into the pores of the support layer;(c) applying a curable composition to the support layer; and(d) curing the composition, thereby forming the discriminating layer on the porous support. The process is particularly useful for preparing gas separation composite membranes.

대표청구항 ▼

1. A process for preparing a composite membrane comprising a porous support layer and a discriminating layer, comprising the steps of: (a) providing a porous support layer;(b) incorporating an inert liquid into the pores of the support layer;(c) applying a curable composition to the support layer; a

1. A process for preparing a composite membrane comprising a porous support layer and a discriminating layer, comprising the steps of: (a) providing a porous support layer;(b) incorporating an inert liquid into the pores of the support layer;(c) applying a curable composition to the support layer; and(d) curing the composition b irradiating the composition for less than 30 seconds, thereby forming the discriminating layer on the porous support; wherein the curable composition is a radiation curable composition and wherein the curable composition is applied continuously to the porous layer by means of a manufacturing unit comprising a curable composition application station, an irradiation source, a composite membrane collecting station, and a means for moving a porous support layer from the curable composition application station to the irradiation source and to the composite membrane collecting station. 2. A process according to claim 1 wherein oxyethylene groups constitute at least 50 wt % of the total weight of non-volatile components in the curable composition. 3. A process according to claim 1 wherein oxyethylene groups constitute at least 70 wt % and at most 96 wt % of the total weight of non-volatile components in the curable composition. 4. A process according to claim 1 wherein step (b) and (c) are performed simultaneously by curtain coating, extrusion coating, slot die coating or slide bead coating. 5. A process according to claim 1 wherein the curable composition and/or the inert liquid are applied to the support layer at a coating speed of at least 15 m/min. 6. A process according to claim 1 wherein curing of the composition begins within 7 seconds of the curable composition being applied to the porous support layer. 7. A process according to claim 1 wherein the viscosity of the curable composition when measured at 35° C. is from 1 to 1000 mPa·s. 8. A process according to claim 1 wherein at least 80 vol % of the pores of the support layer are filled with the inert liquid such that the discriminating layer is smooth. 9. A process according to claim 1 wherein the composition comprises: (i) 0 to 20 parts in total of monofunctional compounds;(ii) 1 to 20 parts in total of difunctional compounds;(iii) 0 to 5 parts in total of polyfunctional compounds;(iv) 75 to 99 parts of an inert liquid; and(v) 0.01 to 5 parts of photoinitiator; wherein all parts are by weight. 10. A process according to claim 1 wherein the porous support has a CO2 permeance of 5 to 150×10−5 m3(STP)/m2·s·kPa. 11. A process according to claim 1 wherein oxyethylene groups constitute at least 70 wt % and at most 96 wt % of the total weight of non-volatile components in the curable composition, step (b) and (c) are performed simultaneously by curtain coating, extrusion coating, slot die coating or slide bead coating, the curable composition and/or the inert liquid are applied to the support layer at a coating speed of at least 15 m/min, curing of the composition begins within 7 seconds of the curable composition being applied to the porous support and the viscosity of the curable composition when measured at 35° C. is from 1 to 1000 mPa·s. 12. A process according to claim 9 wherein oxyethylene groups constitute at least 70 wt % and at most 96 wt % of the total weight of non-volatile components in the curable composition, step (b) and (c) are performed simultaneously by curtain coating, extrusion coating, slot die coating or slide bead coating, the curable composition and/or the inert liquid are applied to the support layer at a coating speed of at least 15 m/min, curing of the composition begins within 7 seconds of the curable composition being applied to the porous support and the viscosity of the curable composition when measured at 35° C. is from 1 to 1000 mPa·s. 13. A process according to claim 8 wherein oxyethylene groups constitute at least 70 wt % and at most 96 wt % of the total weight of non-volatile components in the curable composition, step (b) and (c) are performed simultaneously by curtain coating, extrusion coating, slot die coating or slide bead coating, the curable composition and/or the inert liquid are applied to the support layer at a coating speed of at least 15 m/min, curing of the composition begins within 7 seconds of the curable composition being applied to the porous support and the viscosity of the curable composition when measured at 35° C. is from 1 to 1000 mPa·s. 14. A process according to claim 1 wherein the inert liquid and the curable composition are coated onto the support layer by a multilayer coating method wherein a layer of the inert liquid and a layer of the curable composition are applied simultaneously to the support layer with the inert liquid layer being the lower layer and therefore contacting the support ahead of the curable composition. 15. A composite membrane obtained by a process comprising the steps of: (a) providing a porous support layer;(b) incorporating an inert liquid into the pores of the support layer;(c) applying a curable composition to the support layer; and(d) curing the composition, thereby forming the discriminating layer on the porous support; wherein the curable composition is a radiation curable composition comprising: (i) 0 to 20 parts in total of monofunctional compounds;(ii) 1 to 20 parts in total of difunctional compounds;(iii) 0 to 5 parts in total of polyfunctional compounds;(iv) 75 to 99 parts of an inert liquid; and(v) 0.01 to 5 parts of photoinitiator; wherein all parts are by weight. 16. A gas separation cartridge comprising a membrane according to claim 15.