초록 ▼

A three-dimensional hydraulically entangled nonwoven composite structure made of nonwoven fibrous web and a fibrous material integrated in the nonwoven fibrous web by hydraulic entanglement is disclosed. The nonwoven composite structure has a greater ability to maintain an embossed pattern when wet

A three-dimensional hydraulically entangled nonwoven composite structure made of nonwoven fibrous web and a fibrous material integrated in the nonwoven fibrous web by hydraulic entanglement is disclosed. The nonwoven composite structure has a greater ability to maintain an embossed pattern when wet and has the ability for the structure to recover after it has been compressed, to a greater degree than previously found. Also disclosed is a method of making an embossed hydraulically entangled nonwoven composite fabric.

대표청구항 ▼

1. A method of making an embossed, hydraulically entangled nonwoven composite fabric having a nonwoven component and a fibrous component consisting of fibers, said method comprising: superposing a fibrous material layer over a nonwoven fibrous web layer;hydraulically entangling said layers to form a

1. A method of making an embossed, hydraulically entangled nonwoven composite fabric having a nonwoven component and a fibrous component consisting of fibers, said method comprising: superposing a fibrous material layer over a nonwoven fibrous web layer;hydraulically entangling said layers to form a composite material;drying the composite material;heating the composite material to form a heated composite material; andembossing the heated composite material in an embossing gap formed by a pair of matched embossing rolls; andwherein heating the composite material occurs after the drying of the composite and the heating is by an additional heat source. 2. The method of claim 1 where prior to embossing the composite material in the embossing gap, the surface of the composite material is heated to a temperature greater than about 140° F. 3. The method of claim 1 where prior to embossing the composite material in the embossing gap, the surface of the composite material is heated to a temperature greater than about 200° F. 4. The method of claim 1 where prior to embossing the composite material in the embossing gap, the surface of the composite material is heated to a temperature greater than about 300° F. 5. The method of claim 1 where the matched embossing rolls are heated. 6. The method of claim 1 wherein the layers are superposed by depositing a fibrous material layer, comprising a suspension of fibers, onto a nonwoven fibrous web layer of continuous filaments, by drying forming or wet-forming. 7. The method of claim 1 wherein the fibrous material layer is superposed over a nonwoven fibrous web layer of continuous spun bonded filaments. 8. The method of claim 1 further comprising the step of adding a material selected from clays, activated charcoals, starches, particulates, and superabsorbent particulates to the superposed layers prior to hydraulic entangling. 9. The method of claim 1 further comprising the step of adding a material selected from clays, activated charcoals, starches, particulates, and superabsorbent particulates to the superposed, hydraulically entangled composite material. 10. The method of claim 6 further comprising the step of adding a material selected from clays, activated charcoals, starches, particulates, and superabsorbent particulates to the suspension of fibers used to form the fibrous material layer on the nonwoven fibrous web layer of continuous filaments. 11. The method of claim 1 wherein the hydraulically entangled nonwoven composite fabric is subjected to a finishing step selected from mechanical softening, pressing, creping, and brushing. 12. The method of claim 1 wherein the hydraulically entangled nonwoven composite fabric is subjected to a chemical post-treatment selected from dyes and adhesives. 13. An embossed, hydraulically entangled nonwoven composite fabric made by the method of claim 1 having a wet compression rebound ratio greater than about 0.13. 14. The embossed, hydraulically entangled nonwoven composite fabric of claim 13 having a wet compression rebound ratio is greater than about 0.15. 15. The embossed, hydraulically entangled nonwoven composite fabric of claim 13 where the wet compression rebound ratio is between about 0.13 and about 3.00. 16. The embossed, hydraulically entangled nonwoven composite fabric of claim 13 where the wet compression rebound ratio is between about 0.13 and about 0.60. 17. The embossed, hydraulically entangled nonwoven composite fabric of claim 13 where the wet compression rebound ratio is between about 0.13 and about 0.45. 18. The embossed, hydraulically entangled nonwoven composite fabric of claim 13 where the wet compression rebound ratio is between about 0.15 and about 0.45. 19. The method of claim 1, wherein the matched embossing rolls comprise a male embossing roller having a plurality of pins extending from the roller periphery and a matching female embossing roller having a plurality of pockets which extend into the roller from the roller periphery, wherein the pins of the male roller extend into the pockets of the female roller in the embossing gap.