초록

A composite material comprising the following components: (a) a first prepreg material with improved resistance to microbuckling and kinkband formation; and(b) a second prepreg material with improved resistance to delamination.

대표청구항 ▼

1. A composite material comprising: (a) a first prepreg material with improved resistance to microbuckling and kinkband formation comprising a first epoxy resin, reinforcing fibers oriented in a °0 reference direction, and insoluble or partially soluble polymer particles; and(b) a second prepreg mat

1. A composite material comprising: (a) a first prepreg material with improved resistance to microbuckling and kinkband formation comprising a first epoxy resin, reinforcing fibers oriented in a °0 reference direction, and insoluble or partially soluble polymer particles; and(b) a second prepreg material with improved resistance to delamination arranged adjacent to the first prepreg material, said second prepreg material comprising a plurality of prepreg plies and at least one of:(i) insoluble or partially soluble interlaminar polymer particles between prepreg plies of the second prepreg material; and(ii) one or more strengthening interleafs between prepreg plies of the second prepreg material,wherein each prepreg ply of the second prepreg material comprises a second epoxy resin and reinforcing fibers oriented in a second direction that forms an angle relative to the 0° reference direction, andwherein the first epoxy resin has an elastic modulus that is higher than the elastic modulus of the second epoxy resin. 2. A composite material according to claim 1, where the insoluble or partially insoluble polymer particles in the first prepreg material and the second prepreg material are made of one or more polymers selected from the group consisting of: polyvinyl acetate, polyamides, polycarbonates, polyacetal, polyphenylene oxide, polyphenylene sulfide, polyallylates, polyesters, polyamidimides, polyimides, polyether imides, polysulfones, polyether sulfones, polyether ether ketones, polyether ketone ketones, polyaramid, polybenzoimidazole, polyethylene, polypropylene, polyamides, cellulose acetate and cellulose butyrate, and co-polymers thereof, and rubber. 3. A composite material according to claim 1, where the strengthening interleafs comprise at least two interleafs respectively having different compositions from each other. 4. A composite material according to claim 1, wherein the at least one strengthening interleaf is selected from the group consisting of: a) a thermosetting resin film for creating a resin rich area in the region between two different prepreg plies;b) a nonwoven textile, veil or fleece made of organic or inorganic fibers and combinations thereof;c) a film or membrane comprising organic or inorganic materials and combinations thereof; andd) a heterogeneous fibers comprising organic or inorganic material and combinations thereof with different fibers other than the ones used as reinforcing fibers. 5. A composite material according to claim 1, wherein the first prepreg material comprises reinforcing fibers different from the reinforcing fibers of the second prepreg material. 6. A composite material according to claim 1, where the first prepreg material and the second prepreg material comprise reinforcing fibers selected from carbon fibres, aramid fibers, glass fibres, alumina, zirconia, silicon carbide, other compound ceramics or metals. 7. A composite material according to claim 1, where the first prepreg material and the second prepreg material comprise carbon or graphite fibers as reinforcing fibers. 8. A composite material according to claim 1, wherein the first epoxy resin has an elastic modulus higher than 3.4 GPA. 9. A composite material according to claim 8, wherein the second epoxy resin has a fracture toughness Gc higher than 0.200 kJ/m2. 10. A process of making a cured composite comprising co-curing (a) a first prepreg material with improved resistance to microbuckling and kinkband formation, said first prepreg material comprising a first epoxy resin, reinforcing fibers oriented in a 0° reference direction, and insoluble or partially soluble polymer particles; and(b) a second prepreg material with improved resistance to delamination arranged adjacent to the first prepreg material, said second prepreg material comprising a plurality of prepreg plies and at least one of(i) insoluble or partially soluble interlaminar polymer particles between prepreg plies of the second prepreg material; and(ii) one or more strengthening interleafs between prepreg plies of the second prepreg material,wherein each prepreg ply of the second prepreg material comprises a second epoxy resin and reinforcing fibers oriented in a direction that forms an angle relative to the 0° reference direction, andwherein the first epoxy resin has an elastic modulus that is higher than the elastic modulus of the second epoxy resin.