초록 ▼

Provided is a catalyst support structure for use as either a NOx catalyst support or as a DPF having a hydrophobic coating. The hydrophobic coating affords a catalyst support structure exhibiting reduced or low absorption when exposed to both liquid catalytic coating or other aqueous media and thus

Provided is a catalyst support structure for use as either a NOx catalyst support or as a DPF having a hydrophobic coating. The hydrophobic coating affords a catalyst support structure exhibiting reduced or low absorption when exposed to both liquid catalytic coating or other aqueous media and thus protecting the catalyst support structure from cracking and spalling during drying. Methods are also provided for making a catalyst support structure with a hydrophobic coating.

대표청구항 ▼

1. A catalyst support structure comprising a multicellular ceramic-body which includes: (i) an external skin portion,(ii) a hydrophobic coating, the hydrophobic coating resulting in a coated ceramic body exhibiting a low absorption of liquid catalytic coating mixtures and aqueous media utilized in a

1. A catalyst support structure comprising a multicellular ceramic-body which includes: (i) an external skin portion,(ii) a hydrophobic coating, the hydrophobic coating resulting in a coated ceramic body exhibiting a low absorption of liquid catalytic coating mixtures and aqueous media utilized in application of the liquid catalytic coating mixtures, wherein the hydrophobic coating is formed directly on the external skin portion of the ceramic body, and(ii) a catalytic coating on the hydrophobic coating. 2. The catalyst support structure according to claim 1 wherein the coated ceramic body exhibits low adsorption such that a 2 μL deionized water drop exhibits a contact angle of greater than 50° when in contact with a surface of the coated ceramic body. 3. The catalyst support structure according to claim 1 wherein the hydrophobic coating is comprised of a passivating material containing cordierite cement. 4. The catalyst support structure according to claim 1 wherein the multicellular ceramic body is a monolithic ceramic honeycomb, having an inlet end, an outlet end, and a multiplicity of mutually adjoining cells extending along the length of the ceramic honeycomb from the inlet end to the outlet end, the cells being separated from one another by porous walls. 5. The catalyst support structure according to claim 4 wherein a portion of the cells on the inlet end and a portion of the cells on the outlet end are plugged, the plugged portion of the cells at the inlet end being different from the plugged portion of the cells at the outlet end, such that exhaust gases enter the ceramic honeycomb through open cells at the inlet end, flow through porous walls, and exit the ceramic honeycomb through open cells at the outlet end. 6. A catalyst support structure according to claim 4 wherein the monolithic ceramic honeycomb is comprised of material selected from the group consisting of cordierite, aluminum titanate, and mixtures thereof. 7. A catalyst support structure according to claim 6 wherein the cordierite or aluminum titanate ceramic honeycomb is further characterized by: a cell density of 10 to 1200 cells per square inch; a cell wall thickness of 0.1 to 50 mil; a cell wall porosity of 10% to 75% by volume; and, a cell wall median pore size of 1 to 50 micrometers. 8. A catalyst support structure according to claim 7 wherein the ceramic honeycomb is characterized by: a cell density of 100 to 600 cells per square inch; a cell wall thickness of 2 to 35 mil; a cell wall porosity of 25% to 65% by volume; and, a cell wall median pore size of 10 to 35 micrometers. 9. A method of producing a coated catalyst support structure having an external hydrophobic coating, the method comprising: a. providing a fired multicellular ceramic body;b. applying an external skin coating to the fired multicellular ceramic body;c. applying a hydrophobic passivating coating to the external skin coating and/or to the entire coated multicellular ceramic body;d. applying a catalyst coating to the coated multicellular ceramic body;e. drying the catalyst-coated multicellular ceramic body; andf. calcining the dried catalyst coated multicellular ceramic body. 10. The method of claim 9 wherein the multicellular ceramic body and the external skin coating are comprised of a cordierite material. 11. The method of claim 9 further comprising heat-treating the dried coated multicellular ceramic body of step e at a temperature of at least 60° C. for at least a time sufficient to crosslink the passivating coating material. 12. The method of claim 11 wherein the heat-treating step is carried out at a temperature of between about 60-500° C. for 3 hours. 13. The method of claim 9 wherein the hydrophobic passivating material is applied by dipping, showering, spraying, rolling, blotting or injecting. 14. The method of claim 9 wherein the hydrophobic passivating material is selected from the group consisting of silicone resin, urethane, oil, silane, wax, carbon, carbon soot and mixtures thereof.