초록

A fishing rod having improved strength and durability to weight characteristics is provided using a thermoplastic toughened epoxy resin. The method of manufacturing this fishing rod includes the use of an insulating layer around rod blanks during a high temperature cure stage.

대표청구항 ▼

1. A method of making a fishing rod comprising a rod segment constructed from a rod segment blank having an axis and an outer conical surface tapering from a butt end to a tip end, the method comprising: providing a first flag prepreg of selected dimensions comprising synthetic carbon fibers orienta

1. A method of making a fishing rod comprising a rod segment constructed from a rod segment blank having an axis and an outer conical surface tapering from a butt end to a tip end, the method comprising: providing a first flag prepreg of selected dimensions comprising synthetic carbon fibers orientated parallel to one another in a thermoplastic toughened resin matrix;providing a second flag prepreg of selected dimensions comprising synthetic carbon fibers orientated parallel to one another in a thermoplastic toughened resin matrix;creating a kit including wraps of said first flag synthetic fibers generally parallel to said rod segment blank outer conical surface wherein said wraps extend from said butt end to said tip end;said kit further including said second flag prepreg layed upon said first flag prepreg such that said synthetic fibers of said second flag are not parallel to said synthetic fibers of said first flag;wherein said synthetic fibers of said second flag prepreg extend from said butt end to said tip end;wrapping a heat shrink film tape about said kit; curing said flags by application of heat;removing said heat shrink film tape from said cured flags thereby forming said rod segment blank; and,initially wrapping an insulating film about said flags and said heat shrink film tape prior to curing, and then subsequently removing said insulating film after curing. 2. The method of claim 1, wherein said curing is at least partially performed at a temperature of at least 275° F. 3. The method of claim 2, wherein said curing is at least partially performed at a temperature at least 300° F. 4. The method of claim 3, wherein said curing is at least partially performed at a temperature of about 350° F. 5. The method of claim 1, wherein said insulating film is a polytetrafluorethylene film. 6. The method of claim 5, wherein said insulating film is 1 mil thick. 7. The method of claim 1, wherein said first flag has a fiber areal weight of less than 120 grams per square meter. 8. The method of claim 7, wherein said second flag has a fiber areal weight of less than 50 grams per square meter. 9. The method of claim 7, wherein said second flag has a fiber areal weight greater than 20 grams per square meter and less than 35 grams per square meter. 10. The method of claim 7, wherein said second flag has a fiber areal weight of about 28 to 30 grams per square meter. 11. The method of claim 1, wherein said dimensions of said second flag prepreg is less than said dimensions of said first flag prepreg. 12. A method of making a fishing rod blank segment comprising: providing a tapered mandrel having an axis and an outer conical surface;providing a main flag prepreg of selected dimensions comprising synthetic fibers orientated parallel to one another in a thermoplastic toughened resin matrix;providing a second flag prepreg of selected dimensions comprising synthetic fibers orientated parallel to one another in a thermoplastic toughened resin matrix;said selected dimension of said second flag prepreg is less than said selected dimension of said main flag prepreg;creating a kit by laying said second flag prepreg upon said first flag prepreg such that said synthetic fibers of said second flag are not parallel to said synthetic fibers of said first flag;wrapping said kit about said mandrel such that said first flag synthetic fibers are generally coplanar with said mandrel axis and generally parallel to said mandrel conical surface;wrapping a heat shrink film tape about said mandrel and said kit;curing said flags by application of heat;removing said heat shrink film and said mandrel from said cured flags forming said fishing rod blank; and,wrapping said mandrel, said flags and said heat shrink film with an insulating film prior to curing and removing said insulating film after curing. 13. The method of claim 12 wherein said curing is at least partially performed at a temperature of at least 275° F. 14. The method of claim 13 wherein said curing is at least partially performed at a temperature at least 300° F. 15. The method of claim 14 wherein said curing is at least partially performed at a temperature of about 350° F. 16. The method of claim 12 wherein said insulating film is a polytetrafluorethylene film. 17. The method of claim 16 wherein said insulating film is 1 mil thick. 18. The method of claim 12 wherein said main flag has a fiber areal weight of less than 120 grams per square meter. 19. The method of claim 18 wherein said second flag has a fiber areal weight of less than 50 grams per square meter. 20. The method of claim 18 wherein said second flag has a fiber areal weight greater than 20 grams per square meter and less than 35 grams per square meter. 21. The method of claim 18 wherein said second flag has a fiber areal weight of about 28 to 30 grams per square meter. 22. The method of claim 12 wherein said thermoplastic toughened resin matrix is an epoxy based resin.