초록 ▼

The present invention relates to an extruded thermoplastic resin foam, particularly relates to a board extruded thermoplastic resin which has low heat conductivity, an excellent heat insulating property over a long period of time, high flame retardancy, and excellent mechanical strength. The extrude

The present invention relates to an extruded thermoplastic resin foam, particularly relates to a board extruded thermoplastic resin which has low heat conductivity, an excellent heat insulating property over a long period of time, high flame retardancy, and excellent mechanical strength. The extruded thermoplastic resin foam having an apparent density of 20 to 50 kg/m3, a closed cells ratio of 85% or more and a thickness of 10 to 150 mm, and containing a non-halogen organic physical blowing agent, wherein the thermoplastic resin composing the extruded foam contains a mixture of 100 parts by weight of a polystyrene resin (A) and 5 to 150 parts by weight of a polyester resin (B), and an endothermic calorific value of the polyester resin (B) less than 5 J/g (including 0) for fusion of the polyester resin on a DSC curve obtained by heat flux differential scanning calorimetry based on JIS K7122 (1987).

대표청구항 ▼

1. An extruded thermoplastic resin foam having: an apparent density of 20 to 50 kg/m3;a closed cells ratio of 85% or more; anda thickness of 10 to 150 mm; andcontaining a non-halogen organic physical blowing agent, wherein:a thermoplastic resin composing the extruded foam contains a mixture of 100 p

1. An extruded thermoplastic resin foam having: an apparent density of 20 to 50 kg/m3;a closed cells ratio of 85% or more; anda thickness of 10 to 150 mm; andcontaining a non-halogen organic physical blowing agent, wherein:a thermoplastic resin composing the extruded foam contains a mixture of 100 parts by weight of a polystyrene resin (A) and 5 to 150 parts by weight of a polyester resin (B), which is a non-crystalline polyester copolymer containing a dicarboxylic acid component and a diol component, wherein a spiroglycol comprises 10 to 80 mol% of the entire diol component that is used to prepare said polyester resin (B) andan endothermic calorific value of the polyester resin (B) is from 0 to less than 5 J/g for fusion of the polyester resin on a DSC curve obtained by heat flux differential scanning calorimetry based on JIS K7122 (1987). 2. The extruded thermoplastic resin foam according to claim 1, wherein the thermoplastic resin is composed of a mixture of 100 parts by weight of the polystyrene resin (A) and 10 to 130 parts by weight of the polyester resin (B). 3. The extruded thermoplastic resin foam according to claim 1, wherein the dicarboxylic: component contains an aromatic dicarboxylic acid or an alkyl ester thereof. 4. The extruded thermoplastic resin foam according to claim 3, wherein the dicarboxylic acid component is dimethyl terephthalate. 5. The extruded thermoplastic resin foam according to claim 1, wherein a melt viscosity (h) of the polyester resin (B) is within a range of 1000 to 6000 Pa·s at a temperature of 200° C. and a shear rate of 100 sec−1. 6. The extruded thermoplastic resin foam according to claim 1, wherein a sea-island structure is formed in a cross section of a cell membrane of the extruded thermoplastic resin foam so that the polystyrene resin (A) forms a continuous phase and the polyester resin (B) forms a dispersion phase. 7. The extruded thermoplastic resin foam according to claim 1, wherein an amount of the non-halogen organic physical blowing agent remaining in the extruded thermoplastic resin foam is 0.1 to 0.9 mol with reference to 1 kg of the extruded thermoplastic resin foam at 100 days after manufacture. 8. The extruded thermoplastic resin foam according to claim 1, wherein a thermal conductivity of the extruded thermoplastic resin foam is 0.029 W/(m·K) or less.