초록 ▼

The invention concerns a method for melting a composition of raw materials including introducing the composition in an oven to form a layer (2) at the surface of the molten pool (4). An oxycombustion burner (10) is arranged above the pool and directed towards the composition layer (2) to produce a m

The invention concerns a method for melting a composition of raw materials including introducing the composition in an oven to form a layer (2) at the surface of the molten pool (4). An oxycombustion burner (10) is arranged above the pool and directed towards the composition layer (2) to produce a melting front (3). Parameters of the burner are adjusted to produce a large covering flame (12) causing an essentially radiation-based thermal transfer. Additionally, a plane containing a longitudinal section of the flame (Z-Z) and a horizontal direction perpendicular to the axis of the oven (X-X) intersects the melting front (3) at a height (h) included ranging between one third and half of the thickness of the composition (e). Such a method provides for a stable operation of the oven and is particularly adapted to a large-capacity oven.

대표청구항 ▼

1. A method of melting a batch of raw vitrifiable materials, comprising the following steps: a batch of raw vitrifiable materials is introduced into a furnace in a charging direction (D) parallel to a longitudinal central axis (X-X) of the furnace, distributing the batch substantially continuously a

1. A method of melting a batch of raw vitrifiable materials, comprising the following steps: a batch of raw vitrifiable materials is introduced into a furnace in a charging direction (D) parallel to a longitudinal central axis (X-X) of the furnace, distributing the batch substantially continuously and uniformly over a defined charging width (L), so as to form a layer of the batch on the surface of the melt; andan oxyfuel burner is placed above the melt in a vertical plane (P) including the axis (X-X) of the furnace, the burner being directed toward the batch layer so as to create a melting front of the batch present in the layer, the melting front being symmetrical with respect to the plane P,adjusting the parameters of the burner, carried out so that: the burner produces a flat flame having a horizontally elongate cross section;a plane containing a longitudinal section of the flame and a horizontal direction perpendicular to the axis (X-X) of the furnace intersects the batch melting front at a height (h) between one third and one half of the thickness (e) of the batch layer measured from the surface of the melt, and intersects the surface of the melt along a line perpendicular to the axis (X-X) of the furnace; andthe flame produces a transfer of heat to the melting front of the batch essentially radiatively. 2. The method of claim 1, in which the parameters of the burner are adjusted so that a longitudinal end of the flame does not touch the melting front of the batch. 3. The method of claim 1, in which the burner resides in a vertical plane that includes the longitudinal central axis (X-X) of the furnace. 4. The method of claim 1, in which the burner is inclined to a vertical direction. 5. The method of claim 4, in which the burner is downwardly inclined at an angle (α) between 45° and 65° to the vertical direction. 6. The method of claim 1, in which the burner is positioned through holes drilled in a crown structure above the melt. 7. The method of claim 1, in which certain parameters of the burner are adjusted so that the fluids injected into the furnace by the burner have a total momentum of between 0.58 N and 5 N. 8. The method of claim 1, in which certain parameters of the burner are adjusted according to the position of advance of the melting front along the axis (X-X) of the furnace. 9. The method of claim 8, in which the parameters of the burner adjusted according to the position of advance of the melting front are chosen from the fuel flow rate, the oxygen-containing gas flow rate, the fuel injection pressure, the oxygen-containing gas injection pressure and the angle (α) of inclination of the burner to the vertical direction. 10. A method of melting a batch of raw vitrifiable materials, comprising the following steps: the batch of raw vitrifiable materials is introduced into a furnace in a charging direction (D) parallel to a longitudinal central axis (X-X) of the furnace, distributing the batch substantially continuously and uniformly over a defined charging width (L), so as to form a layer of the batch on the surface of the melt;an oxyfuel burner is placed above the melt, the burner being directed toward the batch layer so as to create a melting front of the batch present in the layer;installing a system for detecting the position of advance of the melting front along the axis (X-X) of the furnace, and in which certain parameters of the burner are slaved to the detected position of advance of the melting front so that: the burner produces a flat flame having a horizontally elongate cross section;the plane containing a longitudinal section of the flame and a horizontal direction perpendicular to the axis (X-X) of the furnace intersects the batch melting front at a height (h) between one third and one half of the thickness (e) of the batch layer measured from the surface of the melt, and intersects the surface of the melt along a line perpendicular to the axis (X-X) of the furnace; andthe flame produces a transfer of heat to the melting front of the batch essentially radiatively. 11. The method of claim 10, in which the system for detecting the position of advance of the melting front comprises a laser.