An electrically conductive coating composition is provided for use on aircraft and other substrate surfaces to prevent the formation of ice or to melt ice. The conductive coating composition may include a nanomaterial such as carbon nanotubes dispersed in a solvent which may be applied to a substrat
An electrically conductive coating composition is provided for use on aircraft and other substrate surfaces to prevent the formation of ice or to melt ice. The conductive coating composition may include a nanomaterial such as carbon nanotubes dispersed in a solvent which may be applied to a substrate surface to form a thin film which is resistively heatable. The conductive coating may also comprise a nanomaterial formed from carbon nanotubes or fullerenes grafted to a polymer containing an active functional group which renders a substrate surface icephobic and is also resistively heatable.
대표청구항▼
1. An electrically conductive coating composition dispersed in a liquid carrier for use on substrates comprising a nanomaterial selected from carbon nanotubes, metal nanorods, functionalized metal nanoparticles, and a nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer conta
1. An electrically conductive coating composition dispersed in a liquid carrier for use on substrates comprising a nanomaterial selected from carbon nanotubes, metal nanorods, functionalized metal nanoparticles, and a nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer containing an active functional group; said conductive coating composition forming a film when applied to a substrate, which film is resistively heatable to prevent the formation of ice on, or to melt ice from, the surface of said substrate. 2. The electrically conductive coating composition of claim 1 wherein said nanomaterial comprises said nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer containing an active functional group, said polymer selected to render the surface of said substrate icephobic. 3. The electrically conductive coating composition of claim 2 wherein said coating exhibits an ice adhesion reduction factor greater than 1. 4. The electrically conductive coating composition of claim 1 wherein said active functional group is selected from methylene, amine, amide, and carboxyl. 5. The electrically conductive coating composition of claim 1 wherein said nanomaterial comprises carbon nanotubes selected from single-walled carbon nanotubes, multi-walled carbon nanotubes, and mixtures of single-walled and multi-walled nanotubes. 6. The electrically conductive coating composition of claim 1 wherein said polymer is selected from a fluoropolymer or a silicone. 7. The coating composition of claim 1 wherein said polymer comprises polydimethyl siloxane. 8. The electrically conductive coating composition of claim 2 wherein a film of said composition has a sheet resistance of between about 10 and 1000 ohms/square. 9. The electrically conductive coating composition of claim 2 wherein said nanomaterial comprises a nanostructure which comprises from about 20 to about 99% by weight of said polymer and from about 0.02 to about 50 wt % of said carbon nanotubes or fullerenes. 10. The electrically conductive coating composition of claim 1 wherein said liquid carrier comprises a solvent selected from alcohols, ethers, ketones, esters, water, halogenated solvents, solvents, aromatic solvents, and mixtures thereof. 11. The conductive coating composition of claim 10 comprising from about 0.001 to about 5% by weight of said nanomaterial and from about 85 to about 99 wt % of said solvent. 12. The conductive coating composition of claim 1 wherein said functionalized metal nanoparticles comprise metal nanoparticles which have been bound together by self-assembly or which have been grafted with polymerizable or condensable monomer groups. 13. A substrate having a resistively heatable film thereon, said film comprising an electrically conductive coating composition comprising a nanomaterial selected from carbon nanotubes, metal nanorods, and functionalized metal nanoparticles, and a nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer containing an active functional group, said film having a sheet resistance of from about 0.01 to about 1000 ohm/sq. 14. The substrate of claim 13 wherein said film has a thickness of from about 0.05 μm to about 1,000 μm. 15. The substrate of claim 13 further including a primer coating on said substrate; wherein said film overlies said primer coating. 16. The substrate of claim 13 further including a thermally conductive top coating over said film selected from polyurethane, epoxy, polycarbonate and siloxane. 17. The substrate of claim 16 wherein said thermally conductive top coating is formed from a nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer containing at least one active functional group. 18. The substrate of claim 13 further including a thermal barrier coating thereon. 19. The substrate of claim 13 wherein said film includes at least two conductive leads embedded therein. 20. The substrate of claim 13 comprising metal, glass, polymers, elastomers, ceramic, aluminum composites, and carbon fiber composites. 21. The substrate of claim 13 wherein said electrically conductive coating composition includes a hydrophobic polymer therein. 22. A substrate having a multilayer coating thereon which is resistively heatable to prevent the formation of ice or to melt ice on the surface of said substrate comprising: a base substrate having first and second major surfaces;a primer coating layer on said first major surface of said substrate;an electrically conductive film layer on said primer coating, said conductive film layer formed from a nanomaterial selected from carbon nanotubes, metal nanorods, and functionalized metal nanoparticles; anda thermally conductive topcoat on said conductive film layer. 23. The substrate of claim 22 including a thermal barrier layer between said primer layer and said conductive film layer. 24. The substrate of claim 22 wherein said thermally conductive topcoat comprises a coating composition comprising a nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer containing an active functional group, said polymer having hydrophobic properties. 25. The substrate of claim 13 wherein said nanomaterial comprises a nanostructure comprising carbon nanotubes or fullerenes grafted to a polymer containing an active functional group; and wherein water droplets applied to the surface of said coating composition exhibit a contact angle on said substrate of at least 80 degrees. 26. The substrate of claim 25 wherein water droplets applied to the surface of said coating composition exhibit a contact angle of at least 100 degrees. 27. The substrate of claim 25 wherein said polymer is a hydrophobic polymer containing at least one active methylene group. 28. The substrate of claim 27 wherein said polymer comprises polydimethyl siloxane. 29. A method of preventing the formation of ice on, or melting ice from, the surface of a substrate comprising: applying an electrically conductive coating composition to a substrate surface to form a film thereon, said coating composition comprising a nanomaterial selected from carbon nanotubes, metal nanorods, functionalized metal nanoparticles; and optionally, a polymer; andresistively heating said conductive coating composition. 30. The method of claim 29 wherein resistively heating said coating comprises applying voltage to said film between about 5 and about 240 V. 31. The method of claim 29 including heating said film to a temperature of between about 20° C. and about 400° C. 32. The method of claim 29 including heating said film to a temperature of between about 40° C. and about 180° C.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (21)
Rutherford Robert B. ; Dudman Richard L., Aircraft de-icing system.
Hastings Otis H. (130 E. Crescent Ave. Mahwah NJ 07430) Hastings Otis M. (130 E. Crescent Ave. Mahwah NJ 07430), Electrically conductive laminate for temperature control of aircraft surface.
Todt, Michael Leslie; Rodrigues, David Ernest; Ting, Sai-Pei, Electrically conductive polymer composite compositions, method for making, and method for electrical conductivity enhancement.
Bonnet, Anthony; Triballier, Karine; Bussi, Philippe; Burchill, Michael; Foure, Michael, Microcomposite power based on an electrical conductor and a fluoropolymer, and objects manufactured with this powder.
Ellsworth, Joseph R.; Martinez, Michael P.; McCordic, Craig H.; Paquette, Jeffrey; Cheyne, Scott R., Modular architecture for scalable phased array radars.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.