초록 ▼

A method for whisker formation on the surface of aluminum-containing metallic alloy fibers and substrates provides a support structure for many technical, medical and pharmaceutical applications. The novel surface modification of metallic alloy fibers and other metallic substrates involves heating t

A method for whisker formation on the surface of aluminum-containing metallic alloy fibers and substrates provides a support structure for many technical, medical and pharmaceutical applications. The novel surface modification of metallic alloy fibers and other metallic substrates involves heating the fiber or substrate in air at temperatures ranging from approximately 800° C. to approximately 1000° C. for a period of time ranging from approximately 10 hours to approximately 100 hours to form whiskers. The use of a metal oxide coating with large ions, such as zirconium oxide, allows the formation of alumina whiskers while preserving the structural integrity of the metallic alloy substrate. Uses of the present invention include, but are not limited to an advanced catalyst support, a highly efficient filter medium, a support for implants and the like.

대표청구항 ▼

1. A method for forming whiskers on the surface of an aluminum-containing metallic alloy substrate comprising the steps of: selecting an aluminum-containing metallic alloy fiber is selected from the group consisting of MCrAIX, where M is at least one of iron (Fe), and cobalt (Co) in a range of appro

1. A method for forming whiskers on the surface of an aluminum-containing metallic alloy substrate comprising the steps of: selecting an aluminum-containing metallic alloy fiber is selected from the group consisting of MCrAIX, where M is at least one of iron (Fe), and cobalt (Co) in a range of approximately 60% to approximately 70%, Cr is chromium in a range of approximately 20% to approximately 30%, Al is aluminum in a range of approximately 5% to approximately 10% and X is at least one of yttrium (Y), zirconium (Zr), hafnium (Hf) and ytterbium (Yb) in a range of approximately 0.05% to approximately 0.15%;applying a hafnium oxide layer to coat the metallic alloy fiber;heating the hafnium oxide coated metallic alloy substrate at oxidation temperatures and for a period of time to form alumina whiskers on the surface of the hafnium oxide coated metallic substrate; anddepositing a catalyst layer on the whiskered surface using dip coating with at least one catalysts selected from platinum, rhodium and a multicomponent sol with one of alumina, zirconia, and ceria increasing the total surface area of the metallic alloy substrate during oxidation. 2. The method of claim 1, wherein the aluminum-containing metallic alloy substrate is FeCrAlX. 3. The method of claim 1, wherein the aluminum-containing metallic alloy substrate is FeCrAlY. 4. The method of claim 1, wherein the metallic alloy substrate is a fiber. 5. The method of claim 1, wherein the heating of the metallic alloy substrate occurs at temperatures from approximately 800° C. to approximately 1000° C. 6. The method of claim 1, wherein the time period for heating is between approximately 50 hours to approximately 100 hours. 7. The method of claim 1, wherein the aluminum-containing metallic alloy substrate is CoCrAlX. 8. A method for forming whiskers on the surface of an aluminum-containing metallic alloy substrate by oxidizing the surface, comprising the steps of: providing an aluminum-containing metallic alloy substrate is selected from the group consisting of MCrAlX, where M is one of cobalt (Co) and nickel (Ni) in a range of approximately 60% to approximately 70%, Cr is chromium in a range of approximately 20% to approximately 30%, Al is aluminum in a range of approximately 5% to approximately 10% and X is at least one of yttrium (Y), zirconium (Zr), hafnium (Hf) and ytterbium (Yb) in a range of approximately 0.05% to approximately 0.15%;applying a hafnium oxide layer to coat the metallic alloy substrate;oxidizing the hafnium oxide coated metallic alloy substrate at selected temperatures and for a period of time to form alumina whiskers on the surface of the hafnium oxide coated metallic substrate; anddepositing a catalyst layer of oxide on the whiskered surface thus increasing the total surface area of the metallic alloy substrate during oxidation. 9. The method of claim 8, wherein the aluminum-containing metallic alloy substrate is selected from the group consisting of MCrAlX, where M is cobalt (Co), Cr is chromium, Al is aluminum and X is at least one of yttrium (Y), zirconium (Zr), hafnium (Hf) and ytterbium (Yb). 10. The method of claim 9, wherein the aluminum-containing metallic alloy substrate is CoCrAlY. 11. The method of claim 9, wherein the aluminum-containing metallic alloy substrate is CoCrAlYb. 12. The method of claim 8, wherein the metallic alloy substrate is a fiber. 13. The method of claim 8, wherein the oxidizing of the metallic alloy substrate occurs at temperatures from approximately 800° C. to approximately 1000° C. 14. The method of claim 8, wherein the time period for heating is between approximately 10 hours to approximately 100 hours. 15. The method of claim 8, wherein the aluminum-containing metallic alloy substrate is selected from the group consisting of MCrAlX, where M is nickel (Ni)), Cr is chromium, Al is aluminum and X is at least one of, zirconium (Zr), hafnium (Hf) and ytterbium (Yb).