초록 ▼

Aqueous liquid and moisture vapor are added to water absorbent resin powder so that particles of the water absorbent resin powder are bound. Supplying the aqueous liquid and moisture vapor to the water absorbent resin powder reduces the amount of particles that remain unbound (ungranulated) and incr

Aqueous liquid and moisture vapor are added to water absorbent resin powder so that particles of the water absorbent resin powder are bound. Supplying the aqueous liquid and moisture vapor to the water absorbent resin powder reduces the amount of particles that remain unbound (ungranulated) and increases the concentration of the water absorbent resin bound particles to provide improved drying efficiency and to obtain particulate water absorbent resin having excellent properties even when the bound particles are highly concentrated. The present invention provides (i) a method for binding water absorbent resin and (ii) a method for producing particulate water absorbent resin including the step of binding particles of water absorbent resin powder.

대표청구항 ▼

1. A method for binding water absorbent resin, comprising the step of adding aqueous liquid and adding saturated moisture vapor to water absorbent resin powder so as to bind particles of the water absorbent resin powder, where the aqueous liquid and saturated moisture vapor are added at the same tim

1. A method for binding water absorbent resin, comprising the step of adding aqueous liquid and adding saturated moisture vapor to water absorbent resin powder so as to bind particles of the water absorbent resin powder, where the aqueous liquid and saturated moisture vapor are added at the same time to the water absorbent resin powder, and wherein 50 to 10 parts by weight of the aqueous liquid is added to 50 to 90 parts by weight of the water absorbent resin powder so that a total amount is 100 parts, the water absorbent resin powder containing an acid group and/or its salt (neutralized product), andthe water absorbent resin powder including 10 wt % or less of water with respect to the total weight of the water absorbent resin. 2. The method as set forth in claim 1, wherein the particles of the water absorbent resin powder are continuously bound. 3. The method as set forth in claim 1, wherein 1 to 100 kg/hr of the saturated moisture vapor is added to 100 kg/hr of the water absorbent resin powder. 4. The method as set forth in claim 1, wherein the particles of the water absorbent resin powder are bound by using a rotary disk mixer. 5. The method as set forth in claim 1, wherein the water absorbent resin powder includes powder of water absorbent resin whose surface has been crosslinked. 6. A method for producing particulate water absorbent resin, comprising the step of adding aqueous liquid and adding saturated moisture vapor to water absorbent resin powder so as to bind particles of the water absorbent resin powder, where said aqueous liquid and saturated moisture vapor are added at the same time to the water absorbent resin powder, the water absorbent resin powder containing an acid group and/or its salt (neutralized product), andthe water absorbent resin powder including 10 wt % or less of water with respect to the total weight of the water absorbent resin, and wherein a solid content of the water absorbent resin powder whose particles have been bound ranges from 50 to 90 wt %. 7. The method as set forth in claim 6, comprising plural steps of binding the particles of the water absorbent resin powder. 8. The method as set forth in claim 6, wherein granulated particles are obtained by the binding step, wherein said granulated particles having particle diameter ranges from 100 μm to 40 mm are added in a polymer classification step or in a step previous to a polymer classification step and subjected to a drying step, or where the granulated particles are added in a step previous to a polymer classification step without a drying step. 9. The method as set forth in claim 1, wherein a gage pressure of the saturated moisture vapor ranges from 0.1 to 2.0 MPa. 10. The method as set forth in claim 6, wherein a gage pressure of the saturated moisture vapor ranges from 0.1 to 2.0 MPa.