Inorganic board and method for manufacturing inorganic board
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B28B-003/00
B27N-003/00
B27N-003/04
B27N-003/08
B27N-003/10
C04B-014/38
C04B-022/00
C04B-024/10
출원번호
US-0785148
(2013-03-05)
등록번호
US-8628713
(2014-01-14)
우선권정보
JP-2012-146826 (2012-06-29)
발명자
/ 주소
Ikeda, Satoshi
Omori, Yusuke
출원인 / 주소
Nichiha Corporation
대리인 / 주소
Birch, Stewart, Kolasch & Birch, LLP
인용정보
피인용 횟수 :
0인용 특허 :
2
초록▼
An inorganic board contains, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml. Also, a method includes: step of producing a slurry
An inorganic board contains, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml. Also, a method includes: step of producing a slurry containing hydraulic material, reinforcing fiber, and wollastonite; step of producing a sheet by dehydrating the slurry; and step of pressing and curing the sheet; wherein, in the step of producing a slurry, a composition of the slurry is set so as to contain, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml.
대표청구항▼
1. An inorganic board, comprising, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml. 2. The inorganic board according to claim 1, w
1. An inorganic board, comprising, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml. 2. The inorganic board according to claim 1, wherein the wollastonite has a difference between a wet volume (after being allowed to stand for 15 minutes) and a wet volume (after being allowed to stand for 30 minutes) of less than 10%. 3. The inorganic board according to claim 1, which is a cured mat obtained by dehydrating a slurry. 4. The inorganic board according to claim 1, further comprising 18 to 64 mass % of inorganic admixture. 5. The inorganic board according to claim 4, wherein at least one of mica, pearlite, coal ash, paper sludge ash, and magnesium hydroxide is contained as the inorganic admixture, andat least one of waste paper and pulp is contained as the reinforcing fiber. 6. A method for manufacturing an inorganic board, comprising: a step of producing a slurry containing a hydraulic material, a reinforcing fiber, and wollastonite;a step of producing a sheet by dehydrating the obtained slurry; anda step of pressing and curing the obtained sheet;wherein, in the step of producing a slurry, a composition of the slurry is set so as to contain, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml. 7. The method for manufacturing an inorganic board according to claim 6, wherein, in the step of producing a slurry, wollastonite having a difference between a wet volume (after being allowed to stand for 15 minutes) and a wet volume (after being allowed to stand for 30 minutes) of less than 10% is used. 8. The method for manufacturing an inorganic board according to claim 6, wherein, in the step of producing a slurry, the slurry is produced so as to further contain 18 to 64 mass % of inorganic admixture in a solid content ratio. 9. The method for manufacturing an inorganic board according to claim 8, wherein, in the step of producing a slurry, at least one of mica, pearlite, coal ash, paper sludge ash, and magnesium hydroxide is used as the inorganic admixture, and at least one of waste paper and pulp is used as the reinforcing fiber.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (2)
Krowl, Thomas R., Calcium silicate insulating material containing blast furnace slag cement.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.