초록 ▼

Disclosed are methods for treating and coating a ferrous metal substrate, such as cold rolled steel, hot rolled steel, and electrogalvanized steel. These methods include contacting the ferrous metal substrate with an aqueous pretreatment composition comprising: (a) a Group IIIB and/or IVB metal comp

Disclosed are methods for treating and coating a ferrous metal substrate, such as cold rolled steel, hot rolled steel, and electrogalvanized steel. These methods include contacting the ferrous metal substrate with an aqueous pretreatment composition comprising: (a) a Group IIIB and/or IVB metal compound; (b) phosphate ions; and (c) water.

대표청구항 ▼

1. A method for coating a ferrous metal substrate, comprising: (a) contacting the ferrous metal substrate with an aqueous pretreatment composition having a pH of 4 to 5.5 and comprising: (i) a Group IIIB and/or IVB metal compound;(ii) phosphate ions; and(iii) water,wherein the Group IIIB and/or IVB

1. A method for coating a ferrous metal substrate, comprising: (a) contacting the ferrous metal substrate with an aqueous pretreatment composition having a pH of 4 to 5.5 and comprising: (i) a Group IIIB and/or IVB metal compound;(ii) phosphate ions; and(iii) water,wherein the Group IIIB and/or IVB metal compound is present in the pretreatment composition in an amount of 10 to 500 ppm metal and the weight ratio of Group IIIB and/or IVB metal to phosphate ions in the pretreatment composition is at least 0.8:1; andwherein the phosphate ions are maintained in a bath of the pretreatment composition in an amount:(i) sufficient to essentially prevent the formation of insoluble rust in the bath; and(ii) insufficient to prevent the deposition of a Group IIIB or IVB metal film having a coverage of at least 10 mg/m2 on the ferrous metal substrate;(iii) resulting in a weight ratio of phosphate to ferric ions of 1 to 1.7:1; and then(b) contacting the substrate with a coating composition comprising a film-forming resin to form a coated metal substrate that exhibits corrosion resistance properties. 2. The method of claim 1, wherein the ferrous metal substrate comprises cold rolled steel. 3. The method of claim 1, wherein the pretreatment composition is brought into contact with the ferrous metal substrate by spraying. 4. The method of claim 1, wherein the IVB metal compound used in the pretreatment composition is a compound of zirconium. 5. The method of claim 4, wherein the compound of zirconium comprises hexafluorozirconic acid. 6. The method of claim 1, wherein the group IIIB and/or IVB metal compound is present in the pretreatment composition in an amount of at least 10 ppm metal and no more than 150 ppm metal. 7. The method of claim 1, wherein a source of phosphate ions is phosphoric acid and/or monosodium phosphate. 8. The method of claim 1, wherein the pretreatment composition also comprises an electropositive metal. 9. The method of claim 1, wherein the pH of the pretreatment composition ranges from 4.5 to 5.5. 10. The method of claim 1, wherein the phosphate ions are maintained in a bath of the pretreatment composition in an amount (iii) resulting in a weight ratio of phosphate to ferric ions of 1.2 to 1.7:1. 11. A method for coating a ferrous metal substrate, comprising: (a) contacting the ferrous metal substrate with an aqueous pretreatment composition having a pH of 4 to 5.5 and comprising: (i) a Group IIIB and/or IVB metal compound;(ii) phosphate ions; and(iii) water,wherein the Group IIIB and/or IVB metal compound is present in the pretreatment composition in an amount of 10 to 500 ppm metal and the weight ratio of Group IIIB and/or IVB metal to phosphate ions in the pretreatment composition is at least 0.8:1; andwherein the phosphate ions are maintained in a bath of the pretreatment composition in an amount:(i) sufficient to essentially prevent the formation of insoluble rust in the bath; and(ii) insufficient to prevent the deposition of a Group IIIB or IVB metal film having a coverage of at least 10 mg/m2 on the ferrous metal substrate;(iii) resulting in a weight ratio of phosphate to additional soluble iron in the ferrous state in a range of 1.7 to 10:1; and then(b) contacting the substrate with a coating composition comprising a film-forming resin to form a coated metal substrate that exhibits corrosion resistance properties. 12. The method of claim 11, wherein the ferrous metal substrate comprises cold rolled steel. 13. The method of claim 11, wherein the pretreatment composition is brought into contact with the ferrous metal substrate by spraying. 14. The method of claim 11, wherein the group IVB metal compound used in the pretreatment composition is a compound of zirconium. 15. The method of claim 14, wherein the compound of zirconium comprises hexafluorozirconic acid. 16. The method of claim 11, wherein the group IIIB and/or IVB metal compound is present in the pretreatment composition in an amount of at least 10 ppm metal and no more than 150 ppm metal. 17. The method of claim 11, wherein a source of phosphate ions is phosphoric acid and/or monosodium phosphate. 18. The method of claim 11, wherein the pretreatment composition also comprises an electropositive metal. 19. The method of claim 11, wherein the pH of the pretreatment composition ranges from 4.5 to 5.5. 20. The method of claim 11, wherein the phosphate ions are maintained in a bath of the pretreatment composition in an amount (iii) resulting in a weight ratio of phosphate to ferric ions of 1.0 to 1.7:1.