Process for manufacturing a self-sealing composition
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C08J-003/20
C08J-003/22
C08L-009/00
C08L-025/02
C08K-003/00
C08K-005/00
출원번호
US-0057138
(2009-07-23)
등록번호
US-8710140
(2014-04-29)
우선권정보
FR-08 55320 (2008-08-01)
국제출원번호
PCT/EP2009/005344
(2009-07-23)
§371/§102 date
20110502
(20110502)
국제공개번호
WO2010/012412
(2010-02-04)
발명자
/ 주소
Pialot, Frederic
Fombelle, Damien
Voge, Bozena
Merino Lopez, Jose
출원인 / 주소
Michelin Recherche et Technique S.A.
대리인 / 주소
Cozen O'Connor
인용정보
피인용 횟수 :
4인용 특허 :
10
초록▼
Process for manufacturing a self-sealing elastomer composition, wherein the process comprises the following steps: firstly a masterbatch comprising at least one diene elastomer and a thermoplastic plasticizing hydrocarbon resin with a content greater than 30 phr is manufactured by compounding these
Process for manufacturing a self-sealing elastomer composition, wherein the process comprises the following steps: firstly a masterbatch comprising at least one diene elastomer and a thermoplastic plasticizing hydrocarbon resin with a content greater than 30 phr is manufactured by compounding these various components in a mixer at a temperature or up to a temperature called the “hot compounding temperature” which is above the softening point of the hydrocarbon resin; and then at least one crosslinking system is incorporated into the masterbatch thus prepared, by compounding everything, in the same mixer or in a different mixer, at a temperature or up to a maximum temperature which is kept below 100° C., in order to obtain said self-sealing composition, and wherein at least one liquid plasticizer having a glass transition temperature (Tg) below −20° C. is furthermore incorporated in an amount of less than 60 phr into said masterbatch or into said composition.
대표청구항▼
1. A process for manufacturing a self-sealing elastomer composition, wherein said process comprises the steps of: a) firstly a masterbatch comprising at least one diene elastomer and a hydrocarbon resin with a content greater than 30 phr is manufactured by compounding these various components in a m
1. A process for manufacturing a self-sealing elastomer composition, wherein said process comprises the steps of: a) firstly a masterbatch comprising at least one diene elastomer and a hydrocarbon resin with a content greater than 30 phr is manufactured by compounding these various components in a mixer at a temperature or up to a temperature called the “hot compounding temperature” which is above the softening point of the hydrocarbon resin; andb) then at least one crosslinking system is incorporated into the masterbatch thus prepared, by compounding everything, in the same mixer or in a different mixer, at a temperature or up to maximum temperature which is kept below 100° C., in order to obtain said self-sealing composition, and wherein at least one liquid plasticizer having a glass transition temperature (Tg) below −20° C. is furthermore incorporated in an amount of 5 to 40 phr into said masterbatch or into said composition, wherein the liquid plasticizer is chosen from the group of liquid elastomers, polyolefinic oils, naphthenic oils, paraffinic oils, DAE oils, MES oils, TDAE oils, mineral oils, vegetable oils, ester plasticizers, phosphate plasticizers and mixtures of these compounds, and wherein the number-average molecular weight of the liquid plasticizer is between 300 and 90,000 g/mol. 2. The process according to claim 1, wherein, during the hot compounding step a), the diene elastomer is brought into contact with the hydrocarbon resin in the solid state. 3. The process according to claim 1, wherein, during the hot compounding step a), the diene elastomer is brought into contact with the hydorcarbon resin in the liquid state. 4. The process according to claim 3, wherein the hydrocarbon resin is injected in the liquid state into the mixer. 5. The process according to claim 1, wherein step a) of hot compounding the diene elastomer with the hydrocarbon resin is carried out away from oxygen. 6. The process according to claim 1, wherein the hot compounding temperature is above 70° C. 7. The process according to claim 1, wherein the hot compounding step a) is carried out in a compounding screw extruder. 8. The process according to claim 1, wherein the maximum compounding temperature of step b) is kept below 80° C. 9. The process according to claim 1, wherein the maximum compounding temperature of step b) is kept below the softening point of the hydrocarbon resin. 10. The process according to claim 1, wherein the maximum compounding temperature of step b) is kept below 50° C. 11. The process according to claim 1, wherein the compounding step b) is carried out on a two-roll open mill. 12. The process according to claim 11, wherein the rolls of the open mill are cooled to a temperature below 40° C. 13. The process according to claim 1, wherein an intermediate step of cooling the masterbatch is inserted between steps a) and b) so as to cool said masterbatch to a temperature below 100° C. 14. The process according to claim 13, wherein the temperature to which the masterbatch is cooled during said intermediate cooling step is below 80° C. 15. The process according to claim 13, wherein the temperature to which the masterbatch is cooled during said intermediate cooling step is below the softening point of the hydrocarbon resin. 16. The process according to claim 1, wherein between 0 and 30 phr of a filler is added to the composition. 17. The process according to claim 16, wherein the filler is introduced during compounding step b). 18. The process according to claim 17, wherein the filler is carbon black. 19. The process according to claim 18, wherein the carbon black content is less than 5 phr. 20. The process according to claim 19, wherein the carbon black content is between 0.5 and 2 phr. 21. The process according to claim 1, wherein the diene elastomer is chosen from the group of polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, isoprene copolymers and blends of such elastomers. 22. The process according to claim 21, wherein the diene elastomer is an isoprene elastomer chosen from the group of natural rubber, synthetic polyisoprenes and blends of such elastomers. 23. The process according to claim 1, wherein the diene elastomer content is greater than 50 phr. 24. The process according to claim 22, wherein the isoprene elastomer is the sole elastomer of the composition. 25. The process according to claim 1, wherein the hydrocarbon resin content is in the 45 to 75 phr range. 26. The process according to claim 1, wherein the hydrocarbon resin has a glass transition temperature which is above 0° C. 27. The process according to claim 1, wherein the number-average molecular weight (Mn) of the hydrocarbon resin is between 400 and 2000 g/mol. 28. The process according to claim 1, wherein the hydrocarbon resin is chosen from the group of cyclopentadiene homopolymer or copolymer resins, dicyclopentadiene homopolymer or copolymer resins, terpene hompolymer or copolymer resins, C5-cut homopolymer or copolymer resins, C9-cut hompolymer or copolymer resins and blends of these resins. 29. The process according to claim 1, wherein the liquid plasticizer is incorporated into the masterbatch. 30. The process according to claim 29, wherein the liquid plasticizer is incorporated into the masterbatch at the same time as the hydrocarbon resin. 31. The process according to claim 1, wherein the liquid plasticizer is chosen from the group of liquid elastomers, polyolefinic oils, vegetable oils and mixtures of these compounds. 32. The process according to claim 1, wherein the crosslinking system is a vulcanization system based on sulphur and optionally a guanidine derivative. 33. The process according to claim 32, wherein the guanidine derivative is diphenylguanidine. 34. The process according to claim 32, wherein the vulcanization system comprises between 0.1 and 1.5 phr of sulphur and between 0 and 1.5 phr of guanidine derivative.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (10)
Hashimoto Takatsugu,JPX, High aromatic oil and rubber composition and oil extended synthetic rubber using the same.
Blok Edward John ; Kralevich ; Jr. Mark Leslie ; Sandstrom Paul Harry ; Futamura Shingo, Rubber composition with liquid high Tg polymer and tire with tread thereof.
Cohen Martin Paul ; Losey Cheryl Ann ; Roennau Raymond Benjamin ; Futamura Shingo ; Materne Thierry Florent Edme,BEX ; Hunt James Oral,LUX ; Thise Ghislain Adolphe Leon,BEX, Silica reinforced rubber composition and tire with tread.
De Trano Mario N. (Massillon OH) Hergenrother William L. (Akron OH) Maglio Ralph A. (Wadsworth OH) Roggeman David M. (North Royalton OH), Solution compounding process for achieving uniform, fine particle size dispersion of curing agents.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.