The present invention provides wood preservative compositions comprising micronized particles. In one embodiment, the composition comprises dispersions of micronized metal or metal compounds. In another embodiment, the wood preservative composition comprises an inorganic component comprising a metal
The present invention provides wood preservative compositions comprising micronized particles. In one embodiment, the composition comprises dispersions of micronized metal or metal compounds. In another embodiment, the wood preservative composition comprises an inorganic component comprising a metal or metal compound and organic biocide. When the composition comprises an inorganic component and an organic biocide, the inorganic component or the organic biocide or both are present as micronized particles. When compositions of the present invention are used for preservation of wood, the micronized particles can be observed as uniformly distributed within the wood and there is minimal leaching of the metal and biocide from the wood.
대표청구항▼
1. Wood comprising an aqueous wood preservative composition, wherein the composition comprises: (a) a biocidally effective amount of particles of a copper compound with a particle size of between 0.001 and 1.0 microns, dispersed in water; and(b) a biocidally effective amount of one or more organic b
1. Wood comprising an aqueous wood preservative composition, wherein the composition comprises: (a) a biocidally effective amount of particles of a copper compound with a particle size of between 0.001 and 1.0 microns, dispersed in water; and(b) a biocidally effective amount of one or more organic biocides;wherein the copper compound is selected from the group consisting of copper hydroxide, cupric oxide, cuprous oxide, copper carbonate, basic copper carbonate, copper oxychloride, copper dimethyldithiocarbamate, copper omadine, and copper borate, andwherein the particles of the copper compound are obtained by milling, distributed throughout a cross-section of the wood, and render the wood resistant to fungal decay. 2. The wood of claim 1, wherein the organic biocide is selected from a group consisting of fungicide, insecticide, algaecide, moldicide, and bactericide. 3. The wood of claim 1, wherein the organic biocide is an azole, a borate, or a fluoride. 4. The wood of claim 3, wherein the organic biocide is an azole. 5. The wood of claim 4, wherein the azole is tebuconazole. 6. The wood of claim 1, wherein the organic biocide is a solid. 7. The wood of claim 6, wherein the organic biocide has a particle size of between 0.001 and 25 microns. 8. The wood of claim 7, wherein the organic biocide is tebuconazole. 9. The wood of claim 1, wherein the wood comprises coniferous wood. 10. The wood of claim 9, wherein the coniferous wood comprises southern pine. 11. The wood of claim 1, wherein the particles of copper compound are uniformly distributed throughout a cross-section of the wood. 12. The wood of claim 11, wherein copper leaching from the wood is reduced as compared to copper leaching from a wood comprising copper monoethanolamine complex. 13. The wood of claim 1, wherein the wood is lumber. 14. Wood comprising an aqueous wood preservative composition, wherein the composition comprises: (a) a biocidally effective amount of particles of a copper compound with a particle size of between 0.001 and 1.0 microns, dispersed in water; and(b) a biocidally effective amount of one or more organic biocides;wherein the copper compound is selected from the group consisting of copper hydroxide, cupric oxide, cuprous oxide, copper carbonate, basic copper carbonate, copper oxychloride, copper dimethyldithiocarbamate, copper omadine, and copper borate,wherein the particles of the copper compound are distributed throughout a cross-section of the wood and render the wood resistant to fungal decay, andwherein copper leaching from the wood is reduced as compared to copper leaching from a wood comprising copper monoethanolamine complex. 15. The wood of claim 14, wherein the organic biocide is selected from a group consisting of fungicide, insecticide, algaecide, moldicide, and bactericide. 16. The wood of claim 14, wherein the organic biocide is an azole, a borate, or a fluoride. 17. The wood of claim 16, wherein the organic biocide is an azole. 18. The wood of claim 17, wherein the azole is tebuconazole. 19. The wood of claim 14, wherein the organic biocide is a solid. 20. The wood of claim 19, wherein the organic biocide has a particle size of between 0.001 and 25 microns. 21. The wood of claim 20, wherein the organic biocide is tebuconazole. 22. The wood of claim 14, wherein the wood comprises coniferous wood. 23. The wood of claim 22, wherein the coniferous wood comprises southern pine. 24. The wood of claim 14, wherein the particles of copper compound are uniformly distributed throughout a cross-section of the wood. 25. The wood of claim 14, wherein the wood is lumber.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (97)
Petigara Ramesh B. (Hatfield PA), 3-Isothiazolones as biocides.
Iwasaki Tetsuji (Wakayama JPX) Kamihisa Yasushi (Wakayama JPX), Biocidal fine powder, its manufacturing method and a suspension for agricultural use containing the above powder.
Neville Matthew (Champaign IL) Fluck David J. (Pesotum IL) Hung Cheng-Hung (Champaign IL) Lucarelli Michael A. (Mattoon IL) Scherber Debra L. (Orangevale CA), Chemical mechanical polishing slurry for metal layers.
Kyte Colin T. (Marlow GB2) Lewis Geoffrey J. (Hazelmere GB2) Pearce Edgar (High Wymcombe GB2) Hume Keith (Camberley GB2), Method of treating timber with composition having a colloidal pigment.
Ludwig Georg-Wilhelm (Krefeld) Exner Otto (Ratingen) Paulus Wilfried (Krefeld) Bchel Karl-Heinz (Burscheid) Holmwood Graham (Wuppertal DEX), Microbicidal active compound combinations.
Williams Gareth (Netherton GB3) Cornfield Judith A. (Castleford GB3) Brown Janet (Castleford GB3) Ryan Neil P. (South Elmsall GB3), Preservatives for wood and other cellulosic materials.
Mulqueen Patrick Joseph,GBX ; Lubetkin Steven Duff,GBX ; Banks Graham,GBX ; Fowles Andrew Mark,GBX, Storage and dilution of stable aqueous dispersions.
Liversidge Gary G. (West Chester PA) Cundy Kenneth C. (Pottstown PA) Bishop John F. (Rochester NY) Czekai David A. (Honeoye Falls NY), Surface modified drug nanoparticles.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.