초록 ▼

In order to obtain a graphite film having an excellent thermal diffusivity, a high density, and excellent flatness without flaws, recesses and wrinkles on the surface, the process for producing a graphite film according to the present invention comprises the graphitization step for a raw material fi

In order to obtain a graphite film having an excellent thermal diffusivity, a high density, and excellent flatness without flaws, recesses and wrinkles on the surface, the process for producing a graphite film according to the present invention comprises the graphitization step for a raw material film made of a polymer film and/or a carbonized polymer film and/or the post-planar pressurization step for the film in this order to prepare a graphite film, wherein the graphitization step is a step of thermally treating two or more stacked raw material films at a highest temperature of 2,000° C. and includes a method of electrically heating the raw material films themselves and/or a method of thermally treating the films while applying pressure to the films planarly, and the post-planar pressurization step includes a method of planarly pressurizing the one raw material film or the multiple stacked raw material films after graphitization by single-plate press or vacuum press.

대표청구항 ▼

1. A process for producing a graphite film comprising the steps of: graphitizing a raw material film made of a polymer film and/or a carbonized polymer film; andconducting a post-planar pressurization step after the step of graphitizing, so that a planar pressure is uniformly and simultaneously appl

1. A process for producing a graphite film comprising the steps of: graphitizing a raw material film made of a polymer film and/or a carbonized polymer film; andconducting a post-planar pressurization step after the step of graphitizing, so that a planar pressure is uniformly and simultaneously applied to the graphitized raw material film, whereinthe graphitized raw material film is pressurized together with a film-like medium other than the graphitized raw material film in the post-planar pressurization step, thereby reducing wrinkles on the graphitized raw material,the graphitization step includes thermal treatment at a temperature of 2,400° C. or higher, andthe raw material film is retained in and in contact with a container that is directly electrified by application of voltage and graphitized while electrifying the container by application of voltage in the graphitization step. 2. The process for producing a graphite film according to claim 1, wherein the container that can be directly electrified by application of voltage is a graphite container. 3. The process for producing a graphite film according to claim 2, wherein the graphitization step is carried out with carbon powder packed between the graphite container and the raw material film and/or around the outer periphery of the graphite container. 4. The process for producing a graphite film according to claim 1, wherein the carbonized polymer film is obtained by a carbonization step of thermally treating a polymer film at a temperature of 600 to 1,800° C. 5. The process for producing a graphite film according to claim 1, wherein the graphitization step is carried out in the state where the two or more raw material films are stacked. 6. The process for producing a graphite film according to claim 5, wherein the number of the stacked films is ten or more in the state where the two or more raw material films are stacked. 7. The process for producing a graphite film according to claim 5, wherein the graphitization step is carried out in the state where the two or more raw material films are stacked and a carbon material having a height smaller than the height of the stacked films is present around the stacked films. 8. The process for producing a graphite film according to claim 1, wherein the post-planar pressurization step is carried out by using a single plate. 9. The process for producing a graphite film according to claim 1, wherein the pressurization is carried out by vacuum press in the post-planar pressurization step. 10. The process for producing a graphite film according to claim 1, wherein the multiple graphitized raw material films are simultaneously pressurized in the post-planar pressurization step. 11. The process for producing a graphite film according to claim 10, further comprising an independent recovery step of recovering the multiple graphitized raw material films planarly pressurized as independent graphite films after the post-planar pressurization step. 12. A process for producing a graphite film comprising the steps of: graphitizing a raw material film made of a polymer film and/or a carbonized polymer film; andconducting a post-planar pressurization step after the step of graphitizing, so that a planar pressure is uniformly and simultaneously applied to the graphitized raw material film, whereinthe multiple graphitized raw material films are simultaneously pressurized in the post-planar pressurization step, thereby reducing wrinkles on the graphitized raw material, andthe process further comprises the independent recovery step of recovering the multiple graphitized raw material films planarly pressurized as independent graphite films after the post-planar pressurization step,the graphitization step includes thermal treatment at a temperature of 2,400° C. or higher, andthe raw material film is retained in and in contact with a container that is directly electrified by application of voltage and graphitized while electrifying the container by application of voltage in the graphitization step. 13. The process for producing a graphite film according to claim 12, wherein the container that can be directly electrified by application of voltage is a graphite container. 14. The process for producing a graphite film according to claim 13, wherein the graphitization step is carried out with carbon powder packed between the graphite container and the raw material film and/or around the outer periphery of the graphite container. 15. The process for producing a graphite film according to claim 12, wherein the carbonized polymer film is obtained by a carbonization step of thermally treating a polymer film at a temperature of 600 to 1,800° C. 16. The process for producing a graphite film according to claim 12, wherein the graphitization step is carried out in the state where the two or more raw material films are stacked. 17. The process for producing a graphite film according to claim 16, wherein the number of the stacked films is ten or more in the state where the two or more raw material films are stacked. 18. The process for producing a graphite film according to claim 16, wherein the graphitization step is carried out in the state where the two or more raw material films are stacked and a carbon material having a height smaller than the height of the stacked films is present around the stacked films. 19. The process for producing a graphite film according to claim 12, wherein the pressurization is carried out by single-plate press in the post-planar pressurization step. 20. The process for producing a graphite film according to claim 12, wherein the pressurization is carried out by vacuum press in the post-planar pressurization step. 21. The process for producing a graphite film according to claim 12, wherein the graphitized raw material film is pressurized together with a film-like medium other than the graphitized raw material film in the post-planar pressurization step. 22. The process for producing a graphite film according to claim 1, wherein the step of graphitizing the raw material film is conducted by applying a planner pressure. 23. The process for producing a graphite film according to claim 12, wherein the step of graphitizing the raw material film is conducted by applying a planner pressure. 24. A process for producing a graphite film comprising a step of graphitizing a raw material film made of a polymer film and/or a carbonized polymer film and a post-planar pressurization step for planarly pressurizing the graphitized raw material film after the step of graphitizing, wherein the graphitized raw material film is pressurized together with a film-like medium other than the graphitized raw material film in the post-planar pressurization step,the raw material film is retained in and in contact with a container that can be directly electrified by application of voltage and graphitized while electrifying the container by application of voltage in the graphitization step,the container that can be directly electrified by application of voltage is a graphite container, andthe graphitization step is carried out with carbon powder packed between the graphite container and the raw material film and/or around the outer periphery of the graphite container. 25. A process for producing a graphite film comprising a step of graphitizing a raw material film made of a polymer film and/or a carbonized polymer film and a post-planar pressurization step for planarly pressurizing the graphitized raw material film after the step of graphitizing, wherein the graphitized raw material film is pressurized together with a film-like medium other than the graphitized raw material film in the post-planar pressurization step, whereinthe graphitization step is carried out in the state where the two or more raw material films are stacked, andthe graphitization step is carried out in the state where the two or more raw material films are stacked and a carbon material having a height smaller than the height of the stacked films is present around the stacked films. 26. A process for producing a graphite film comprising the step of graphitizing a raw material film made of a polymer film and/or a carbonized polymer film and a post-planar pressurization step for planarly pressurizing the graphitized raw material film after the step of graphitizing, wherein the multiple graphitized raw material films are simultaneously pressurized in the post-planar pressurization step,the process further comprises the independent recovery step of recovering the multiple graphitized raw material films planarly pressurized as independent graphite films after the post-planar pressurization step,the raw material film is retained in and in contact with a container that can be directly electrified by application of voltage and graphitized while electrifying the container by application of voltage in the graphitization step,the container that can be directly electrified by application of voltage is a graphite container, andthe graphitization step is carried out with carbon powder packed between the graphite container and the raw material film and/or around the outer periphery of the graphite container. 27. A process for producing a graphite film comprising the step of graphitizing a raw material film made of a polymer film and/or a carbonized polymer film and a post-planar pressurization step for planarly pressurizing the graphitized raw material film after the step of graphitizing, wherein the multiple graphitized raw material films are simultaneously pressurized in the post-planar pressurization step,the process further comprises the independent recovery step of recovering the multiple graphitized raw material films planarly pressurized as independent graphite films after the post-planar pressurization step,the graphitization step is carried out in the state where the two or more raw material films are stacked, andthe graphitization step is carried out in the state where the two or more raw material films are stacked and a carbon material having a height smaller than the height of the stacked films is present around the stacked films.