초록 ▼

Iodine containing amorphous fluoropolymers having at least one fluoropolymer with a cure site, where the fluoropolymer has a Mooney viscosity of 2 or less (ML 1+10) at 100° C. according to ASTM D1646, and a peel strength to a roll mill of 10 dN/cm or less and methods for making such iodine containin

Iodine containing amorphous fluoropolymers having at least one fluoropolymer with a cure site, where the fluoropolymer has a Mooney viscosity of 2 or less (ML 1+10) at 100° C. according to ASTM D1646, and a peel strength to a roll mill of 10 dN/cm or less and methods for making such iodine containing amorphous fluoropolymers are described. Articles derived from the cured product of such iodine containing amorphous fluoropolymers are also described. Solutions, dispersions and coatings derived from such iodine containing amorphous fluoropolymers are also described.

대표청구항 ▼

1. An iodine containing amorphous fluoropolymer composition comprising a first fluoropolymer having a cure site wherein the cure site is an iodine group derived from 1,4-diiodooctafluorobutane, and the cure site is present in an amount of from 0.25 to 1 mol %, further wherein the first fluoropolymer

1. An iodine containing amorphous fluoropolymer composition comprising a first fluoropolymer having a cure site wherein the cure site is an iodine group derived from 1,4-diiodooctafluorobutane, and the cure site is present in an amount of from 0.25 to 1 mol %, further wherein the first fluoropolymer has a total weight percent of iodine of from 0.2 to 2 wt %, and further wherein the first fluoropolymer comprises repeating units derived from vinylidene difluoride and hexafluoropropylene and has a Mooney viscosity of 2 or less, ML 1+10, at 100° C. according to ASTM D1646-06 TYPE A, and further wherein the first fluoropolymer has a storage modulus at 25° C. and 6.3 rad/s of greater than or equal to 300 kPa and at 25° C. and 0.1 rad/s of less than or equal to 200 kPa. 2. An aqueous dispersion comprising the iodine containing amorphous fluoropolymer composition of claim 1. 3. A coating composition comprising the dispersion of claim 2. 4. The fluoropolymer composition according to claim 1 wherein the first fluoropolymer comprises at least one cure site monomer. 5. The fluoropolymer composition of claim 4 wherein the cure site monomer is selected from the group consisting of CH2═CHI, CF2═CHI, CF2═CFI, CH2═CHCH2I, CF2═CFCF2I, CH2═CHCF2CF2I, CF2═CFCH2CH2I, CF2═CFCF2CF2I, CH2═CH(CF2)6CH2CH2I, CF2═CFOCF2CF2I, CF2═CFOCF2CF2CF2I, CF2═CFOCF2CF2CH2I, CF2═CFCF2OCH2CH2I, CF2═CFO(CF2)3—OCF2CF2I, CH2═CHBr, CF2═CHBr, CF2═CFBr, CH2═CHCH2Br, CF2═CFCF2Br, CH2═CHCF2CF2Br, CF2═CFOCF2CF2Br. 6. The fluoropolymer composition according to claim 1 further comprising a filler. 7. The fluoropolymer composition according to claim 1 wherein the fluoropolymer first is peroxide curable. 8. The fluoropolymer composition according to claim 1 further comprising a peroxide and a coagent. 9. The fluoropolymer composition according to claim 1 further comprising at least a second amorphous fluoropolymer having a Mooney viscosity of greater than 2, ML 1+10 at 100° C. according to ASTM D1646. 10. The fluoropolymer composition according to claim 1 wherein the first fluoropolymer further comprises interpolymerized units derived from formal containing perfluorovinylethers. 11. The fluoropolymer composition according to claim 1 wherein the first fluoropolymer is formed by emulsifier-free polymerization. 12. The fluoropolymer composition according to claim 1 wherein the first fluoropolymer is polymerized with a buffer or ammonium hydroxide. 13. The fluoropolymer composition according to claim 1 wherein the first fluoropolymer is coagulated by shear or salt. 14. The fluoropolymer composition according to claim 1 wherein the first fluoropolymer is coagulated with adding salt and ammonium hydroxide. 15. A solution comprising the iodine containing amorphous fluoropolymer composition of claim 1. 16. A coating composition comprising the solution of claim 15.