초록 ▼

Additives for application in construction chemistry are proposed comprising an organic and/or inorganic core component A) with rheology-enhancing properties and a shell component B) applied to the same by virtue of physical and/or chemical interactions which acts as a coating. Component A) should be

Additives for application in construction chemistry are proposed comprising an organic and/or inorganic core component A) with rheology-enhancing properties and a shell component B) applied to the same by virtue of physical and/or chemical interactions which acts as a coating. Component A) should be a of water-soluble and/or water-swellable and/or water-absorbable compound of the non-cellulose type with viscosity-enhancing properties in the final application. The shell component B) should preferably be a film-forming polymer which is able to release component A) during the application in construction chemistry in a retarded manner such as for example polyvinyl alcohol, polyvinyl acetate and polyethylene glycol. Component B) can be composed of several layers and comprises at least one reactive layer. The new additive is used as an additive with a time-delayed action in paints and also for timed control of the increase in viscosity or development of rheology in building material systems based on inorganic binders.

대표청구항 ▼

1. An additive comprising at least one core component A) selected from an inorganic core component and an organic component wherein the organic core component comprises a non-cellulosic water-soluble, water-swellable or water-absorbable compound selected from the group consisting of an oligosacchari

1. An additive comprising at least one core component A) selected from an inorganic core component and an organic component wherein the organic core component comprises a non-cellulosic water-soluble, water-swellable or water-absorbable compound selected from the group consisting of an oligosaccharide, a polysaccharide, a sulfo group-containing copolymer and a copolymer based on acrylamide, and wherein the inorganic core component is derived from borax, ammonium sulphate or zeolite, with a rheology-enhancing property and a shell component B) applied to the same by virtue of a chemical interaction which acts as a coating, wherein the shell component B) forms chemical cross-links with the core component A) and wherein the shell component B) consists of a film-forming polymer selected from the group consisting of polyvinyl alcohol, polyvinyl acetate, polyvinyl pyrrolidine, polyvinylidene chloride, an alginate, a cellulose derivative, a starch derivative, gelatin, a wax, and mixtures thereof, or a dialdehyde, and at least one additional process additive selected from a plasticizer, an anticaking agent, or an antifoaming agent, and the shell component B) is applied onto the core component A) with the aid of component C), wherein component C) is a dialdehyde in liquid form and has resulted in a chemical crosslinking of the shell component B). 2. The additive according to claim 1, wherein, component A) exhibits at least one property selected from the group consisting of plasticity, dynamic viscosity, flow limit, rheopexy and thixotrophy. 3. The additive according to claim 1, wherein the sulfo group-containing copolymer is a water-soluble or water-swellable sulfo group-containing copolymer containing at least one a) 3 to 96 mole % structural groups of formula I; wherein R1 is hydrogen or methyl, R2, R3 and R4 are independently selected from hydrogen, an aliphatic hydrocarbon residue with 1 to 6 C atoms, or a phenyl residue optionally substituted with methyl groups;M is hydrogen, a monovalent or divalent metal cation, ammonium or an organic amine residue; andA is ½ or 1;b) 3 to 96 mole % of at least one structural croup of formula IIa or IIb wherein R5 and R6 are independently hydrogen, an optionally substituted aliphatic hydrocarbon residue with 1 to 20 C atoms, a cycloaliphatic hydrocarbon residue with 5 to 8 C atoms, an aryl residue with 6 to 14 C atoms;Q is hydrogen or —CHR5R7;wherein if Q is not H, R5 and R6 in IIb together form a —CH2—(CH2)y-methylene group in which y is from 1 to 4;R7 is hydrogen, an aliphatic hydrocarbon residue with 1 to 4 C atoms, —COOH or —COO−Ma and R1and M are as defined above,c) 0.05 to 75 mole % of a structural group of formula III wherein Y is O, NH or NR5;R8 is R5 or R6;X is halogen, C1 to C4 alkylsulfate or C1 to C4 alkylsulfonate;X is 1 to 6;and R1, R5 and R6 are as defined above;d) 0.01 to 50 mole % of a structural group of formula IV wherein Z is —COO(CmH2mO)n—R5, —(CH2)p—O(CmH2mO)n—R5;m is from 2 to 4;n is from 0 to 200;p is from 0 to 20;and R1 is defined above. 4. The additive according to claim 1, wherein the sulfo group-containing copolymer is a water-soluble or water-swellable sulfo group-containing copolymer comprising a) 3 to 96 mole % of a structural group of formula V wherein R1 is hydrogen or methyl R2, R3 and R4 are independently hydrogen, an aliphatic hydrocarbon residue with 1 to 6 C atoms or a phenyl residue optionally substituted with methyl groups;M is hydrogen, a monovalent or divalent metal cation, ammonium or an organic amine residue; anda is ½ or 1;b) 3 to 96 mole % of a structural group of at least one of formula IVa or VIb wherein W is —CO—, —CO—O—(CH2)x—, or —CO—NR2—(CH2)x—; x is 1 to 6;R5 and R6 are independently hydrogen, an optionally substituted aliphatic hydrocarbon residue with 1 to 20 C atoms, a cycloaliphatic hydrocarbon residue with 5 to 8 C atoms, an aryl residue with, 6 to 14 C atoms and Q is hydrogen or —CHR5R7; wherein if Q is not H, R5 and R6 in IIb together form a —CH2—(CH2)y-methylene group in which y=1 to 4;R7 is hydrogen, an aliphatic hydrocarbon residue with 1 to 4 C atoms, —COOH or —COO−Ma; andR1, R2 and M are as defined above;c) 0.05 to 75 mole % of a structural group of at least one of formula VIIa or VIIb wherein Y is O, NH or NR5;V is —(CH2)x—, R8 is R5 or X is halogen, C1 to C4 alkylsulfate or C1 to C4 alkylsulfonate; andR1, R2, R3, R5, R6 and x are as defined above;d) 0.01 to 30 mole % a structural group of formula VIII wherein Z=—COO(CmH2mO)n—R9, —(CH2)p—O(CmH2mO)n—R9; R9 is or a saturated or unsaturated, linear or branched, aliphatic hydrocarbon residues with 22 to 40 C atoms; R10 is H, C1-C4 alkyl, phenyl, benzyl, C1-C4 alkoxy, halogen, cyano, —COOH, —COOR5, —CO—NH2 or —OCOR5;R11 is an arylalkyl group with a C1-C12 alkyl or C6-C14 aryl residue; M is from 2 to 4;n is from 0 to 200;p is from 0 to 20;and R1 and R5 are as defined above. 5. The additive according to claim 1, wherein the sulfo group-containing copolymer is a water-soluble sulfo group-containing copolymer and terpolymer having a number average molecular weight of 50,000 to 20,000,000 g/mol and contains a) 3 to 96 mole % of a structural group of formula IX wherein R1 is hydrogen or methyl; R2, R3 and R4 are independently hydrogen, an aliphatic hydrocarbon residue with 1 to 6 C atoms, a phenyl residue optionally substituted with methyl groups;V is NH or oxygen;M is hydrogen, a monovalent or divalent metal cation, ammonium or an organic amine residue;n is from 1 to 5;a is ½ or 1;b) 3 to 96 mole % structural groups of structural formula X wherein W is —CO(O)—(CH2)x— or —CO—NR2—(CH2)x—; x is from 1 to 6R5 and R6 are independently hydrogen, an optionally substituted aliphatic hydrocarbon residue with 1 to 20 C atoms, a cycloaliphatic hydrocarbon residue with 5 to 8 C atoms or an aryl residue with 6 to 14 C atoms; andR1 is as defined above; orc) 0.05 to 75 mole % of a structural group of formula XI wherein Y is O, NH or NR5V is —(CH2)x—, R7 is R5 or X is halogen, C1 to C4 alkylsulfate or C1 to C4 alkylsulfonate; andR1, R5, R6, M, a and x are defined above. 6. The additive according to claim 1, wherein the sulfo group-containing copolymer is a water-soluble sulfo group-containing copolymer comprising at least one of a) 3 to 96 mole % of formula XII wherein R1is hydrogen or methyl;R2, R3 and R4 are independently selected from hydrogen, an aliphatic hydrocarbon residue with 1 to 6 C atoms, a phenyl residue optionally substituted with a methyl group;M is hydrogen, a monovalent cation, a divalent metal cation, ammonium or an organic amine residue; anda is ½ or 1;b) 3 to 96 mole % of formula XIII whereinR1 is as defined above; and R5 and R6 are independently of one another hydrogen, an aliphatic hydrocarbon residue with 1 to 20 C atoms, a cycloaliphatic hydrocarbon residue with 5 to 8 C atoms or an aryl residue with 6 to 14 C atoms;c) 0.001 to 10 mole % of a structural group of formula XIV whereinY is —COO(CnH2nO)p—R7, —(CH2)q—O(CnH2nO)p—R7;R7 is  , or or an unsaturated, saturated, linear or branched aliphatic alkyl residue with 10 to 40 C atoms;R8 is H, C1 to C6 alkyl, an arylalkyl group with a C1 to C12 alkyl group or C6 to C14 aryl residue;n is from 2 to 4;p is from 0 to 200;q is from 0 to 20x is from 0 to 3 andand R1 is as defined above; andd) 0.1 to 30 mole % of a structural group of formula (XV) whereinZ is —(CH2)q—O(CnH2nO)p—R9;R9 is H, C1 to C4 alkyl; andR1, n, p and q are as defined above. 7. The additive according to claim 6, wherein the copolymers consisting of structural groups a), b), c) and d) as well as a), b) or d) in addition contain up to 50 mole % based on the sum of the structural groups a), b), d) or c) of another structural group e) based on formula (XVI) wherein W is —CO—O—(CH2)m— or —CO—NR2—(CH2)m—;M is from 1 to 6; andR1, R2, R5 and R6 are as defined above. 8. The additive according to claim 1, wherein the polyacrylamide has non-ionic, anionic, cationic or amphoteric properties. 9. The additive according to claim 1, wherein component A) is partially cross-linked. 10. The additive according to claim 1, wherein component A) has an average particle size range of≦500 μm. 11. The additive according to claim 1, wherein the additive has an average particle size range of ≦2000 μm. 12. A method for causing a time-delayed action in a composition comprising the step of adding the additive of claim 1 to the composition. 13. A paint comprising a paint and the additive of claim 1. 14. A method for time-controlling at least one of the increase in viscosity or development of rheology in filled aqueous systems comprising the step of adding the additive of claim 1 to the filled aqueous system. 15. The method of claim 14, further comprising the step of adding cellulose ethers or cellulose ether substitute to the filled aqueous system. 16. The method according to claim 15, wherein the cellulose ether substitutes are selected from the group consisting of an oligosaccharide, a polysaccharide, sulfo group-containing copolymers, copolymers based on acrylamide, a hydrocolloid-forming substance and a hydrogel-forming substance. 17. The method according to claim 14, wherein the filled aqueous systems are building material systems comprising an inorganic binder. 18. The method according to claim 17, wherein the building material systems are tile adhesives, plasters, setting compounds, joint fillers, wall mortars, repair mortars and jointing mortars. 19. The method according to claim 17, wherein the building material systems are suitable for mechanical stirring or mechanical application. 20. The additive according to claim 1, wherein the water-swellable or water-absorbable compound is a starch ether, welan gum, divtan guar, xanthan, chitosan or guar. 21. The additive according to claim 8, wherein the polyacrylamide is at least one of a homopolymer or copolymer of acrylamide having a monomer selected from acrylic acid, acrylamidopropanesulfonic acid, quarternated dimethylaminopropyl acrylamide or quartenated dimethylaminoethyl acrylate. 22. The additive according to claim 1, wherein the oligosaccharide or polysaccharide is selected from the group consisting of starch ethers, welan gum, diutan gum, xanthan, chitosan and guar derivatives. 23. The method according to claim 17 , wherein the inorganic binder is a mineral binder. 24. The method according to claim 23, wherein the mineral binder is based on calcium sulfate. 25. The method according to claim 23, wherein the mineral binder is cement, gypsum, brine or anhydrite. 26. The method according to claim 19, wherein the dry mortar is a plaster or a tile adhesive. 27. The additive according to claim 1, wherein said cross-link is reversible.