초록 ▼

A coated abrasive product includes a particulate material containing green, unfired abrasive aggregates having a generally spheroidal or toroidal shape, the aggregates formed from a composition comprising abrasive grit particles, a nanoparticle binder, a dual function material, and a cross-linking a

A coated abrasive product includes a particulate material containing green, unfired abrasive aggregates having a generally spheroidal or toroidal shape, the aggregates formed from a composition comprising abrasive grit particles, a nanoparticle binder, a dual function material, and a cross-linking agent. These green unfired abrasive aggregates can also be used in free abrasive products and bonded abrasive products.

대표청구항 ▼

1. An aggregate forming mixture comprising: an aqueous slurry comprisingabout 0.1 to about 50% by wt. of a plurality of microparticle abrasive grains;about 0.1 to about 80% by wt. of a nanoparticle binder;about 0.5 to about 40% by wt. of a dual function material; andabout 0.5 to about 15% by wt. of

1. An aggregate forming mixture comprising: an aqueous slurry comprisingabout 0.1 to about 50% by wt. of a plurality of microparticle abrasive grains;about 0.1 to about 80% by wt. of a nanoparticle binder;about 0.5 to about 40% by wt. of a dual function material; andabout 0.5 to about 15% by wt. of a cross-linking agent. 2. The aggregate forming mixture of claim 1 wherein the dual function material is a metallic salt of a fatty acid. 3. The aggregate forming mixture of claim 2 wherein the metal of the metallic acid salt is selected from the group consisting of sodium, aluminum, calcium, magnesium, lead, zinc, or combinations thereof. 4. The aggregate forming mixture of claim 2 wherein the fatty acid is selected from the group consisting of lauric, myristic, palmitic, stearic, oleic, linoleic, or combinations thereof. 5. The aggregate forming mixture of claim 2 wherein the dual function material is zinc stearate. 6. The aggregate forming mixture of claim 1 wherein the cross-linking agent is a selected from the group consisting of starches, sugars, cellulose, glucose, fructose, maltose, amylopectin, amylose, cellulose or combinations thereof. 7. The aggregate forming mixture of claim 1 wherein the cross-linking agent is a selected from the group consisting of dextrin, polydextrin, cyclodextrin, malto-dextrin, or combinations thereof. 8. An aggregate comprising: about 0.1 to about 85% by wt. of a plurality of abrasive microparticles;about 1 to about 90% by wt. of a nanoparticle binder;about 0.5 to about 20% by wt. of a dual function material; andabout 0.5 to about 15% by wt. of a cross-linking agent. 9. The aggregate of claim 8 wherein the aggregate has a generally spheroidal or toroidal shape. 10. The aggregate of claim 8 wherein the aggregate is green and unfired. 11. The aggregate of claim 8 wherein the aggregate has a size not less than 10 microns and not more than 80 microns. 12. The aggregate of claim 8 wherein the dual function material is zinc stearate and the cross-linking agent is dextrin. 13. A coated abrasive product, comprising: a substrate; andparticulate material bonded to the substrate, the particulate material comprising green, unfired abrasive aggregates having a generally spheroidal or toroidal shape, the aggregates formed from a composite composition comprising abrasive grit particles having an average particle size between about 0.1 microns and about 50 microns contained within a nanoparticle binder, wherein the nanoparticle binder comprises particles having an average particles size of less than about 100 nm, a dual function material, and a cross-linking agent. 14. The coated abrasive product of claim 13, wherein the nanoparticle binder forms a continuous matrix phase in which the abrasive grit particles are uniformly distributed. 15. The coated abrasive product of claim 13, wherein the aggregates having said spheroidal shape are hollow. 16. The coated abrasive product of claim 13, wherein the nanoparticle binder has an average particle size of less than 80 nanometers. 17. A method for forming abrasive particulate material, comprising: forming a slurry comprising a liquid carrier, abrasive grit particles, a nanoparticle binder, a dual function material, and a cross-linking agent; andspray drying the slurry to form green, unfired composite aggregates comprising the abrasive grit particles contained within the nanoparticle binder, the dual function material, and the cross-linking agent, wherein the nanoparticle binder constitutes between about 15% to about 60% of the aggregate on a dry weight basis; andclassifying the aggregates for use in an abrasive product. 18. An aggregate comprising: a plurality of abrasive microparticles;a nanoparticle binder;a dual function material; anda cross-linking agent,wherein the aggregate has a generally spheroidal or toroidal shape. 19. An aggregate comprising: a plurality of abrasive microparticles;a nanoparticle binder;a dual function material; anda cross-linking agent,wherein the aggregate has a size not less than 10 microns and not more than 80 microns.