초록 ▼

A method for sealing the curved vacuum glass comprises: first preparing metallized layer bonded with the glass plate on the edge surface of the curved glass to be sealed by locally heating the metal slurry coating; then air-tightly sealing the edges of two glass plates by using the metal brazing tec

A method for sealing the curved vacuum glass comprises: first preparing metallized layer bonded with the glass plate on the edge surface of the curved glass to be sealed by locally heating the metal slurry coating; then air-tightly sealing the edges of two glass plates by using the metal brazing technology, or air-tightly sealing the edges of two glass plates by air-tightly welding the metal sealing sheet between the metallized layers of two glass plates to be sealed. A curved vacuum glass is also provided. The method makes the sealing part have firm connection, good air tightness and good thermal shock resistance. The sealing structure made of the metal sealing sheet is well compatible with the temperature deformation caused by the temperature difference between the internal and external glass plates of the vacuum glass.

대표청구항 ▼

1. A method for sealing curved vacuum glass, comprising the following steps: 1) preparing metal paste coatings on surfaces to be sealed on edges of two curved glass plates;2) locally heating the positions of the metal paste coatings to sinter the metal paste coatings into two metallized layers bonde

1. A method for sealing curved vacuum glass, comprising the following steps: 1) preparing metal paste coatings on surfaces to be sealed on edges of two curved glass plates;2) locally heating the positions of the metal paste coatings to sinter the metal paste coatings into two metallized layers bonded with the edges of the two curved glass plates, respectively; and3) directly air-tightly joining the mutually corresponding two metallized layers on the two curved glass plates to be sealed by brazing two metal sheets with the two metallized layers on the edges of the two curved glass plates, respectively;wherein one of the two metal sheets is positioned between the two curved glass plates and is brazed onto one of the two metallized layers sintered on an inner surface of one of the two curved glass plates and the other of the two metal sheets is positioned onto an outer surface of the other of the two curved glass plates and is brazed onto the other of the two metallized layers sintered on the outer surface of the other of the two curved glass plates; andwherein edges of the two metal sheets protruding from the edges of the two curved glass plates are joined to the by a metal brazing process or an ultrasonic welding process. 2. The method according to claim 1, wherein the metal paste coatings are prepared on the surfaces of the two glass plates via dip coating, spray coating, screen printing, manual coating or mechanical coating. 3. The method according to claim 1, wherein the local heating manner in the step 2) is laser heating, flame heating, current heating, induction heating or microwave heating. 4. The method according to claim 1, wherein the two metal sheets comprise a solder metal and when the step 3) is performed, a solder metal foil is placed on the corresponding metallized layers on the two curved glass plates, or the solder metal is pre-plated on the surface of at least one of the metallized layers, and subsequent welding-joining is completed by the metal brazing process or the ultrasonic welding process. 5. The method according to claim 4, wherein the solder metal foil and the solder metal are made of tin alloy solder. 6. The method according to claim 1, wherein the metal brazing process is performed under the protection of an inert gas, or in an environment of H2 gas or N2 gas, or in a vacuum environment. 7. The method according to claim 1, wherein the brazing temperature of the metal brazing process is less than or equal to 350° C. 8. A method for sealing curved vacuum glass, wherein the method comprises the following steps: 1) preparing metal paste coatings on surfaces to be sealed on edges of two curved glass plates;2) locally heating the positions of the metal paste coatings to sinter the metal paste coatings into two metallized layers bonded with the two curved glass plates, respectively; and3) joining a metal sealing sheet between the metallized layers of the two curved glass plates to be sealed to realize air-tight sealing of the edges of the two curved glass plates;wherein the metal sealing sheet comprises a U-shaped metal sheet, and two sides of the U-shaped metal sheet are respectively air-tightly joined with the two metallized layers on the two curved glass plates to be sealed to realize air-tight sealing of the edges of the two curved glass plates;wherein one side of the U-shaped metal sheet is positioned between the two curved glass plates to be scaled and air-tightly joined with the metallized layer on an inner surface of one curved glass plate by a metal brazing process or an ultrasonic welding process, and the other side of the U-shaped metal sheet goes around an edge of the other curved glass plate and then is air-tightly joined with the metallized layer on an outer surface of the other curved glass plate by the metal brazing process or the ultrasonic welding process.