초록 ▼

A cell-support matrix having narrowly defined uniformly vertically and non-randomly organized porosity and pore density and a method for preparation thereof. The matrix suitable for preparation of cellular or acellular implants for growth and de novo formation of an articular hyaline-like cartilage.

A cell-support matrix having narrowly defined uniformly vertically and non-randomly organized porosity and pore density and a method for preparation thereof. The matrix suitable for preparation of cellular or acellular implants for growth and de novo formation of an articular hyaline-like cartilage. A gel-matrix composite system comprising collagen-based matrix having a narrowly defined porosity capable of inducing hyaline-like cartilage production from chondrocytes in vivo and in vitro.

대표청구항 ▼

1. A cell-supporting matrix having a substantially vertically organized porosity, said matrix comprising: (i) a substantially homogeneous vertical pore orientation, wherein at least 85% of the pores in the matrix are pores oriented in a vertically-organized arrangement;(ii) a basal surface having po

1. A cell-supporting matrix having a substantially vertically organized porosity, said matrix comprising: (i) a substantially homogeneous vertical pore orientation, wherein at least 85% of the pores in the matrix are pores oriented in a vertically-organized arrangement;(ii) a basal surface having pores; and(iii) an apical surface having pores,wherein at least 85% of said pores at the basal surface and at least 85% of said pores at the apical surface have a diameter of 200±100 micrometers; andwherein said surfaces have a pore density of 25±10 pores per mm2; andwherein the matrix is prepared by precipitating a collagenous or collagen peptide containing biocompatible polymeric material. 2. The matrix of claim 1 wherein at least 95% of said basal and apical pores have diameters of 200±100 micrometers. 3. The matrix of claim 1 wherein at least 98% of said basal and apical pores have diameters of 200±100 micrometers. 4. The matrix of claim 1 wherein at least 85% of said basal pores and at least 85% of said apical pores are 200±50 micrometers in diameter. 5. The matrix of claim 1 wherein the collagenous or collagen peptide containing biocompatible polymeric material is selected from the group consisting of Type I collagen, Type II collagen, Type IV collagen, collagen containing proteoglycan, collagen containing glycosaminoglycan, collagen containing glycoprotein, alpha 1 Type I collagen peptide, alpha 2 Type I collagen peptide, and a combination thereof. 6. The matrix of claim 5 wherein said polymeric material is Type I collagen. 7. The matrix of claim 1 prepared by polymerizing a solution of Type I collagen comprising from 4 mg to 8 mg of Type I collagen per milliliter of solution. 8. The matrix of claim 7 wherein said solution comprises from 4 mg to 6 mg of Type I collagen per milliliter of solution. 9. The matrix of claim 8 wherein said solution comprises a non-ionic surfactant, and said Type I collagen is polymerized in the presence of a 3% aqueous ammonia solution. 10. The matrix of claim 9 wherein said solution comprises about 0.3% by weight of polyoxyethylenepolyoxypropylene block co-polymer surfactant. 11. The matrix of claim 9 wherein said Type I collagen is polymerized at a pressure between 3 torr and 10 torr. 12. The matrix of claim 9 wherein said Type I collagen is polymerized in an inert atmosphere. 13. The matrix of claim 12 wherein said Type I collagen is polymerized in nitrogen or argon atmosphere. 14. The matrix of claim 9 prepared by polymerizing said solution comprising 4 mg of Type I collagen per milliliter of solution, wherein said surfactant is polyoxyethylene-polyoxypropylene block co-polymer surfactant, in the presence of about 3% aqueous ammonia at a pressure of 3 torr of nitrogen. 15. A cell-supporting matrix prepared by a process comprising: polymerizing a solution of Type I collagen comprising from 4 mg to 8 mg of Type I collagen per milliliter of solution in the presence of about 3% aqueous ammonia, at a pressure between 3 torr and 10 torr of an inert atmosphere;wherein said collagen solution comprises a non-ionic polyoxyethylene-polyoxypropylene block co-polymer surfactant at a concentration of about 0.3%, by weight,wherein said matrix has a substantially homogeneous vertical pore orientation, and at least 85% of the pores in the matrix are oriented in a vertically-organized arrangement;wherein at least 85% of said pores at a basal surface of said matrix and at least 85% of pores at an apical surface of said matrix are 200±100 micrometers in diameter; andwherein said surfaces have a pore density of 25±10 pores per mm2. 16. The matrix of claim 15 wherein said pores are 200±50 micrometers in diameter. 17. The matrix of claim 15 wherein said inert atmosphere comprises nitrogen or argon. 18. The matrix of claim 15 wherein said solution comprising 4 mg of Type I collagen per milliliter of solution is polymerized under a nitrogen atmosphere at a pressure of 3 torr.