Powder metal scrolls and sinter-brazing methods for making the same
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B23K-001/19
C22C-033/02
B22F-007/06
F04C-018/02
B22F-005/00
출원번호
US-0720853
(2010-03-10)
등록번호
US-8955220
(2015-02-17)
발명자
/ 주소
Scancarello, Marc J.
Ruxanda, Roxana E. L.
출원인 / 주소
Emerson Climate Technologies, Inc.
대리인 / 주소
Harness, Dickey & Pierce, P.L.C.
인용정보
피인용 횟수 :
0인용 특허 :
52
초록▼
Methods of forming scroll compressor components are provided. The methods include forming at least one component of a scroll member from a powder metallurgy technique and joining the component with another distinct component via a sinter-brazing process. For example, a baseplate having a spiral scro
Methods of forming scroll compressor components are provided. The methods include forming at least one component of a scroll member from a powder metallurgy technique and joining the component with another distinct component via a sinter-brazing process. For example, a baseplate having a spiral scroll involute is joined to a hub via a joint interface having brazing material to form a braze joint with superior quality. At least one component is formed from a powder metal material including carbon and at least one species that reacts with or binds carbon to prevent migration during brazing of the sinter-brazing heat process. Optionally, during the powder metallurgy process, an alloy with a lower concentration of carbon is selected, which may be incorporated into a crystal structure with the species that prevents carbon migration.
대표청구항▼
1. A method of forming a scroll member comprising: heating a first scroll component comprising a powder metal material comprising an iron alloy in a furnace having a temperature of greater than or equal to about 1,900° F. (1,037° C.) for at least partial sintering during a first heating process, whe
1. A method of forming a scroll member comprising: heating a first scroll component comprising a powder metal material comprising an iron alloy in a furnace having a temperature of greater than or equal to about 1,900° F. (1,037° C.) for at least partial sintering during a first heating process, wherein said first scroll component is a hub and said iron alloy comprises carbon at greater than or equal to about 0.4% to less than or equal to about 0.6% by weight;cooling said first scroll component, wherein after said first heating process and said cooling said iron alloy has greater than or equal to about 95% by weight of a total amount of carbon remaining in said iron alloy in a form bound to and/or reacted with at least one species in said iron alloy that minimizes carbon migration;disposing a brazing material in a joint interface region formed between a portion of said first scroll component and a portion of a second scroll component comprising a baseplate and an involute, wherein said second scroll component comprises a second distinct iron alloy comprising carbon at greater than or equal to about 0.7% to less than or equal to about 0.9% by weight; andheating to sinter-braze said first and second scroll components having said brazing material therebetween in a furnace having a temperature of greater than or equal to about 1,900° F. (1,037° C.) in a second heating process to form the scroll member having a braze joint coupling said portion of said first scroll component to said portion of said second scroll component. 2. The method of claim 1, wherein prior to said first heating process, said first scroll component is processed to a green form by compressing said powder metal material to a void fraction of less than or equal to about 18% by volume of a total volume of the first scroll component. 3. The method of claim 1, wherein said at least one species that minimizes carbon migration in said iron alloy during said second heating process is selected from the group consisting of: iron, copper, vanadium, chromium, molybdenum, and combinations thereof. 4. The method of claim 3, wherein said first heating process and said cooling is controlled so as to form one or more crystal structures in said iron alloy that incorporate greater than or equal to about 95% by weight of said carbon. 5. The method of claim 4, wherein at least one of said species that minimizes carbon migration comprises iron and one or more of said crystal structures includes a pearlite phase, wherein said first heating process is conducted until greater than or equal to about 99% by weight of said carbon is incorporated into said pearlite phase in said first scroll component. 6. The method of claim 1, wherein said first scroll component comprises said iron alloy having greater than or equal to about 95% by weight of total carbon remaining in said iron alloy in a form bound to and/or reacted with at least one of said species in said iron alloy to minimize carbon migration, wherein said first scroll component is formed by a metallurgy process selected from the group consisting of: forging, extruding, wrought, casting, and equivalents thereof. 7. The method of claim 1, wherein said brazing material comprises an element selected from a group consisting of: copper, nickel, boron, manganese, silicon, iron, and combinations thereof. 8. The method of claim 1, wherein said first scroll component and said second scroll component are each formed from powder metal material and each are at least partially sintered via said first heating process prior to said disposing and heating to sinter-braze. 9. The method of claim 1, wherein a portion of said hub and a portion of said baseplate are joined after said heating to sinter-braze at said joint interface region to form said braze joint. 10. A method of forming a scroll member comprising: heating a first scroll component comprising a powder metal material comprising an iron alloy for partial sintering during a first heating process, wherein said first scroll component is a hub and said iron alloy comprises carbon at greater than or equal to about 0.4% to less than or equal to about 0.6% by weight;cooling said first scroll component, wherein after the first heating process and said cooling said iron alloy has greater than or equal to about 95% by weight of a total amount of carbon present in said iron alloy in a form bound to and/or reacted with at least one species in said iron alloy that minimizes carbon migration;disposing a brazing material between a portion of said first scroll component and a second scroll component comprising a baseplate and an involute, wherein said second scroll component comprises a second distinct iron alloy comprising carbon at greater than or equal to about 0.7% to less than or equal to about 0.9% by weight; andheating to sinter-braze said first and second scroll components having said brazing material therebetween via a second heating process in a furnace having a temperature of greater than or equal to about 1,900° F. (1,037° C.) to form the scroll member having a braze joint coupling a portion of said first scroll component to a portion of said second scroll component. 11. The method of claim 10, wherein prior to said first heating process, said first scroll component is processed to a green form by compressing said powder metal material to a void fraction of less than or equal to about 18% by volume of a total volume of the first scroll component. 12. The method of claim 10, wherein after said first heating process and said cooling, said first scroll component has greater than or equal to about 97% by weight of total carbon present in said form bound to and/or reacted with said at least one species that minimizes carbon migration during said second heating process. 13. The method of claim 12, wherein after said first heating process and said cooling, said first scroll component has greater than or equal to about 99% by weight of total carbon present in said form bound to and/or reacted with said at least one species that minimizes carbon migration during said second heating process. 14. The method of claim 12, wherein said at least one species that minimizes carbon migration in said powder metal material during said second heating process is selected from the group consisting of: iron, copper, vanadium, chromium, molybdenum, and combinations thereof. 15. The method of claim 12, wherein during said first heating process at least a portion of said powder metal material forms a pearlite phase, and said first heating process is conducted until greater than or equal to about 99% of said carbon is incorporated into said pearlite phase in said first scroll component. 16. The method of claim 10, wherein said first scroll component and said second scroll component are both formed from powder metal material and both of said first and second scroll components are partially sintered via first heating processes prior to said second heating process to sinter-braze. 17. The method of claim 10, wherein said brazing material comprises an element selected from a group consisting of: copper, nickel, boron, manganese, silicon, iron, and combinations thereof. 18. The method of claim 10, wherein said second scroll component is formed by a metallurgical process selected from the group consisting of: forging, extruding, working (wrought), casting, and combinations thereof. 19. The method of claim 1, wherein said first heating process and said second heating process are conducted for a combined duration of about 3 or more hours. 20. A method of forming a scroll member comprising: heating a hub scroll component comprising a powder metal material comprising an iron alloy comprising carbon at greater than or equal to about 0.4 to less than or equal to about 0.6% by weight in a furnace having a temperature of greater than or equal to about 1,900° F. (1,037° C.) for at least partial sintering during a first heating process;cooling said hub scroll component, wherein after said first heating process and said cooling said iron alloy has greater than or equal to about 99% by weight of a total amount of carbon remaining in said iron alloy in a form bound to and/or reacted with at least one species in said iron alloy that minimizes carbon migration;disposing a brazing material in a joint interface region formed between a portion of said hub scroll component and a portion of a second scroll component defining a baseplate and an involute, wherein said second scroll component comprises a second distinct iron alloy comprising carbon at greater than or equal to about 0.7 to less than or equal to about 0.9% by weight; andheating to sinter-braze said hub scroll component and said second scroll component having said brazing material therebetween in a furnace having a temperature of greater than or equal to about 1,900° F. (1,037° C.) in a second heating process to form the scroll member having a braze joint coupling said portion of said hub scroll component to said portion of said second scroll component.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (52)
Utter Robert E. ; Haller David K., Bearing lubrication system for a scroll compressor.
Krause Robert F. (Valparaiso IN) Bularzik Joseph H. (Munster IN) Kokal Harold R. (Glenwood IL), High density metal components manufactured by powder metallurgy.
Purnell Charles G. (Coventry GBX) Mahmoud Mohammad S. (London GBX) Brownlie Helen A. (Coventry GBX), Method of sintering machinable ferrous-based materials.
Caillat Jean-Luc (Dayton OH) Elson John P. (Sidney OH) Anderson Gary J. (Sidney OH) Monnier Kenneth J. (Sidney OH) Fogt James F. (Sidney OH), Non-orbiting scroll mounting arrangements for a scroll machine.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.