초록

A bow wave in a composite laminate generated during part consolidation is reduced by transmitting atmospheric pressure loads to a region of the part having low compaction pressure due to bridging of a vacuum bag at an edge of the part.

대표청구항 ▼

1. A method of reducing bow wave formation in a composite laminate part during consolidation, comprising: forming a composite laminate part comprising a first component bonded to a second component, wherein forming further comprises: placing the composite laminate part in a vacuum bag; andevacuating

1. A method of reducing bow wave formation in a composite laminate part during consolidation, comprising: forming a composite laminate part comprising a first component bonded to a second component, wherein forming further comprises: placing the composite laminate part in a vacuum bag; andevacuating the vacuum bag, which creates a first compaction pressure around a majority of the composite laminate part and a second compaction pressure, lower than the first compaction pressure, applied to the remainder of the composite laminate part and being located at a region at a base of a co-bonded composite structure where the vacuum bag stretches over an area of the composite laminate part rather than pressing against the composite laminate part during evacuation; andimmediately after forming the composite laminate part, transmitting atmospheric pressure loads to the region at the base of the co-bonded composite structure where the vacuum bag stretches over an area of the composite laminate rather than pressing against it. 2. The method of claim 1, wherein the region at the base of the co-bonded composite structure is located at an edge of a radius in the composite laminate part, and transmitting atmospheric pressure loads includes applying the transmitted pressure loads at the edge of the radius. 3. The method of claim 1, wherein transmitting atmospheric pressure loads includes placing a caul on the composite laminate part at the region at the base of the co-bonded composite structure. 4. A method of reducing a bow wave produced in a region at the base of a co-bonded composite structure having a first uncured composite part during consolidation in a vacuum bag with a second composite part, comprising: placing a caul device over the first uncured composite part and the second composite part covering the region at the base of a co-bonded composite structure; andusing the caul device to apply atmospheric pressure loads to the region at the base of a co-bonded composite structure having the first uncured composite part. 5. The method of claim 4, wherein the region at the base of a co-bonded composite structure is along an edge of a radius on the first uncured composite part, and placing the caul device includes: placing a first caul over the radius and the edge of the radius on the first uncured composite part, andplacing a second caul on the second composite part overlapping the first caul. 6. The method of claim 5, wherein using the caul device to apply atmospheric pressure loads includes using the second caul to apply pressure to the first caul in the region at the base of a co-bonded composite structure. 7. A method of fabricating a composite structure assembly including a laminate spar joined to a stiffener having a flange, comprising: forming and precuring the stiffener to create a precured stiffener;laying up the laminate spar on a mandrel having a second radius;assembling the precured stiffener with the laminate spar, including placing a layer of adhesive between the flange of the stiffer and a web of the spar;installing a caul device on the composite structure assembly, including molding a first portion of the caul device to an end of the stiffener overlying the flange of the stiffener, and molding a second portion, having an extremity overlying the first portion, to conform to a third radius formed in the spar;vacuum bagging the composite structure assembly;placing the composite structure assembly in an autoclave; andusing autoclave pressure to consolidate the composite structure assembly, including using the caul device to transmit pressure from the flange to an edge of the third radius formed in the spar. 8. The method of claim 2, wherein transmitting atmospheric pressure loads includes placing a caul on the composite laminate part at the region at the base of the co-bonded composite structure. 9. The method of claim 1, wherein applying the second compaction pressure further includes: placing a vacuum bag over the fiber reinforced, laminate part; placing the fiber reinforced laminate part covered by the vacuum bag in an autoclave; drawing a vacuum in the vacuum bag; and applying pressure to the vacuum bag using the autoclave.