Hydroprocessing catalysts and methods for making thereof
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B01J-027/04
B01J-027/043
B01J-027/045
B01J-037/00
B01J-037/04
B01J-031/00
B01J-027/02
B01J-027/24
B01J-023/00
B01J-023/40
B01J-023/42
B01J-023/44
B01J-023/58
B01J-023/883
B01J-023/24
B01J-023/85
B01J-023/887
B01J-027/051
B01J-035/00
B01J-037/20
C10G-049/04
C10G-049/06
C10G-049/12
B01J-035/10
출원번호
US-0331690
(2011-12-20)
등록번호
US-9040447
(2015-05-26)
발명자
/ 주소
Mironov, Oleg
Kuperman, Alexander E.
출원인 / 주소
Chevron U.S.A. Inc.
인용정보
피인용 횟수 :
0인용 특허 :
80
초록▼
A process for making an improved slurry catalyst for the upgrade of heavy oil feedstock is provided. In the process, a metal precursor solution comprising at least a water-soluble molybdenum compound and a water-soluble metal zinc compound is mixed under high shear mixing conditions to generate an e
A process for making an improved slurry catalyst for the upgrade of heavy oil feedstock is provided. In the process, a metal precursor solution comprising at least a water-soluble molybdenum compound and a water-soluble metal zinc compound is mixed under high shear mixing conditions to generate an emulsion. The emulsion is subsequently sulfided with a sulfiding agent ex-situ, or in-situ in a heavy oil feedstock to form the slurry catalyst. The in-situ sulfidation in heavy oil is under sufficient condition for the heavy oil feedstock to generate the sulfiding source needed for the sulfidation.
대표청구항▼
1. A process for preparing a slurry catalyst for use in upgrading a heavy oil feedstock, comprising: providing a metal precursor solution comprising at least a water-soluble molybdenum compound and a water-soluble metal zinc compound in water;mixing the metal precursor solution with a hydrocarbon di
1. A process for preparing a slurry catalyst for use in upgrading a heavy oil feedstock, comprising: providing a metal precursor solution comprising at least a water-soluble molybdenum compound and a water-soluble metal zinc compound in water;mixing the metal precursor solution with a hydrocarbon diluent under sufficiently high shear mixing to generate an emulsion with droplet sizes ranging from 0.1 to 300 μm;sulfiding the emulsion with at least a sulfiding agent to form a slurry catalyst having a particle size ranging from 1 to 300 μm;wherein the emulsion is subjected to reduction at a temperature above ambient either before or after the sulfiding step; andwherein the zinc compound is present in the slurry catalyst in a sufficient amount for a zinc to molybdenum weight ratio ranging from 1:10 to 10:1. 2. The process of claim 1, wherein the emulsion is mixed with the heavy oil feedstock in a reactor under in-situ sulfiding condition for the heavy oil feedstock to provide the sulfiding agent needed for to sulfide the emulsion forming the slurry catalyst. 3. The process of claim 2, wherein the in-situ sulfiding condition is at a temperature from 752° F. to 1112° F. and a pressure from 1435 psig (10 MPa) to 3610 psig (25MPa). 4. The process of claim 1, where the sulfidation of the emulsion forming the slurry catalyst occurs ex-situ prior to the heavy oil upgrade. 5. The process of claim 4, wherein the sulfiding agent is selected from the group of elemental sulfur, hydrogen sulfide, ammonium sulfide, ammonium polysulfide ([(NH4)2Sx), ammonium thiosulfate ((NH4)2S203), sodium thiosulfate Na2S203), thiourea CSN2H4, carbon disulfide, dimethyl disulfide (DMDS), dimethyl sulfide (DMS), tertiarybutyl polysulfide (PSTB) and tertiarynonyl polysulfide (PSTN), and mixtures thereof. 6. The process of claim 4, wherein the hydrocarbon diluent is selected from gasoline, diesel, vacuum gas oil, cycle oil, jet oil, fuel oil, heavy oil feedstock, and mixtures thereof. 7. The process of claim 4, wherein a sufficient amount of sulfiding agent is provided a molar ratio of sulfur to molybdenum of at least 1.5 to 1 to sulfide the emulsion to form the slurry catalyst. 8. The process of claim 1, wherein the hydrocarbon diluent comprises a mixture of heavy oil feedstock and at least one of a VGO, MCO, HCO, and mixtures thereof. 9. The process of claim 1, wherein the emulsion comprises droplets having a size of 0.5 to 200 μm. 10. The process of claim 1, wherein the emulsion comprises droplets having a size of less than 100 μm. 11. The process of claim 1, wherein providing a metal precursor solution comprising at least a water-soluble molybdenum compound and a water -soluble metal zinc compound in water comprises providing a solution having a concentration of molybdenum in solution of less than 10 wt. %. 12. The process of claim 1, wherein the metal precursor solution comprising at least a water-soluble molybdenum compound and a water-soluble metal zinc compound in water has a concentration of zinc in solution of less than 10 wt. %. 13. The process of claim 1, wherein the metal precursor solution comprising at least a water-soluble molybdenum compound and a water-soluble metal zinc compound in water has pH of at least 4. 14. The process of claim 1, wherein the slurry catalyst prepared therefrom has a total surface area of at least 100 m2/g. 15. The process of claim 1, wherein the slurry catalyst prepared therefrom has a has a total pore volume of at least 0.4 cc/g and a polymodal pore distribution with at least 70% of pore sizes in the range of 5 to 1,000 Angstroms in diameter. 16. A process for preparing a slurry catalyst for use in upgrading heavy oil feedstock, comprising: providing a metal precursor solution comprising at least a water-soluble molybenum salt selected from molybdates, alkali metal heptamolybdates, alkali metal orthomolybdates, alkali metal isomolybdates, phosphomolybdic acid, molybdenum oxide, molybdenum carbide, molybdenum nitride, aluminum molybdate, molybdic acid, and mixtures thereof, and a water -soluble zinc salt, at a zinc to molybdenum weight ratio ranging from 1:30 to 5:1;mixing the metal precursor solution with a hydrocarbon diluent under high shear mixing and under reducing conditions to generate an emulsion comprising droplets having a size of 0.1to 300 μm, the hydrocarbon diluent selected from gasoline, diesel, vacuum gas oil (VGO), cycle oil (MCO or HCO), jet oil, fuel oil, heavy oil feedstock, and mixtures thereof;mixing the emulsion with at least a heavy oil feedstock under in-situ sulfiding conditions for the heavy oil feedstock to provide at least a sulfiding agent to sulfide the emulsion forming a slurry catalyst. 17. The process of claim 16, wherein the emulsion is mixed with the heavy oil feedstock at a temperature from 752° F. to 1112° F. under a pressure from 1435 psig (10MPa) to 3610 psig (25 MPa) for in-situ sulfiding to take place. 18. The process of claim 16, wherein the slurry catalyst prepared therefrom has an average particle size ranging from 1 to 300 μm.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (80)
Goyal Shri K. (Naperville IL), Antifoam process for delayed coking.
Jain Anil K. (Oakville CAX) Pruden Barry B. (Oakville CAX) Lambiris Dennis (Repentigny CAX) Rivard Serge (Montreal CAX) Liu Dirkson D. S. (Ottawa CAX), Antifoam to achieve high conversion in hydroconversion of heavy oils.
Harle,Virginie; Martin,Catherine; Payen,Edmond; Lamonier,Carole; Blanchard,Pascal, Catalyst based on a group VI metal and a group VIII metal at least partially present in the form of heteropolyanions in the oxide precursor.
Duddy John E. ; Abrams Lawrence M. ; Hildebrandt Steven J., Catalytic multi-stage hydrodesulfurization of metals-containing petroleum residua with cascading of rejuvenated catalyst.
Van Driesen Roger P. (Titusville NJ) Adams William R. (Upper Montclair NJ) Caspers John (Basking Ridge NJ) Baldasarri Mario (Paramus NJ) Trimble Harold (Panama City Beach FL), Control of bed expansion in expanded bed reactor.
Harandi Mohsen N. (Langhorne PA) Herbst Joseph A. (Turnersville NJ) Owen Hartley (Belle Mead NJ) Schipper Paul H. (Doylestown PA) Thomson Robert T. (Lawrenceville NJ), Demetallation in FCC regenerator.
Galiasso Roberto (San Antonio de Los Altos VEX) Salazar Jose A. (Edo. Miranda VEX) Morales Alfredo (San Antonio de Los Altos VEX) Carrasquel Angel R. (Edo. Miranda VEX), Hydroconversion of heavy crudes with high metal and asphaltene content in the presence of soluble metallic compounds and.
Sears Paul L. (Dunrobin CAX) de Bruijn Theo J. W. (Constance Bay CAX) Dawson William H. (Edmonton CAX) Pruden Barry B. (Calgary CAX) Jain Anil K. (Calgary CAX), Hydrocracking of heavy hydrocarbon oils with heavy hydrocarbon recycle.
Danot Michel,FRX ; Allali Nabil,MAX ; Gaborit Valerie,FRX ; Geantet Christophe,FRX ; Afanassiev Pavel,FRX ; Mignard Samuel,FRX ; Kasztelan Slavik,FRX, Hydrodefining and hydrocracking catalyst comprising a mixed sulphide comprising sulphur, at least one group VB element and at least one group VIB element.
Wallace Paul S. ; Johnson Kay A. ; Thacker Pradeep S. ; Kasbaum Janice L. ; Barkley R. Walter ; Niccum Jacquelyn Gayle, Integration of solvent deasphalting and gasification.
Seamans James D. (1 Cormac Ct. Reisterstown MD 21136) Welch James G. (107 Fireside Cir. Baltimore MD 21212) Gasser Neal G. (508 Windy Knoll Dr. Mt. Airy MD 21771), Method of presulfiding a hydrotreating catalyst.
Seamans James D. (Reisterstown MD) Welch James G. (Baltimore MD) Gasser Neal G. (Mt. Airy MD) Adams Charles T. (Houston TX), Method of presulfiding a hydrotreating, hydrocracking or tail gas treating catalyst.
Ginestra, Josiane Marie-Rose; Seamans, James Dallas; Lee, Kenneth Scott, Method of restoring catalytic activity to a spent hydrotreating catalyst, the resulting restored catalyst, and a method of hydroprocessing.
Happel John (Hastings-on-Hudson NY) Hnatow Miguel A. (Verona NJ) Bajars Laimonis (Princeton Junction NJ), Methods of making high activity transition metal catalysts.
Eijsbouts, Sonja; Oogjen, Bob Gerardus; Homan Free, Hermannus Willem; Cerfontain, Marinus Bruce; Riley, Kenneth Lloyd; Soled, Stuart Leon; Miseo, Sabato, Mixed metal catalyst, its preparation by co-precipitation, and its use.
Eijsbouts, Sonja; Oogjen, Bob Gerardus; Homan Free, Harmannus Willem; Cerfontain, Marinus Bruce; Riley, Kenneth Lloyd; Soled, Stuart Leon; Miseo, Sabato, Process for preparing a mixed metal catalyst composition.
Eijsbouts, Sonja; Oogjen, Bob Gerardus; Homan Free, Harmannus Willem; Cerfontain, Marinus Bruce; Riley, Kenneth Lloyd; Soled, Stuart Leon; Miseo, Sabato, Process for preparing a mixed metal catalyst composition.
Zhou Peizheng ; Lee Lap-Keung ; Zhou Jinglai,CNX ; Lu Yijun,CNX ; Li Guohui,CNX, Skeletal iron catalyst having improved attrition resistance and product selectivity in slurry-phase synthesis processes.
Reynolds, Bruce E.; Lam, Fred W.; Chabot, Julie; Antezana, Fernando J.; Bachtel, Robert; Gibson, Kirk R.; Threlkel, Richard; Leung, Pak C., Upflow reactor system with layered catalyst bed for hydrotreating heavy feedstocks.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.