초록 ▼

Brominated styrene-butadiene copolymers are useful gas transport films. The gas transport films are made by brominating a starting styrene-butadiene copolymer, and then forming the brominated styrene-butadiene copolymer into a film. The film may contain a blend of the brominated styrene-butadiene co

Brominated styrene-butadiene copolymers are useful gas transport films. The gas transport films are made by brominating a starting styrene-butadiene copolymer, and then forming the brominated styrene-butadiene copolymer into a film. The film may contain a blend of the brominated styrene-butadiene copolymer with one or more other polymers. The films have excellent selectivities between certain pairs of gasses, and exhibit high gas transport rates for various gasses such as carbon dioxide and water vapor.

대표청구항 ▼

1. A method for making a gas transport film comprising a brominated styrene-butadiene copolymer, comprising brominating a starting styrene-butadiene copolymer having styrene units and 60 to 90 mole-% butadiene units to brominate at least 70 mol-% of the butadiene units and no more than 10% of the ar

1. A method for making a gas transport film comprising a brominated styrene-butadiene copolymer, comprising brominating a starting styrene-butadiene copolymer having styrene units and 60 to 90 mole-% butadiene units to brominate at least 70 mol-% of the butadiene units and no more than 10% of the aromatic rings of the styrene units and then forming the brominated styrene-butadiene copolymer into a supported or free-standing film, the film having a thickness of 10 nanometers of 5 micrometers if supported or 0.025 to 0.5 mm if free-standing. 2. The method of claim 1 wherein the brominated styrene-butadiene copolymer is a block copolymer of styrene and butadiene having an apparent molecular weight, as measured by gel permeation chromatography against a polystyrene standard, of from 50,000 to 200,000. 3. The method of claim 2 wherein at least 85% of the butadiene units in the starting styrene-butadiene copolymer are 1,2-butadiene units. 4. The method of claim 1, wherein the brominated styrene-butadiene copolymer is made by brominating a solution of a starting styrene-butadiene copolymer with a quaternary ammonium tribromide or quaternary phosphonium tribromide. 5. A gas transport film made in accordance with the method of claim 1. 6. The gas transport film of claim 5 wherein the brominated styrene-butadiene copolymer is present in the film as a blend with at least one additional organic polymer. 7. The gas transport film of claim 6, wherein the blend contains an amount of the brominated styrene-butadiene copolymer to provide the blend with a bromine content from 0.1 to 25 percent by weight. 8. The gas transport film of claim 7 wherein the additional organic polymer is selected from LDPE, HDPE, LLDPE, substantially linear polyethylene; polystyrene, a styrene-acrylic acid copolymer; polyvinylidene chloride, or poly(ethylene terephthalate). 9. The gas transport film of claim 5, which has a water vapor permeability of at least 15 g·mil/m2·day at 37.8° C. and is impermeable to liquid water. 10. A polymer foam thermal insulation product having a gas transport film of claim 5 attached to at least one surface thereof. 11. A floor covering product having a facing layer and at least one layer of the gas transport film layer of claim 5 attached directly or indirectly to a reverse side of the facing layer. 12. A building construction comprising at least one wall or roof structure having a layer of the gas transport film of claim 5 applied to a major surface thereof. 13. A method for separating gases, comprising contacting a gaseous mixture containing at least one first gas and at least one second gas with a feed side of a membrane comprising the gas transport film of claim 5 and withdrawing a gas enriched in the first gas from a lower pressure downstream side of the membrane. 14. A method for separating an acid gas from a gaseous alkane or alkene, comprising contacting a gaseous mixture of at least one acid gas and at least one gaseous alkane or alkene with a feed side of a membrane comprising the gas transport film of claim 5, and withdrawing a gas enriched in the acid gas from a lower pressure downstream side of the membrane.