초록 ▼

A porous silicon based material comprising porous crystalline elemental silicon formed by reducing silicon dioxide with a reducing metal in a heating process followed by acid etching is used to construct negative electrode used in lithium ion batteries. Gradual temperature heating ramp(s) with optio

A porous silicon based material comprising porous crystalline elemental silicon formed by reducing silicon dioxide with a reducing metal in a heating process followed by acid etching is used to construct negative electrode used in lithium ion batteries. Gradual temperature heating ramp(s) with optional temperature steps can be used to perform the heating process. The porous silicon formed has a high surface area from about 10 m2/g to about 200 m2/g and is substantially free of carbon. The negative electrode formed can have a discharge specific capacity of at least 1800 mAh/g at rate of C/3 discharged from 1.5V to 0.005V against lithium with in some embodiments loading levels ranging from about 1.4 mg/cm2 to about 3.5 mg/cm2. In some embodiments, the porous silicon can be coated with a carbon coating or blended with carbon nanofibers or other conductive carbon material.

대표청구항 ▼

1. A porous silicon based material comprising particulate porous crystalline elemental silicon having an x-ray diffraction (XRD) spectra, using a Cu Kα a source, with a crystalline silicon peak at a value of 2θ of 28 to 30 degrees at least twice the peak intensity as a broad amorphous peak from 2θ o

1. A porous silicon based material comprising particulate porous crystalline elemental silicon having an x-ray diffraction (XRD) spectra, using a Cu Kα a source, with a crystalline silicon peak at a value of 2θ of 28 to 30 degrees at least twice the peak intensity as a broad amorphous peak from 2θ of 15 to 25 degrees, and an average pore sizes in the range of 5 nm to 500 nm in diameter, wherein the porous silicon is substantially free of carbon embedded within the silicon structure, reducing metal and reducing metal oxides. 2. The material of claim 1 further comprising a carbon coating on the porous silicon. 3. The material of claim 1 wherein the porous silicon has a surface area from about 10 m2/g to about 200 m2/g. 4. The material of claim 1 having an average pore size from about 15 nm to about 200 nm. 5. The material of claim 1 having an x-ray diffraction (XRD) spectrum with a crystalline silicon peak at a value of 2θ of 28 to 30 degrees at least four times the greatest intensity from amorphous phase scattering from 2θ of 15 to 25 degrees. 6. The material of claim 1 having an x-ray diffraction spectrum with a broad monotonically decreasing amorphous scattering from 2θ of 10 to 25 degrees. 7. A lithium based battery electrode comprising a binder and the porous silicon based material of claim 1, wherein the electrode has a discharge specific capacity of at least 1800 mAh/g at the 7th cycle at rate of C/3 discharged from 1.5V to 0.005V against lithium. 8. The electrode of claim 7 wherein the electrode has an irreversible capacity loss from about 25% to about 15%. 9. The electrode of claim 7 wherein the electrode retains at least 80% of capacity up to 50 charge/discharge cycles. 10. The electrode of claim 7 wherein the binder comprises a polyimide binder. 11. The electrode of claim 7 wherein the electrode has a discharge specific capacity of at least 2000 mAh/g at the 7th cycle at rate of C/3 discharged from 1.5V to 0.005V against lithium. 12. The electrode of claim 7 wherein the electrode is contacting a current collector with a loading on one side of the current collector from about 1.4 mg/cm2 to about 4 mg/cm2. 13. A lithium ion battery comprising, the electrode of claim 7;a positive electrode comprising a lithium metal oxide approximately represented by the formula Li1+bNiαMnβCoγAδO2−zFz, where b ranges from about 0.01 to about 0.3, α ranges from about 0 to about 0.4, β range from about 0.2 to about 0.65, γ ranges from 0 to about 0.46, δ ranges from 0 to about 0.15 and z ranges from 0 to about 0.2 with the proviso that both α and γ are not zero, and where A is Mg, Sr, Ba, Cd, Zn, Al, Ga, B, Zr, Ti, Ca, Ce, Y, Nb, Cr, Fe, V, Li or combinations thereof, anda separator between the negative electrode and the positive electrode, wherein the positive electrode has a discharge specific capacity of at least 200 mAh/g at rate of C/3. 14. The battery of claim 13 wherein about 90% of the battery capacity was retained over 50 cycles relative to the 6th cycle at discharge rate of C/3. 15. The battery of claim 13 further comprising supplemental lithium. 16. A porous silicon based material comprising particulate porous crystalline elemental silicon having an average pore sizes in the range of 5 nm to 500 nm in diameter and a discharge specific capacity of at least 1800 mAh/g at the 7th cycle at rate of C/3discharged from 1.5V to 0.005V against lithium; wherein the porous silicon is substantially free of reducing metal and reducing metal oxides. 17. The porous silicon based material of claim 16 further comprising a carbon coating on the porous crystalline element silicon. 18. The porous silicon based material of claim 16 further comprising carbon nanofibers (CNF) blended with the porous crystalline elemental silicon.