A method for coloring powders is provided that includes mixing a base powder and non-incorporated pigments. A colored powder composition having a base powder particle and at least a partial shell of non-incorporated pigments about the base powder particle is also provided. Articles having a coating
A method for coloring powders is provided that includes mixing a base powder and non-incorporated pigments. A colored powder composition having a base powder particle and at least a partial shell of non-incorporated pigments about the base powder particle is also provided. Articles having a coating of the colored powder composition are also provided.
대표청구항▼
1. A method, comprising: providing at least one base powder having a median particle size of at least 25 μm;providing at least one non-incorporated white pigment;providing at least one non-incorporated coloring pigment; andmixing the base powder, the non-incorporated white pigment and the non-incorp
1. A method, comprising: providing at least one base powder having a median particle size of at least 25 μm;providing at least one non-incorporated white pigment;providing at least one non-incorporated coloring pigment; andmixing the base powder, the non-incorporated white pigment and the non-incorporated coloring pigment in dry form for about 15 to 30 minutes to form a colored mixture, wherein at least a majority of the non-incorporated white pigments and the coloring pigments on the surface of the base powder are distributed on the surface of the base powder and are capable of being re-distributed to another base powder upon further mixing, wherein the colored mixture is a free flowing powder, and wherein the colored mixture comprises at least 1 wt. % non-incorporated white pigment, based on the total weight of the colored mixture. 2. The method of claim 1, wherein the base powder comprises up to 25 wt. % of an incorporated white pigment, based on the total weight of the base powder. 3. The method of claim 1, wherein the mixing step is accomplished at a temperature below 40° C. 4. The method of claim 1, wherein the mixing step does not cause significant change in the particle size of the base powder. 5. The method of claim 1, wherein the base powder has a median particle size of 30 to 70 μm and a melt viscosity of at least 90 Pas at 160° C. 6. The method of claim 1, wherein the base powder is not colored. 7. The method of claim 1, wherein the base powder is colored. 8. The method of claim 1, wherein the method further comprises the steps of: measuring the color of a sample of the colored mixture of claim 1;adding additional quantities of base powder, non-incorporated white pigment, and/or non-incorporated coloring pigment to the colored mixture; andmixing the colored mixture and additional quantities of base powder, non-incorporated white pigment, and/or non-incorporated coloring pigment to redistribute the non-incorporated pigments across the base powders to form an adjusted colored mixture having a different color. 9. A method, comprising: providing at least one base powder having a median particle size of at least 25 μm, wherein the base powder is a thermoset material;providing at least one non-incorporated white pigment;providing at least one non-incorporated coloring pigment; andmixing the base powder, the non-incorporated white pigment and the non-incorporated coloring pigment in dry form for about 15 to 30 minutes to form a colored mixture, wherein the colored mixture comprises at least 1 wt. % non-incorporated white pigment, based on the total weight of the colored mixture, and wherein the colored mixture is a free-flowing powder. 10. The method of claim 9, wherein the base powder comprises up to 25 wt. % of an incorporated white pigment, based on the total weight of the base powder. 11. The method of claim 9, wherein the colored mixture comprises at least 2 wt. % non-incorporated white pigment, based on the total weight of the colored mixture. 12. The method of claim 9, wherein the colored mixture comprises at least 3 wt. % non-incorporated white pigment, based on the total weight of the colored mixture. 13. The method of claim 9, wherein the base powder contains between 3 and 15 wt. % of an incorporated white pigment, based on the total weight of the base powder, and the colored mixture comprises between 2 and 10 wt. % non-incorporated white pigment, based on the total weight of the colored mixture. 14. The method of claim 9, wherein base powder comprises between 7 and 15 wt. % of an incorporated TiO2, based on the total weight of the base powder, and the colored mixture comprises between 4 and 8 wt. % non-incorporated TiO2, based on the total weight of the colored mixture. 15. The method of claim 14, wherein the white pigment is selected from the group consisting of titanium dioxide, HALOX, powders of zinc sulfide and barium sulphate, aluminum phosphate nanoparticles, and zinc oxide. 16. The method of claim 9, wherein the colored mixture is a free flowing powder. 17. The method of claim 8, wherein at least a majority of additional quantities of the non-incorporated white pigments and the non-incorporated coloring pigments on the surface of the base powder are distributed on the surface of the base powder and are capable of being redistributed to another base powder upon further mixing.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (41)
Morgan Andrew R. (Low Fell GBX) Sinclair-Day John D. (Greenside GBX) Handyside Timothy M. (High West GBX), Colored powder coating compositions.
Murakami, Toru; Asai, Yasuhiko; Nakajima, Tohru; Watanabe, Yoshihiro, Fluorescent particles, method for preparing the same and paper preventing forgery using the fluorescent particle.
Burke ; Jr. ; deceased Oliver W. (late of Fort Lauderdale FL BY Norma Scala ; administratrix) Humphreys Victor T. (Pompano Beach FL), Intrachromospheruloid/intraleuco-spheruloid pigment compositions and processes for producing same.
Ladatto, Steven M.; Hughes, Don; Seatherton, Gareth, Invertible mixing system with angled blade assembly and method for mixing powders with such system.
Rolles Rolf (New Kensington PA) Williams ; Jr. James E. (New Kensington PA) Kondis Thomas J. (Pittsburgh PA), Method of producing glossy or frosted powder coatings.
O'Keeffe Luke James,GBX ; Nixon Steven Alistair,GBX ; Cameron Colin,GBX ; Penman Alan Keith,GBX, Powder coating composition of semi-crystalline polyester and curing agent.
Ring John,GB3 ; Cassidy Stephen Paul,GB3 ; Cordiner Andrew George,GB3 ; Morgan Andrew Robert,GB3 ; Handyside Timothy Marc,GB3 ; Sinclair-Day John David,GB3, Powder coating compositions.
Sinclair-Day John D. (Tyne & Wear GB3) Cassidy Stephen P. (Newcastle upon Tyne GB3) Ring John (Newcastle upon Tyne GB3) Cordiner Andrew G. (Newcastle upon Tyne GB3), Powder coating compositions.
Rangaswamy Subramaniam (Rochester Hills MI) Miller Robert A. (Oak Park MI), Thermal spray powders for abradable coatings, abradable coatings containing solid lubricants and methods of fabricating.
Pettit ; Jr. Paul H. (Wilmington DE), Thermosetting powder coating composition of a blend of acrylic polymers having different glass transition temperatures a.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.