초록 ▼

A new approach for improving fire resistance of cellulosic materials is provided, especially when the cellulosic material is to be used in polymer composites. Cellulosic material is treated with an aqueous mixture of alkali metal or ammonium hydroxide and alkaline earth or aluminum metal salt simult

A new approach for improving fire resistance of cellulosic materials is provided, especially when the cellulosic material is to be used in polymer composites. Cellulosic material is treated with an aqueous mixture of alkali metal or ammonium hydroxide and alkaline earth or aluminum metal salt simultaneously with or within a short period of time of preparing the mixture. The treated cellulosic material becomes self-extinguishing and may also have improved thermal stability, improved interfacial thermal resistance, improved resistance to damage by oxidants and other chemical agents, improved resistance to biological agents and/or improved resistance to damage by ultra-violet light.

대표청구항 ▼

1. A process of producing a fire-resistant cellulosic material comprising: treating a cellulosic material with an aqueous reaction mixture of an alkali metal or ammonium hydroxide and an alkaline earth or aluminum metal salt, wherein the treating is done simultaneously with or in 1 day or less of mi

1. A process of producing a fire-resistant cellulosic material comprising: treating a cellulosic material with an aqueous reaction mixture of an alkali metal or ammonium hydroxide and an alkaline earth or aluminum metal salt, wherein the treating is done simultaneously with or in 1 day or less of mixing the alkali metal or ammonium hydroxide and alkaline earth or aluminum metal salt; and, drying the treated cellulosic material. 2. The process according to claim 1, wherein the alkaline earth or aluminum metal salt comprises alkaline earth metal salt. 3. The process according to claim 2, wherein the alkaline earth metal salt comprises magnesium or calcium. 4. The process according to claim 2, wherein the alkaline earth metal salt is a chloride, a fluoride, a bromide, an iodide or a nitrate. 5. The process according to claim 2, wherein the alkaline earth metal salt is calcium or magnesium chloride. 6. The process according to claim 1, wherein the alkaline earth or aluminum metal salt comprises aluminum chloride. 7. The process according to claim 1, wherein the hydroxide is selected from the group consisting of: an alkali metal hydroxide, NaOH, or NH4OH. 8. The process according to claim 1, wherein the hydroxide is NH4OH and the metal salt is AlCl3. 9. The process according to claim 1, wherein the aqueous reaction mixture utilizes 0.5-10 wt % of the alkaline earth or aluminum metal salt and 0.5-4 wt % of the alkali metal or ammonium hydroxide, and wherein a product of the reaction of the alkaline earth or aluminum metal salt and the alkali metal or ammonium hydroxide is present in an amount of 0.5 wt % or more. 10. The process according to claim 1, wherein the short period of time is 5 seconds to 5 hours, 5 seconds to 30 minutes, 5 seconds to 10 minutes, or 1 minute to 5 hours. 11. The process according to claim 1, wherein the cellulosic material comprises material from wood sources, agricultural sources, synthetic sources, recycled paper or recycled cardboard. 12. The process according to claim 1, wherein the cellulosic material is further treated with a layered nanoparticulate material before, at the same time or after treating with the aqueous reaction mixture. 13. The process according to claim 12, wherein treating with the layered nanoparticulate material is done after treating with the aqueous reaction mixture. 14. The process according to claim 12, wherein the layered nanoparticulate material comprises one of the following: a layered clay; a layered double hydroxide, montmorillonite, sepiolite, palygorskite, bentonite, fluoromica or a mixture thereof; or a layered double hydroxide, montmorillonite or a mixture thereof. 15. A fire-resistant cellulosic material produced by the process as defined in claim 1. 16. The fire-resistant cellulosic material according to claim 15 which is self-extinguishing. 17. A polymer composite comprising a polymer matrix and the fire-resistant cellulosic material as defined in claim 15 dispersed in the polymer matrix. 18. The polymer composite according to claim 17, wherein the polymer matrix comprises an organic polymer, a thermoset resin; a polyolefin or a phenolic resin; polypropylene or a phenol formaldehyde; or unsaturated polyester or an epoxy polymer. 19. The polymer composite according to claim 17 further comprising a surfactant for improving compatibility of the fire-resistant cellulosic material with the polymer matrix. 20. The polymer composite according to claim 19, wherein the surfactant comprises an amine, a di-functional amine, a poly-functional amine, an alkanolamine, an acid, a carboxylate or any mixture thereof. 21. The polymer composite according to claim 17, wherein the polymer matrix is present in an amount from about 0.1 to about 99.9 weight percent or from about 40 to about 98 weight percent based on total weight of the polymer composite.