초록 ▼

Described is a catalyst comprising a substrate and a catalyst coating of two or more layers: (a) a first layer comprising Pt and/or Pd on the substrate; and (b) a second layer comprising Pt on the first layer; these layers each further comprising: one or more particulate support materials; one or mo

Described is a catalyst comprising a substrate and a catalyst coating of two or more layers: (a) a first layer comprising Pt and/or Pd on the substrate; and (b) a second layer comprising Pt on the first layer; these layers each further comprising: one or more particulate support materials; one or more oxygen storage component (OSC) materials; and one or more nitrogen oxide storage materials comprising one or more elements selected from the group of alkali and/or alkaline earth metals, wherein the total amount of alkali and alkaline earth metals ranges from 0.18 to 2.5 g/in3 calculated as the respective alkali metal oxides M2O and alkaline earth metal oxides MO. Also described is a method for the production of a catalyst, as well as a process for the treatment of a gas stream comprising nitrogen oxide, in particular of an exhaust gas stream resulting from an internal combustion engine.

대표청구항 ▼

1. An oxidation catalyst for the oxidation of NO and hydrocarbons, the catalyst comprising a substrate and a catalyst coating, the catalyst coating comprising two or more layers, said layers comprising: (a) a first layer provided on the substrate, said first layer comprising Pt and/or Pd; and(b) a s

1. An oxidation catalyst for the oxidation of NO and hydrocarbons, the catalyst comprising a substrate and a catalyst coating, the catalyst coating comprising two or more layers, said layers comprising: (a) a first layer provided on the substrate, said first layer comprising Pt and/or Pd; and(b) a second layer provided on the first layer, said second layer comprising Pt; the first and second layers each further comprising: one or more particulate support materials;one or more oxygen storage component (OSC) materials; andone or more nitrogen oxide storage materials comprising one or more elements selected from the group of alkali and/or alkaline earth metals, wherein the total amount of alkali and alkaline earth metals comprised in the one or more nitrogen oxide storage materials contained in the catalyst ranges from 0.18 to 2.5 g/in3 calculated as the respective alkali metal oxides M2O and alkaline earth metal oxides MO, wherein Rh is contained in the catalyst in an amount of 1 g/ft3 or less. 2. The catalyst of claim 1, wherein at least part of the one or more platinum group metals is supported on the one or more particulate support materials. 3. The catalyst of claim 1, wherein the second layer contains less than 500 ppm of Ba. 4. The catalyst of claim 1, wherein the first layer comprises less than 500 ppm of Rh, and/or, wherein the second layer comprises less than 500 ppm of Rh. 5. The catalyst of claim 1, wherein the one or more particulate support materials comprise metal oxide support particles. 6. The catalyst of claim 1, wherein the one or more OSC materials contained in the catalyst comprise one or more compounds selected from the group consisting of zirconia, ceria, lanthana, praseodymia, neodymia, and mixtures thereof. 7. The catalyst of claim 1, wherein the alkaline and/or alkaline earth metals contained in the catalyst are selected from the group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, and Ba. 8. The catalyst of claim 1, wherein the alkaline and/or alkaline earth metals contained in the catalyst are comprised in the one or more oxygen storage materials as their respective carbonates and/or oxides. 9. The catalyst of claim 1, wherein the catalyst coating comprises Pt and Pd in a Pt:Pd weight ratio comprised in the range of from 1:10 to 100:1. 10. The catalyst of claim 1, wherein the catalyst comprises Pt in a loading of from 5 to 180 g/ft3. 11. The catalyst of claim 1, wherein the catalyst comprises Pd in a loading of from 0.5 to 18 g/ft3. 12. The catalyst of claim 1, wherein Rh is contained in the catalyst in an amount of 500 ppm or less. 13. The catalyst of claim 1, wherein the one or more nitrogen oxide storage materials contained in the catalyst comprise Ba in an amount ranging from 0.18 to 2.0 g/in3 calculated as BaO. 14. The catalyst of claim 1, wherein the catalyst coating comprises Pt and Ba in a weight ratio of platinum to barium calculated as Pt:BaO which ranges from 0.01 to 1.0. 15. The catalyst of claim 1, wherein the first layer comprises two or more separate layers, said separate layers being provided on one another. 16. The catalyst of claim 1, wherein the catalyst is comprised in an exhaust gas treatment system comprising an internal combustion engine and an exhaust gas conduit in fluid communication with the internal combustion engine, wherein the catalyst is present in the exhaust gas conduit. 17. The catalyst of claim 16, wherein the exhaust gas treatment system further contains a selective catalytic reduction (SCR) catalyst in the exhaust gas conduit. 18. A process for the treatment of a gas stream comprising nitrogen oxide comprising conducting said gas stream over and/or through a catalyst according to claim 1. 19. A method comprising a step of contacting one or more chemical with a catalyst according to claim 1, for catalyzing the oxidation of one or more of the chemical compounds. 20. A method for producing an oxidation catalyst for the oxidation of NO and hydrocarbons, the method comprising the steps of: (i) providing a substrate;(ii) impregnating one or more particulate support materials with at least one Pt- and/or at least one Pd-source;(iii) adding one or more oxygen storage component (OSC) materials, one or more nitrogen oxide storage materials comprising one or more elements selected from the group of alkali and/or alkaline earth metals, and a solvent to the product obtained in step (ii) to obtain a slurry;(iv) milling the slurry obtained in step (iii);(v) providing the resulting slurry of step (iv) onto the substrate in one or more coating steps as a layer;(vi) optionally repeating steps (ii) to (v) one or more times;(vii) impregnating one or more particulate support materials with at least one Pt-source;(viii) adding one or more oxygen storage component (OSC) materials, one or more nitrogen oxide storage materials comprising one or more elements selected from the group of alkali and/or alkaline earth metals, and a solvent to the product obtained in step (vii) to obtain a slurry;(ix) milling the slurry obtained in step (viii);(x) providing the resulting slurry of step (ix) onto the coated substrate in one or more coating steps as a layer; wherein the total amount of alkali and alkaline earth metals comprised in the one or more nitrogen oxide storage materials contained in the catalyst ranges from 0.18 to 2.5 g/in3 calculated as the respective alkali metal oxides M2O and alkaline earth metal oxides MO, wherein Rh is contained in the catalyst in an amount of 1 g/ft3 or less.