Catalysts having metal nano-particle catalyst supported on surface-treated natural cellulose fibers and preparation method thereof
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B01J-031/02
B01J-037/34
B01J-027/20
B01J-023/28
B01J-023/42
B01J-023/75
B01J-023/755
B01J-035/00
B01J-035/10
B01J-037/02
C01B-003/40
C01B-031/08
C10G-002/00
B01J-031/06
출원번호
US-0943547
(2010-11-10)
등록번호
US-9259728
(2016-02-16)
우선권정보
KR-10-2009-0107802 (2009-11-10)
발명자
/ 주소
Kim, Hee-Yeon
Jeong, Nam-Jo
Han, Seong-Ok
출원인 / 주소
Korea Institute of Energy Research
대리인 / 주소
Renner, Otto, Boisselle & Sklar, LLP
인용정보
피인용 횟수 :
0인용 특허 :
1
초록▼
The present disclosure relates to a catalyst having metal catalyst nanoparticles supported on natural cellulose fibers and a method of preparing the same, whereby natural cellulose fibers are subjected to specific pretreatment to increase a surface area and form defects on the surface thereof and me
The present disclosure relates to a catalyst having metal catalyst nanoparticles supported on natural cellulose fibers and a method of preparing the same, whereby natural cellulose fibers are subjected to specific pretreatment to increase a surface area and form defects on the surface thereof and metal catalyst nanoparticles are then supported on the cellulose catalyst support in a highly dispersed state, thereby providing improved catalysis while allowing production of the catalyst at low cost. The catalyst may be utilized for various catalytic reactions.
대표청구항▼
1. A catalyst having metal catalyst nanoparticles supported on a cellulose catalyst support prepared from natural cellulose fibers, comprising: a cellulose catalyst; andthe metal catalyst nanoparticles deposited directly onto the surface of the cellulose catalyst support by chemical vapor deposition
1. A catalyst having metal catalyst nanoparticles supported on a cellulose catalyst support prepared from natural cellulose fibers, comprising: a cellulose catalyst; andthe metal catalyst nanoparticles deposited directly onto the surface of the cellulose catalyst support by chemical vapor deposition or impregnation,wherein the cellulose catalyst support is treated by:(1) irradiating an electron beam of 10 to 500 kGy to the natural cellulose fibers,(2) the natural cellulose fibers treated with the electron beam are cut to a length of 1˜2 mm in a state of being impregnated in liquid nitrogen and are then heated from 500 to 1500° C. at a rate of 5 to 20° C./min under in an atmosphere composed of a 1:1 mixture of hydrogen and nitrogen, the temperature being maintained at 500 to 1500° C. for 0.5 to 2 hours to carbonize the natural cellulose fibers,(3) the heat-treated natural cellulose fibers are immersed in 0.1˜0.5 M aqueous sulfuric acid solution and then subjected to sweeping in 10˜60 cycles at −0.15˜1.3 V at a sweep rate of 50 mV/s,(4) the swept natural cellulose fibers are then immersed in a 30% nitric acid solution and chemically treated at 100˜150° C. andthrough a series of electron beam treatment, heat treatment, and chemical treatment, the cellulose catalyst support has pores with an inner channel size of up to 10 μm and a BET surface area of 230-383 m2/g, and functional groups introduced to a surface of the natural cellulose fibers. 2. The catalyst of claim 1, wherein the metal catalyst nanoparticles comprise platinum catalyst nanoparticles, and the catalyst having the platinum catalyst nanoparticles supported on the cellulose catalyst support is used for hydrogenation of tetralin or benzene, or oxidation of alcohol. 3. The catalyst of claim 1, wherein the metal catalyst nanoparticles comprise nickel catalyst nanoparticles, and the catalyst having the nickel catalyst nanoparticles supported on the cellulose catalyst support is used for desulfurization, denitrification, or demetallation. 4. The catalyst of claim 1, wherein the metal catalyst nanoparticles comprise molybdenum catalyst nanoparticles, and the catalyst having the molybdenum catalyst nanoparticles supported on the cellulose catalyst support is used for desulfurization, denitrification, or demetallation. 5. The catalyst of claim 1, wherein the metal catalyst nanoparticles comprise cobalt catalyst nanoparticles, and the catalyst having the cobalt catalyst nanoparticles supported on the cellulose catalyst support is used as a co-catalyst for desulfurization, denitrification or demetallation, co-catalyst for platinum catalysts in fuel cells, catalyst for Fisher-Tropsch reaction, catalyst for oxidation and partial oxidation of hydrocarbons, catalyst for reforming reactions, catalyst for amination of ethanol, catalyst for hydrogenation, or catalyst for water-gas shift reactions.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (1)
Rodriguez Nelly M. (State College PA) Baker R. Terry K. (State College PA), Storage of hydrogen in layered nanostructures.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.