초록 ▼

A light weight pressure vessel (10) has been proposed. The vessel (10) is made of a steel, aluminum or non-metal liner (11) which is reinforced with high strength steel wires (21) of 2000-7000 MPa strength. The matrix is filled with a polymer epoxy resin (45). A top layer of fabric tape (33) soaked

A light weight pressure vessel (10) has been proposed. The vessel (10) is made of a steel, aluminum or non-metal liner (11) which is reinforced with high strength steel wires (21) of 2000-7000 MPa strength. The matrix is filled with a polymer epoxy resin (45). A top layer of fabric tape (33) soaked in resin (45) has been used to embed the finish end (24) of the wire (21) and to provide a protective layer over the wire reinforced area. The mesh or net fabric wrap tape (33) has periodic openings to allow penetration of polymer epoxy resin (45). A top coat of a UV resistant polyurethane paint (47) has been applied.

대표청구항 ▼

1. A light weight Type II helical wound cylindrical metal pressure vessel comprised of at least a thin walled steel seamless inner liner or shell formed as one-piece having spun or integrally formed ends free of welds, the inner shell being a cylindrical vessel made of steel of strength 950-1400 MPa

1. A light weight Type II helical wound cylindrical metal pressure vessel comprised of at least a thin walled steel seamless inner liner or shell formed as one-piece having spun or integrally formed ends free of welds, the inner shell being a cylindrical vessel made of steel of strength 950-1400 MPa and a tensile ductility of over 10% and has no longitudinal seam, for leak proof containment of gas which is wrapped with layers of high strength reinforcing monofilament wire covering at least the main body of the inner liner or shell, the monofilament wire being of a diameter between 0.10 and 2.0 mm, where the steel monofilament wire has a strength 2000 MPa to 7000 MPa and where the average lateral space between the monofilament wire is 0 to 25% of the wire diameter and where a polymer is applied to fully fill inter monofilament wire cavities and adhere to surfaces of the monofilament wire and where a non-metallic fabric soaked with the polymer is wrapped on the top of the one or more high strength reinforcing monofilament wires to provide a protective layer of 0.5 to 5 mm thickness, and wherein the one or more reinforcing monofilament wires have a cut end or ends taped or otherwise affixed to the liner at a start of the wrap inward of an outermost coil and a cut end or ends at a finish layer underlying the non-metallic fabric, the monofilament wires being wrapped in the absence of welding and wherein the vessel is wrapped having 4 layers of the monofilament wire embedded in the polymer with the strength efficiency of the monofilament wire utilized at burst pressures of the vessel in the range of 90 to 100 percent of the wire strength due to a high winding density and wire ductility reducing the number of layers and overall thickness of the wrapped vessel to accommodate the expansion of the liner at all load levels up to burst pressure thereby reducing stress in the thin walled inner liner under expansion at all load levels wherein the wrapped layers of high strength reinforcing monofilament wire covering the main body expand and contract with the expansion and contraction of the liner or shell of the pressure vessel without uncoiling. 2. The vessel of claim 1, wherein the strength of the steel monofilament wire is 3000 to 5000 MPa and has a reduction in area at tensile fracture of more than 20% and where the average lateral space between wires is less than 5% of the wire diameter. 3. The vessel of claim 1, where the inner shell is made of aluminum alloy. 4. The vessel of claim 1 where the vessel is fully wrapped by the reinforcing monofilament wire to provide both, longitudinal and transverse reinforcement. 5. The vessel of claim 1 wherein the non metallic fabric is comprised of a fiberglass or polymer tape which has multiple openings of 0.1 mm or larger to allow easy penetration of the polymer. 6. The vessel of claim 1 where the over wrap fabric is a fiberglass mesh tape of 20 mm to 100 mm width with multiple openings of 1 mm to 5 mm and thickness of 0.2 to 1.0 mm. 7. The vessel of claim 1 where the finish end of the monofilament wire is placed securely between layers of the over wrap fabric and the full structure is filled with the polymer. 8. The vessel of claim 1 where the finish end of the wrapping monofilament wire is placed over a fiberglass or other fabric tape of 20 mm to 50 mm width having periodic openings of over 0.5 mm and is covered by the same fiberglass or other fabric tape and the polymer. 9. The vessel of claim 1 which has a top layer of a second polymer which is resistant to ultra violet rays. 10. A light weight Type II helical wound cylindrical metal pressure vessel comprised of at least a thin walled steel seamless inner liner or shell formed as one-piece having spun or integrally formed ends free of welds, the inner shell being a cylindrical vessel made of steel of strength 950-1400 MPa and a tensile ductility of over 10% and has no longitudinal seam, for leak proof containment of gas which is wrapped with layers of high strength reinforcing wire of a diameter of 0.35 mm, where the wire is monofilament steel wire having a strength 3000 MPa to 5000 MPa and where the average lateral space between the reinforcing wire is 0 to 5% of the wire diameter and where a polymer is applied to fully fill the inter wire cavities and adhere to wire surfaces and where a non-metallic fabric soaked with the polymer is wrapped on the top of the reinforcing monofilament steel wire to provide a protective layer of 0.5 to 5 mm thickness, and wherein the reinforcing monofilament steel wire has a cut end or ends taped or otherwise affixed to the liner at a start of the wrap inward of an outermost coil and a cut end or ends at a finish layer underlying the non-metallic fabric, the monofilament steel wire being wrapped in the absence of welding, and wherein the vessel is wrapped having 4 to 6 layers of wire embedded in the polymer with the strength efficiency of the monofilament wire utilized at burst pressures of the vessel in the range of 90 to 100 percent of the wire strength due to a high winding density and wire ductility reducing the number of layers and overall thickness of the wrapped vessel to accommodate the expansion of the liner at all load levels up to burst pressure thereby reducing stress in the thin walled inner liner under expansion at all load levels, wherein the steel wire has a reduction in area at tensile fracture of more than 20% wherein the wrapped layers of high strength reinforcing monofilament wire covering the main body expand and contract with the expansion and contraction of the liner or shell of the pressure vessel without uncoiling. 11. The vessel of claim 10, where the inner shell is made of aluminum alloy. 12. The vessel of claim 10 where the vessel is fully wrapped by the reinforcing monofilament steel wire to provide both, longitudinal and transverse reinforcement. 13. The vessel of claim 10 wherein the non-metallic fabric is comprised of a fiberglass or polymer tape which has multiple openings of 0.1 mm or larger to allow easy penetration of the polymer. 14. The vessel of claim 10 where the over wrap fabric is a fiberglass mesh tape of 20 mm to 100 mm width with multiple openings of 1 mm to 5 mm and thickness of 0.2 to 1.0 mm. 15. The vessel of claim 10 where the finish end of the monofilament wire is placed securely between layers of the over wrap fabric and the full structure is filled with the polymer. 16. The vessel of claim 10 where the finish end of the wrapping wire is placed over a fiberglass or other fabric tape of 20 mm to 50 mm width having periodic openings of over 0.5 mm and is covered by the same fiberglass or other fabric tape and the polymer. 17. The vessel of claim 10 which has a top layer of a second polymer which is resistant to ultra violet rays. 18. A light weight Type II helical wound cylindrical metal pressure vessel comprised of at least a thin walled steel seamless inner liner or shell formed as one-piece having spun or integrally formed ends free of welds, the inner shell being a cylindrical vessel made of steel of strength 950-1400 MPa and a tensile ductility of over 10% and has no longitudinal seam, for leak proof containment of gas which is wrapped with layers of one or more high strength reinforcing wires or in a multi-layered wrap-around covering at least the main body of the inner liner or shell, the steel wires being in one strand, each strand being a monofilament wire of a diameter of 0.35 mm, where the strands are steel wire of strength 2000 MPa to 7000 MPa and where the average lateral space between the reinforcing strands is 0 to 25% of the monofilament wire diameter and where a polymer is applied to fully fill inter wire cavities and adhere to wire surfaces and where a non-metallic fabric soaked with the polymer is wrapped on the top of the one or more reinforcing strands to provide a protective layer of 0.5 to 5 mm thickness, and wherein the one or more reinforcing strands have a cut end or ends taped or otherwise affixed to the liner at a start of the wrap inward of an outermost coil and a cut end or ends at a finish layer underlying the non-metallic fabric, the one or more strands being wrapped in the absence of welding and wherein the vessel is wrapped having 4 layers of the monofilament wire embedded in the polymer has the strength efficiency of the strands utilized at burst pressures of the vessel in the range of 90 to 100 percent of the wire strength due to a high winding density and wire ductility and the multi-layered wrap-around layers of wire covering the main body expand and contract with the expansion and contraction of the liner or shell of the pressure vessel without uncoiling. 19. The vessel of claim 18 wherein the strength of the steel monofilament wire is 3000 to 5000 MPa and has a reduction in area at tensile fracture of more than 20% and where the average lateral space between the monofilament wires is less than 5% of the wire diameter. 20. The vessel of claim 18 where the inner shell is made of aluminum alloy. 21. The vessel of claim 18 where the vessel is fully wrapped by the reinforcing monofilament wires to provide both, longitudinal and transverse reinforcement. 22. The vessel of claim 18 wherein the non metallic fabric is comprised of a fiberglass or polymer tape which has multiple openings of 0.1 mm or larger to allow easy penetration of the polymer. 23. The vessel of claim 18 where the over wrap fabric is a fiberglass mesh tape of 20 mm to 100 mm width with multiple openings of 1 mm to 5 mm and thickness of 0.2 to 1.0 mm. 24. The vessel of claim 18 where the finish end of the monofilament wire is placed securely between layers of the over wrap fabric and the full structure is filled with the polymer. 25. The vessel of claim 18 where the finish end of the wrapping wire is placed over a fiberglass or other fabric tape of 20 mm to 50 mm width having periodic openings of over 0.5 mm and is covered by the same fiberglass or other fabric tape and the polymer. 26. The vessel of claim 18 which has a top layer of a second polymer which is resistant to ultra violet rays.