초록 ▼

A versatile binder comprising at least one or more sulfopolyesters is provided. These sulfopolyester binders can enhance the dry tensile strength, wet tensile strength, tear force, and burst strength of the nonwoven articles in which they are incorporated. Additionally, the water permeability of the

A versatile binder comprising at least one or more sulfopolyesters is provided. These sulfopolyester binders can enhance the dry tensile strength, wet tensile strength, tear force, and burst strength of the nonwoven articles in which they are incorporated. Additionally, the water permeability of these binders can be modified as desired by blending different types of sulfopolyesters to produce the binder. Therefore, the binder can be used in a wide array of nonwoven end products and can be modified accordingly based on the desired properties sought in the nonwoven products.

대표청구항 ▼

1. A wet-laid process to produce a bound nonwoven article, said wet-laid process comprising: (a) melt spinning multicomponent fibers comprising at least one water dispersible sulfopolyester and one or more water non-dispersible polymers immiscible with said sulfopolyester, wherein said multicomponen

1. A wet-laid process to produce a bound nonwoven article, said wet-laid process comprising: (a) melt spinning multicomponent fibers comprising at least one water dispersible sulfopolyester and one or more water non-dispersible polymers immiscible with said sulfopolyester, wherein said multicomponent fibers have a striped configuration and an as-spun denier of less than 15 dpf;(b) cutting said multicomponent fibers into cut multicomponent fibers having a length of less than 25 millimeters;(c) contacting said cut multicomponent fibers with water to remove said sulfopolyester thereby forming a wet lap comprising cut water non-dispersible fibers, wherein said cut water non-dispersible fibers are formed of a thermoplastic polycondensate, wherein said cut water non-dispersible fibers comprise ribbon fibers having a transverse aspect ratio of at least 2:1 and not more than 100:1;(d) transferring said wet lap to a wet-laid nonwoven zone to produce an unbound nonwoven article; and(e) applying a binder dispersion comprising at least one sulfopolyester binder to said nonwoven article; wherein said sulfopolyester binder contains substantially equimolar proportions of acid moiety repeating units (100 mole percent) to hydroxy moiety repeating units (100 mole percent), wherein said sulfopolyester binder comprises repeating units of components (i), (ii), (iii), and (iv) as follows, wherein all stated mole percentages are based on the total of all acid and hydroxy moiety repeating units being equal to 200 mole percent: i. at least 50 mole percent and not more than 99 mole percent of isophthalic acid,ii. at least 1 mole percent and not more than 50 mole percent of 5-sulfoisophthalic acid,iii. at least 20 mole percent and not more than 95 mole percent of 1,4-cyclohexanedimethanol, andiv. at least 5 mole percent and not more than 80 mole percent of diethylene glycol and/or ethylene glycol. 2. The wet-laid process of claim 1, wherein said cut multicomponent fibers have a length of at least 0.25 millimeters and not more than 25 millimeters. 3. The wet-laid process of claim 1, wherein said bound nonwoven article comprises said sulfopolyester binder in an amount of at least 1 weight percent and not more than 40 weight percent. 4. The wet-laid process of claim 1, further comprising, subsequent to said applying of step (e), subjecting said nonwoven article and binder dispersion to heat setting. 5. The wet-laid process of claim 1, further comprising, prior to said transferring of step (d), adding additional fibers and/or additives to said wet lap. 6. The wet-laid process of claim 5, wherein said additional fibers are selected from the group consisting of cellulosic fiber pulp, inorganic fibers, polyester fibers, nylon fibers, polyolefin fibers, rayon fibers, lyocell fibers, cellulose ester fibers, and combinations thereof. 7. The wet-laid process of claim 5, wherein said nonwoven article comprises said additional fibers in an amount of at least 10 weight percent and not more than 80 weight percent, wherein said nonwoven article comprises said cut water non-dispersible fibers in an amount of at least 20 weight percent and not more than 90 weight percent, wherein said bound nonwoven article comprises said sulfopolyester binder in an amount of at least 1 weight percent and not more than 40 weight percent. 8. The wet-laid process of claim 1, wherein said nonwoven article is selected from the group consisting of a battery separator, a high efficiency filter, and a high strength paper. 9. The wet-laid process of claim 5, wherein said nonwoven article comprises said additional fibers in an amount of at least 20 weight percent and not more than 95 weight percent, wherein said nonwoven article comprises said cut water non-dispersible fibers in an amount of at least 1 weight percent and not more than 25 weight percent, wherein said nonwoven article comprises said sulfopolyester binder in an amount of at least 1 weight percent and not more than 40 weight percent. 10. The wet-laid process of claim 1, further comprising, subsequent to said applying of step (e), drying said nonwoven article and binder dispersion. 11. The wet-laid process of claim 1, further comprising, subsequent to said applying of step (e), applying a coating to said nonwoven article and binder dispersion. 12. The wet-laid process of claim 11, further comprising, prior to said applying a coating, drying said nonwoven article and binder dispersion. 13. The wet-laid process of claim 1, wherein said binder dispersion comprises a blend of at least a first sulfopolyester and a second sulfopolyester, wherein said first sulfopolyester or said second sulfopolyester comprise said sulfopolyester binder. 14. The wet-laid process of claim 13, wherein said first and second sulfopolyesters comprise different amounts of a sulfomonomer. 15. The wet-laid process of claim 14, wherein said sulfomonomer is 5-sulfoisophthalic acid. 16. The wet-laid process of claim 13, wherein said first and second sulfopolyesters comprise different amounts of a hydrophobic glycol. 17. The wet-laid process of claim 16, wherein said hydrophobic glycol is 1,4-cyclohexanedimethanol. 18. The wet-laid process of claim 13, wherein said first sulfopolyester is hydrophilic and said second sulfopolyester is hydrophobic. 19. The wet-laid process of claim 13, wherein said first sulfopolyester comprises repeating units of components (a), (b), (c) and (d) as follows, wherein all stated mole percentages are based on the total of all acid and hydroxy moiety repeating units being equal to 200 mole percent: (a) at least 70 mole percent and not more than 90 mole percent of isophthalic acid,(b) at least 10 mole percent and not more than 30 mole percent of 5-sulfoisophthalic acid,(c) at least 25 mole percent and not more than 70 mole percent of 1,4-cyclohexanedimethanol; and(d) at least 30 mole percent and not more than 75 mole percent of diethylene glycol and/or ethylene glycol and;wherein said second sulfopolyester comprises repeating units of components (a), (b), (c) and (d) as follows, wherein all stated mole percentages are based on the total of all acid and hydroxy moiety repeating units being equal to 200 mole percent:(a) at least 80 mole percent and not more than 98 mole percent of isophthalic acid,(b) at least 2 mole percent and not more than 20 mole percent of 5-sulfoisophthalic acid,(c) at least 50 mole percent and not more than 95 mole percent of 1,4-cyclohexanedimethanol; and(d) at least 5 mole percent and not more than 50 mole percent of diethylene glycol and/or ethylene glycol. 20. The wet-laid process of claim 1, wherein the major transverse axis of at least 75 weight percent of said ribbon fibers in said bound nonwoven article are oriented at an angle of less than 30 degrees from the nearest surface of said bound nonwoven article.