초록 ▼

A method includes (1) a thermal diffusion process for using an alkali metal salt raw material having an average particle size of 1 mm or less in diameter, supplying a vapor of the alkali metal salt produced by heating the alkali metal salt raw material together with a carrier gas to the inside of a

A method includes (1) a thermal diffusion process for using an alkali metal salt raw material having an average particle size of 1 mm or less in diameter, supplying a vapor of the alkali metal salt produced by heating the alkali metal salt raw material together with a carrier gas to the inside of a silica-based glass pipe from one end side of the glass pipe, and heating the glass pipe using a heat source which relatively moves in a longitudinal direction of the glass pipe to cause an oxidation reaction of an alkali metal and thermally diffuse the alkali metal into an inner side of the glass pipe, (2) a collapsing process for collapsing the glass pipe after the thermal diffusion process to prepare a core rod; and (3) a cladding portion addition process for adding a cladding portion around the core rod prepared in the collapsing process.

대표청구항 ▼

1. A method of manufacturing an optical fiber preform, the method comprising: a thermal diffusion process including supplying a vapor of the alkali metal salt produced by heating the alkali metal salt raw material having an average particle size of 1 mm or less in diameter together with a carrier ga

1. A method of manufacturing an optical fiber preform, the method comprising: a thermal diffusion process including supplying a vapor of the alkali metal salt produced by heating the alkali metal salt raw material having an average particle size of 1 mm or less in diameter together with a carrier gas to the inside of a silica-based glass pipe from one end side of the glass pipe, and heating the glass pipe using a heat source which relatively moves in a longitudinal direction of the glass pipe to cause an oxidation reaction of the vapor of the alkali metal salt and thermally diffuse the alkali metal into an inner side of the glass pipe;a collapsing process of collapsing the glass pipe after the thermal diffusion process to prepare a core rod; anda cladding portion addition process of adding a cladding portion around the core rod prepared in the collapsing process. 2. The method of manufacturing an optical fiber preform according to claim 1, comprising a drying process of heating the alkali metal salt raw material at a temperature of 270° C. or more to dry the alkali metal salt raw material before the thermal diffusion process. 3. The method of manufacturing an optical fiber preform according to claim 2, wherein the alkali metal salt raw material is heated at a temperature less than a melting point of the alkali metal salt raw material to dry the alkali metal salt raw material in the drying process. 4. The method of manufacturing an optical fiber preform according to claim 2, wherein the drying process includes: a first drying process of heating the alkali metal salt raw material at a temperature less than a melting point of the alkali metal salt raw material to dry the alkali metal salt raw material; anda second drying process of heating the alkali metal salt raw material at a temperature equal to or more than the melting point of the alkali metal salt raw material to dry the alkali metal salt raw material after the first drying process. 5. The method of manufacturing an optical fiber preform according to claim 1, wherein the glass pipe contains chlorine and fluorine, an average concentration of each of the chlorine and the fluorine is 10 atomic ppm or more, and a concentration of other additives is 10 atomic ppm or less. 6. The method of manufacturing an optical fiber preform according to claim 1, wherein the alkali metal is thermally diffused into an inner side of the glass pipe so that the concentration of the alkali metal has a maximum value of 500 atomic ppm or more in the thermal diffusion process. 7. An optical fiber preform made by the method of manufacturing an optical fiber preform according to claim 1, wherein an average concentration of an OH group in a core portion is 0.002 mol·ppm or less. 8. An optical fiber made by drawing the optical fiber preform according to claim 7, wherein a transmission loss increase due to OH group absorption in a wavelength range of 1.38 μm is 0.1 dB/km or less.